Pressure-sensitive adhesive composition
Assignee: Nitto Denko Corp
•
Filing: 1978-01-23
•
Granted: 1979-05-01
•
Expires: 1998-01-23
Abstract
Abstract A pressure-sensitive adhesive composition comprising a liquid diene polymer containing therein an average of about 2.0 to about 2.5 functional groups capable of reacting with an isocyanate group, an isocyanate compound containing therein 2 or more isocyanate groups, and a tackifier, wherein an anionic surface active agent is compounded therewith in an amount of about 0.2 to about 10 parts by weight per 100 parts by weight of the total weight of the liquid diene polymer and the isocyanate compound. This pressure-sensitive adhesive composition is coated on a support and heated to produce a pressure-sensitive adhesive layer whereby a pressure-sensitive adhesive tape, for example, can be obtained.
Inventors
- 👤 Ichiro Ijichi
- 👤 Shigetoshi Kai
- 👤 Hikaru Teranishi
- 👤 Akira Morioka
- 👤 Kazuyoshi Seki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 18:29
CPC Classifications
C; C09; C09J; C09J175/00; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/67; C08G18/69; C08K; C08K5/00; C08K5/04; C08K5/09; C08K5/36; C08K5/41; C08K5/42; C08K5/49; C08K5/51; C08L; C08L45/00; C08L61/00; C08L61/04; C08L61/06; C08L61/18; C08L75/00; C08L91/00; C09J7/00; C09J7/30; C09J7/38; C08G2170/00; C08G2170/40; C08L2666/00; C08L2666/02; C08L2666/28
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
188 words
A pressure-sensitive adhesive composition for producing a pressure-sensitive adhesive, the pressure-sensitive adhesive composition comprising (i) a liquid diene polymer containing in the molecule thereof an average of about 2.0 to about 2.5 functional groups capable of reacting with an isocyanate, (ii) an isocyanate compound containing therein 2 or more isocyanate groups in the molecule thereof, and (iii) a tackifier, wherein an anionic surface active agent (iv) is present in an amount of about 0.2 to about 10 parts by weight per 100 parts by weight of the total weight of said liquid diene polymer and isocyanate compound, said anionic surface active agent being selected from the group consisting of (a) carboxylates represented by the formulae RCH 2 --COONa and ##STR4## (b) sulfonates represented by the formulae ##STR5## (c) sulfate salts represented by the formulae ##STR6## (d) alkyl phosphoric acid diester salts having 1 to 18 carbon atoms in the alkyl moiety thereof; and (e) alkylphenol type phosphoric acid diester salts having 1 to 18 carbon atoms in the alkyl moiety thereof wherein R, R' and R" are branched or straight chain hydrocarbons having 1 to 18 carbon atoms.
Claim 2
Dependent Claim
188 words
A pressure-sensitive adhesive composition for producing a pressure-sensitive adhesive, the pressure-sensitive adhesive composition comprising (i) a liquid diene polymer containing in the molecule thereof an average of about 2.0 to about 2.5 functional groups capable of reacting with an isocyanate, (ii) an isocyanate compound containing therein 2 or more isocyanate groups in the molecule thereof, and (iii) a tackifier, wherein an anionic surface active agent (iv) is present in an amount of about 0.2 to about 10 parts by weight per 100 parts by weight of the total weight of said liquid diene polymer and isocyanate compound, said anionic surface active agent being selected from the group consisting of (a) carboxylates represented by the formulae RCH 2 --COONa and ##STR4## (b) sulfonates represented by the formulae ##STR5## (c) sulfate salts represented by the formulae ##STR6## (d) alkyl phosphoric acid diester salts having 1 to 18 carbon atoms in the alkyl moiety thereof; and (e) alkylphenol type phosphoric acid diester salts having 1 to 18 carbon atoms in the alkyl moiety thereof wherein R, R' and R" are branched or straight chain hydrocarbons having 1 to 18 carbon atoms.
Claim 3
Dependent Claim
30 words
The pressure-sensitive adhesive composition according to claim 1, wherein the liquid diene polymer is liquid at room temperature and has a molecular weight of from about 1,000 to about 50,000.
Claim 4
Dependent Claim
34 words
The pressure-sensitive adhesive composition according to claim 1, wherein the liquid diene polymer contains one or more functional groups selected from the class consisting of --OH, --CH 2 OH, --COOH, --NH 2 and --SH.
Claim 5
Dependent Claim
62 words
The pressure sensitive adhesive composition according to claim 1, wherein the isocyanate compound is selected from the group consisting of diisocyanates, diisocyanate or triisocyanate compounds produced from diisocyanates and polyhydroxy compounds, or blocked polyisocyanates produced by reacting the isocyanate groups of the preceding isocyanate compounds with a compound of the formula ROH, wherein R is an aromatic alicyclic or aliphatic monovalent group.
Claim 6
Dependent Claim
39 words
The pressure-sensitive adhesive composition according to claim 4, wherein said isocyanate compound is present in an amount of about 0.75 to about 1.2 equivalents of the isocyanate group per equivalent of the functional group of the liquid diene polymer.
Claim 7
Dependent Claim
32 words
The pressure-sensitive adhesive composition according to claim 1, wherein the tackifier is selected from the group consisting of an alkylphenol resin, a terpene phenol resin, a xylene-formaldehyde resin, rosin, and hydrogenated rosin.
Claim 8
Dependent Claim
37 words
The pressure-sensitive adhesive composition according to claim 1, wherein the composition further contains a catalyst in an amount of about 0.01 to about 5.0 parts by weight per 100 parts by weight of the liquid diene polymer.
Claim 9
Dependent Claim
41 words
The pressure-sensitive adhesive composition according to claim 1, wherein the liquid diene polymer is selected from the group consisting of a homopolymer of butadiene, isoprene or chloroprene or a copolymer of butadiene, isoprene or chloroprene and a vinyl monomer copolymerizable therewith.
Claim 10
Dependent Claim
16 words
The pressure-sensitive adhesive composition according to claim 8, wherein said vinyl monomer is styrene or acrylonitrile.
Claim 11
Dependent Claim
43 words
The pressure-sensitive adhesive composition according to claim 8, wherein said liquid diene polymer is said copolymer and wherein said vinyl monomer is present in an amount of about 5 to about 40% by weight based on the total weight of the diene polymer.
Claim 12
Dependent Claim
60 words
The pressure-sensitive adhesive composition according to claim 1, wherein said anionic surface active agent is selected from the group consisting of (a) carboxylates represented by the formulae ##STR7## (b) sulfonates represented by the formulae ##STR8## (c) sulfate salts represented by the formulae ##STR9## wherein R, R' and R" are branched or straight chain hydrocarbons having 1 to 18 carbon atoms.
Claim 13
Dependent Claim
36 words
The pressure-sensitive adhesive composition according to claim 1, wherein said anionic surface active agent is selected from the group consisting of sodium dioctylsulfosuccinate, sodium dodecylbenzene sulfonate, sodium naphthalene sulfonate and the sodium sulfate of lauryl alcohol.
Claim 14
Dependent Claim
198 words
A pressure-sensitive adhesive comprising the following pressure-sensitive adhesive composition which has been heated to about 100° to about 180° C. for about 40 seconds to about 5 minutes: (i) a liquid diene polymer containing in the molecule thereof an average of about 2.0 to about 2.5 functional groups capable of reacting with the isocyanate, (ii) an isocyanate compound containing therein 2 or more isocyanate groups in the molecule thereof, and (iii) a tackifier, wherein an anionic surface active agent (iv) is present in an amount of about 0.2 to about 10 parts by weight per 100 parts by weight of the total weight of said liquid diene polymer and isocyanate compound, said anionic surface active agent being selected from the group consisting of (a) carboxylates represented by the formulae ##STR10## (b) sulfonates represented by the formulae ##STR11## (c) sulfate salts represented by the formulae ##STR12## (d) alkyl phosphoric acid diester salts having 1 to 18 carbon atoms in the alkyl moiety thereof; and (e) alkylphenol type phosphoric acid diester salts having 1 to 18 carbon atoms in the alkyl moiety thereof wherein, R, R' and R" are branched or straight chain hydrocarbons having 1 to 18 carbon atoms.
Claim 15
Dependent Claim
198 words
A pressure-sensitive adhesive comprising the following pressure-sensitive adhesive composition which has been heated to about 100° to about 180° C. for about 40 seconds to about 5 minutes: (i) a liquid diene polymer containing in the molecule thereof an average of about 2.0 to about 2.5 functional groups capable of reacting with the isocyanate, (ii) an isocyanate compound containing therein 2 or more isocyanate groups in the molecule thereof, and (iii) a tackifier, wherein an anionic surface active agent (iv) is present in an amount of about 0.2 to about 10 parts by weight per 100 parts by weight of the total weight of said liquid diene polymer and isocyanate compound, said anionic surface active agent being selected from the group consisting of (a) carboxylates represented by the formulae ##STR10## (b) sulfonates represented by the formulae ##STR11## (c) sulfate salts represented by the formulae ##STR12## (d) alkyl phosphoric acid diester salts having 1 to 18 carbon atoms in the alkyl moiety thereof; and (e) alkylphenol type phosphoric acid diester salts having 1 to 18 carbon atoms in the alkyl moiety thereof wherein, R, R' and R" are branched or straight chain hydrocarbons having 1 to 18 carbon atoms.
Claim 16
Dependent Claim
58 words
The pressure-sensitive adhesive of claim 13, wherein said anionic surface active agent is selected from the group consisting of (a) carboxylates represented by the formulae ##STR13## (b) sulfonates represented by the formulae ##STR14## (c) sulfate salts represented by the formulae ##STR15## wherein R, R' and R" are branched or straight chain hydrocarbons having 1 to 18 carbon atoms.
Claim 17
Dependent Claim
33 words
The pressure-sensitive adhesive of claim 13, wherein said anionic surface active agent is selected from the group consisting of sodium dioctylsulfosuccinate, sodium dodecylbenzene sulfonate, sodium naphthalene and the sodium sulfate of lauryl alcohol.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-04-30 | 1982-10-30 | 1983-05-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-04-30 | 1986-10-30 | 1987-05-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-04-30 | 1990-10-30 | 1991-05-01 | $7700.00 | Window Closed / Lapsed |