Method and apparatus for making layered amorphous semiconductor alloys using microwave energy
Assignee: Sovonics Solar Systems
•
Filing: 1983-12-23
•
Granted: 1985-06-04
•
Expires: 2003-12-23
Abstract
Abstract An apparatus and process utilizes microwave energy for depositing amorphous alloy materials in layered form onto a receiving surface. The process results in materials having unique properties suitable for many applications including photovoltaic applications. The process includes the steps of providing at least one source of microwave energy, providing at least two reaction gases, each gas containing at least one alloying element to be deposited onto the receiving surface, and selectively exciting the reaction gases with microwave energy to create excited species containing the alloying elements to be deposited for depositing the alloys in alternating layers onto the receiving surface. For depositing alternating layers of silicon and germanium alloys, the reactions gases can include silane (SiH 4 ) or silicon tetrafluoride (SiF 4 ), and germane (GeH 4 ) or germanium tetrafluoride (GeF 4 ). In accordance with one disclosed embodiment, the reaction gases are excited separately with the excited species therefrom being sequentially introduced to the receiving surface for layered deposition. In accordance with another disclosed embodiment, the reaction gases are premixed to form a mixture and thereafter, the reaction gases are selectively excited in a plasma which is moved back and forth in the direction of flow of the reaction gas mixture to form selective excited species. Layered deposition results as a consequence of both the selective depletion of one alloying element bearing species from the gas mixture flow and from the motion of the plasma excitation zone relative to the receiving surface.
Inventors
- 👤 Stanford R. Ovshinsky
- 👤 Stephen J. Hudgens
- 👤 Marc A. Kastner
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 18:03
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/02; C23C16/44; C23C16/50; C23C16/511; H; H10; H10F; H10F10/00; H10F10/10; H10F71/00; Y; Y02; Y02E; Y02E10/00; Y02E10/50
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
103 words
A process for depositing amorphous alloy materials in layered form onto a receiving surface comprising: providing at least one source of microwave energy; providing at least two reaction bases, each said gas containing at least one alloying element to be deposited onto said receiving surface; selectively exciting said reaction gases with said microwave energy to create from said reaction gases sequentially excited species containing said alloying elements to be deposited to form at least one region or layer of amorphous alloy material; and depositing said alloy in a plurality of alternating sublayers onto said receiving surface to form said amorphous alloy material region.
Claim 2
Dependent Claim
103 words
A process for depositing amorphous alloy materials in layered form onto a receiving surface comprising: providing at least one source of microwave energy; providing at least two reaction bases, each said gas containing at least one alloying element to be deposited onto said receiving surface; selectively exciting said reaction gases with said microwave energy to create from said reaction gases sequentially excited species containing said alloying elements to be deposited to form at least one region or layer of amorphous alloy material; and depositing said alloy in a plurality of alternating sublayers onto said receiving surface to form said amorphous alloy material region.
Claim 3
Dependent Claim
32 words
A process as defined in claim 1 wherein said step of selectively exciting said reaction gases includes separately exciting said reaction gases and sequentially introducing said excited species onto said receiving surface.
Claim 4
Dependent Claim
33 words
A process as defined in claim 2 comprising the further steps of providing a pair of microwave energy sources and exciting each said reaction gas with a respective one of said microwave sources.
Claim 5
Dependent Claim
17 words
A process as defined in claim 1 wherein each said reaction gas is a reaction gas mixture.
Claim 6
Dependent Claim
71 words
A process as defined in claim 1 comprising the further steps of forming a mixture of said reaction gases, flowing said gas mixture over said receiving surface, creating a plasma by coupling said microwave energy into said reaction gas mixture, and moving said plasma in the direction of flow of said gas mixture for selectively creating said excited species and depositing said alloying elements onto said receiving surface in layered form.
Claim 7
Dependent Claim
15 words
A process as defined in claim 5 wherein said reaction gases have different dissociation energies.
Claim 8
Dependent Claim
52 words
A process as defined in claim 5 comprising the further steps of providing said microwave energy source with an antenna for coupling said microwave energy into said reaction gas mixture, and moving said antenna with respect to said receiving surface along the direction of said gas mixture flow for moving said plasma.
Claim 9
Dependent Claim
37 words
A process as defined in claim 5 wherein said plasma is moved rectilinearly and wherein the period of said plasma movement is long compared to the time required to deposit several atomic layers of the alloy materials.
Claim 10
Dependent Claim
15 words
A process as defined in claim 1 where said reaction gases include semiconductor containing compounds.
Claim 11
Dependent Claim
17 words
A process as defined in claim 9 wherein at least one of said reaction gases includes silicon.
Claim 12
Dependent Claim
25 words
A process as defined in claim 10 wherein said at least one reaction gas is silane (SiH 4 ) or silicon tetrafluoride (SiF 4 ).
Claim 13
Dependent Claim
17 words
A process as defined in claim 9 wherein at least one of said reaction gases includes germanium.
Claim 14
Dependent Claim
25 words
A process as defined in claim 12 wherein said at least one reaction gas is germane (GeH 4 ) or germanium tetrafluoride (GeF 4 ).
Claim 15
Dependent Claim
32 words
A process as defined in claim 1 wherein said reaction gases include silicon and germanium, and wherein alternating sublayers of amorphous silicon and amorphous germanium alloys are deposited onto said receiving surface.
Claim 16
Dependent Claim
38 words
A process as defined in claim 14 including forming said germanium alloy sublayers to absorb photons and produce charge carrier pairs and forming said silicon alloy sublayers to effect transport of the charge carriers for efficient charge collection.
Claim 17
Dependent Claim
27 words
A process as defined in claim 14 including forming said alternating alloy sublayers to include at least one density of states reducing element, said element being fluorine.
Claim 18
Dependent Claim
27 words
A process as defined in claim 14 including forming said alternating alloy sublayers to include at least one density of states reducing element, said element being hydrogen.
Claim 19
Dependent Claim
61 words
A process as defined in claim 1 including forming a plurality of alternating amorphous semiconductor alloy layers, forming alternating alloy layers from at least two different semiconductor alloys having a different band gap from one another, and forming a bulk composite material from said plurality of sublayers having a composite band gap intermediate the band gaps of said different alloy sublayers.
Claim 20
Dependent Claim
22 words
A process as defined in claim 18 including forming said bulk composite materials with greater than two sets of alternating alloy sublayers.
Claim 21
Dependent Claim
21 words
A process as defined in claim 18 including forming at least one of said alternating sublayers from an amorphous silicon alloy.
Claim 22
Dependent Claim
21 words
A process as defined in claim 18 including forming at least one of said alternating sublayers from an amorphous germanium alloy.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-06-03 | 1988-12-03 | 1989-06-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-06-03 | 1992-12-03 | 1993-06-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-06-03 | 1996-12-03 | 1997-06-04 | $7700.00 | Window Closed / Lapsed |