Assignee: Hoechst AG
•
Filing: 1982-07-27
•
Granted: 1985-02-12
•
Expires: 2002-07-27
Abstract
Abstract The present invention relates to molded articles of an open-cell structure, containing a copolymer which is comprised of copolymerized, fluorinated olefin, copolymerized vinyl acetate and optionally copolymerized olefin, the acetate groups of the copolymer being optionally saponified into OH groups. The molded articles possess an inherent latent structural convertibility and have effective pores of a diameter in the range from 0.002 to 10 μm. The invention further includes processes for the preparation of the specified molded articles and processes for converting their structure. The invention also relates to several uses of molded articles according to the invention.
Inventors
- 👤 Axel Walch
- 👤 Walter Seifried
- 👤 Wolfgang Michel
- 👤 Jurgen Kuhls
- 👤 Jurgen Wildhardt
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 16:32
CPC Classifications
G; G03; G03G; G03G7/00; G03G7/006; G03G7/0073; A; A61; A61L; A61L15/00; A61L15/16; A61L15/22; A61L15/225; A61L15/42; A61L15/425; C; C08; C08J; C08J9/00; C08J9/28; D; D01; D01D; D01D5/00; D01D5/24; G01; G01N; G01N33/00; G01N33/48; G01N33/50; G01N33/52; G01N33/521; G01N33/53; G01N33/543; G01N33/544; G01N33/545; G03C; G03C1/00; G03C1/76; G03C1/795; G03G7/0006; G03G7/002; G03G7/0026; G03G7/004; C08J2201/00; C08J2201/04; C08J2201/054; C08J2201/0542; C08J2201/0544; C08J2327/00; C08J2327/02; C08J2327/12; C08J2329/00; C08J2329/02; C08J2329/04
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
164 words
A microporous molded article having an open-cell structure and comprising a thermoplastic material which possesses an inherent latent structural convertibility and includes effective pores of a diameter in the range from about 0.002 to 10 μm, said thermoplastic material comprising at least about 70 percent by weight of a terpolymer which is composed of from about 20 to 80 percent by weight, relative to the total weight of the terpolymer, of copolymerized fluorinated olefin selected from the group consisting of ethylene and propylene, up to about 40 percent by weight, relative to the total weight of the terpolymer, of copolymerized olefin selected from the group consisting of ethylene and propylene, and from about 80 to 20 percent by weight, relative to the total weight of the copolymer, of copolymerized vinyl acetate, with at least 5 percent of the total proportion of acetate groups contained in the copolymer being converted by saponification into OH groups after copolymerization of the specified comonomers to form the terpolymer.
Claim 2
Dependent Claim
164 words
A microporous molded article having an open-cell structure and comprising a thermoplastic material which possesses an inherent latent structural convertibility and includes effective pores of a diameter in the range from about 0.002 to 10 μm, said thermoplastic material comprising at least about 70 percent by weight of a terpolymer which is composed of from about 20 to 80 percent by weight, relative to the total weight of the terpolymer, of copolymerized fluorinated olefin selected from the group consisting of ethylene and propylene, up to about 40 percent by weight, relative to the total weight of the terpolymer, of copolymerized olefin selected from the group consisting of ethylene and propylene, and from about 80 to 20 percent by weight, relative to the total weight of the copolymer, of copolymerized vinyl acetate, with at least 5 percent of the total proportion of acetate groups contained in the copolymer being converted by saponification into OH groups after copolymerization of the specified comonomers to form the terpolymer.
Claim 3
Dependent Claim
88 words
A molded article according to claim 1, wherein said terpolymer comprises about 30 to 70 percent by weight, relative to its total weight, of copolymerized tetrafluoroethylene, from about up to 20 percent by weight of copolymerized ethylene, and from about 70 to 30 percent by weight, relative to the total weight of the terpolymer, of copolymerized vinyl acetate, with at least 5 percent of the acetate groups contained in the terpolymer being converted by saponification into OH groups after copolymerization of the specified comonomers to form the terpolymer.
Claim 4
Dependent Claim
26 words
A molded article according to claim 1 or 2, wherein more than about 80 percent of the acetate groups are converted by saponification into OH groups.
Claim 5
Dependent Claim
16 words
A molded article according to claim 1 or 2, which comprises the form of a film.
Claim 6
Dependent Claim
162 words
A molded article having an open-cell structure and comprising a thermoplastic material which possesses an inherent latent structural convertibility and includes effective pores of a diameter in the range from about 0.002 to 10 μm, said thermoplastic material comprising at least about 70 percent by weight of a copolymer which is composed of from about 20 to 80 percent by weight, relative to the total weight of the copolymer, of copolymerized perfluorinated olefin from the group consisting of ethylene and propylene, from about 0 to 40 percent by weight, relative to the total weight of the copolymer, of copolymerized olefin from the group consisting of ethylene and propylene and from about 80 and 20 percent by weight, relative to the total weight of the copolymer, of copolymerized vinyl acetate, with at least 5 percent of the total proportion of acetate groups contained in the copolymer being converted by saponification into OH groups after copolymerization of the specified comonomers to form the copolymer.
Claim 7
Dependent Claim
162 words
A molded article having an open-cell structure and comprising a thermoplastic material which possesses an inherent latent structural convertibility and includes effective pores of a diameter in the range from about 0.002 to 10 μm, said thermoplastic material comprising at least about 70 percent by weight of a copolymer which is composed of from about 20 to 80 percent by weight, relative to the total weight of the copolymer, of copolymerized perfluorinated olefin from the group consisting of ethylene and propylene, from about 0 to 40 percent by weight, relative to the total weight of the copolymer, of copolymerized olefin from the group consisting of ethylene and propylene and from about 80 and 20 percent by weight, relative to the total weight of the copolymer, of copolymerized vinyl acetate, with at least 5 percent of the total proportion of acetate groups contained in the copolymer being converted by saponification into OH groups after copolymerization of the specified comonomers to form the copolymer.
References Cited (Backward Citations)
US2468664A
Cited
DE1214395B
Cited
US3445434A
Cited
GB1155531A
Cited
DE1544928A1
Cited
US3615024A
Cited
US4049589A
Cited
US4238571A
Cited
FR2364243A1
Cited
EP0012557A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-02-12 | 1988-08-13 | 1989-02-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-02-12 | 1992-08-13 | 1993-02-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-02-12 | 1996-08-13 | 1997-02-12 | $7700.00 | Window Closed / Lapsed |