US4507430A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Water-base polyurethane emulsion
Assignee: Hodogaya Chemical Co Ltd
•
Filing: 1984-08-03
•
Granted: 1985-03-26
•
Expires: 2004-08-03
Abstract
Abstract A water-base polyurethane emulsion useful as an adhesive or coating material for a polyolefin resin, which comprises a polyol component and a polyisocyanate component, characterized in that a hydrogenated polyalkadiene polyol is used as the polyol component.
Inventors
- 👤 Shigeru Shimada
- 👤 Akira Kuroda
- 👤 Junichi Tomiuga
- 👤 Shinzi Ishikawa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 16:40
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/36; C08J9/365; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/40; C08G18/62; C08G18/6204; C08G18/6208; C08G18/67; C08G18/69; C08G18/696; C08J5/00; C08J5/12; C08J5/124; C08J5/127; C09; C09J; C09J175/00; C09J175/04; C09J175/12; C08J2323/00; C08J2323/02
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
37 words
A water-base polyurethane emulsion useful as an adhesive or coating material for a polyolefin resin, which comprises a polyol component and a polyisocyanate component, characterized in that a hydrogenated polyalkadiene polyol is used as the polyol component.
Claim 2
Dependent Claim
37 words
A water-base polyurethane emulsion useful as an adhesive or coating material for a polyolefin resin, which comprises a polyol component and a polyisocyanate component, characterized in that a hydrogenated polyalkadiene polyol is used as the polyol component.
Claim 3
Dependent Claim
44 words
The water-base polyurethane emulsion according to claim 1, wherein the hydrogenated polyalkadiene polyol has an average molecular weight of from 500 to 4,000, an average number of functional hydroxyl groups of from 1.5 to 3, and a hydrogen saturation degree of at least 40%.
Claim 4
Dependent Claim
18 words
The water-base polyurethane emulsion according to claim 1, wherein the hydrogenated polyalkadiene polyol is a hydrogenated polybutadiene polyol.
Claim 5
Dependent Claim
18 words
The water-base polyurethane emulsion according to claim 1, wherein the hydrogenated polybutadiene polyol is a hydrogenated poly-1,3-pentadiene polyol.
Claim 6
Dependent Claim
67 words
The water-base polyurethane emulsion according to claim 1, wherein the hydrogenated polyalkadiene polyol is a hydrogenated polyol of a copolymer of a conjugated diene monomer selected from the group consisting of 1,3-butadiene and 1,3-pentadiene, with an olefin monomer selected from the group consisting of styrene, acrylonitrile, methacrylonitrile, methylacrylate and ethylmethacrylate, the content of the conjugated diene monomer being at least 50% by weight of the total monomers.
Claim 7
Dependent Claim
39 words
The water-base polyurethane emulsion according to claim 1, wherein the polyisocyanate component is selected from the group consisting of tolylene diisocyanate, 4,4'-diphenylmethane diisocyanate, naphthylene, diisocyanate, 1,6-hexamethylene diisocyanate, xylylene diisocyanate, isophorone diisocyanate, 4,4'-methylene bis(cyclohexyl isocyanate), 1,3-bis(isocyanatomethyl)cyclohexane and trimethyl hexamethylene diisocyanate.
Claim 8
Dependent Claim
64 words
The water-base polyurethane emulsion according to claim 1, wherein the polyol component further contains at least one polyol selected from the group consisting of polyoxytetramethylene glycol, polyoxypropylene polyol, polyoxyethylene polyol, a polyol obtained by the addition of ethyleneoxide or propyleneoxide to bisphenol A, polyethyleneadipate polyol, polypropyleneadipate polyol, polybutyleneadipate polyol, polycarbonate polyol, polyhexamethyleneadipate polyol, polycaprolactone polyol, ehtylene glycol, propylene glycol, 1,4-butane diol and 1,6-hexane diol.
Claim 9
Dependent Claim
23 words
The water-base polyurethane emulsion according to claim 7, wherein the polyol component contains at least 20% by weight of the hydrogenated polyalkadiene polyol.
Claim 10
Dependent Claim
40 words
A water-base polyurethane emulsion useful as an adhesive or coating material for a polyolefin resin, which is prepared by reacting a hydrogenated polybutadiene polyol with a polyisocyanate compound to form a polyurethane prepolymer and emulsifying the polyurethane prepolymer in water.
Claim 11
Dependent Claim
40 words
A water-base polyurethane emulsion useful as an adhesive or coating material for a polyolefin resin, which is prepared by reacting a hydrogenated polybutadiene polyol with a polyisocyanate compound to form a polyurethane prepolymer and emulsifying the polyurethane prepolymer in water.
Claim 12
Dependent Claim
31 words
The water-base polyurethane emulsion according to claim 9, wherein the polyurethane prepolymer is reacted with an active hydrogen compound having an anionic or a catonic salt-forming group prior to the emulsification.
Claim 13
Dependent Claim
19 words
The water-base polyurethane emulsion according to claim 10, wherein the active hydrogen compound is a half-ester of polyoxypropylene triol.
References Cited (Backward Citations)
US3993614A
Cited
US3988278A
Cited
US3983058A
Cited
US4152309A
Cited
US4389509A
Cited
US4208311A
Cited
JPS5613327A
Cited
US4376840A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-03-25 | 1988-09-24 | 1989-03-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-03-25 | 1992-09-24 | 1993-03-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-03-25 | 1996-09-24 | 1997-03-26 | $7700.00 | Window Closed / Lapsed |