Low temperature hardening of the surface of a ferrous metal workpiece in a fluidized bed furnace
Assignee: Individual
•
Filing: 1983-03-15
•
Granted: 1984-07-24
•
Expires: 2003-03-15
Abstract
Abstract The surface of a ferrous metal workpiece is heat treated by immersing the workpiece to be treated in the fluidized particulate bed of a fluidized bed furnace. The bed is fluidized by a gas atmosphere comprising ammonia gas, hydrocarbon gas, and optionally a non-reactive gas. The temperature of the fluidized bed is maintained at about 600° F. to 1250° F. The proportion of the ammonia gas in the gaseous atmosphere may be varied to alter the surface characteristics of the treated workpiece. The compound layer and the underlying diffusion zone exhibit increased thicknesses. Increased hardness and increased impact loading resistance of the treated surface are obtainable.
Inventors
- 👤 John A. Ross
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 16:31
CPC Classifications
C; C21; C21D; C21D1/00; C21D1/34; C21D1/53; C23; C23C; C23C8/00; C23C8/06; C23C8/28; C23C8/30; C23C8/32
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
131 words
A method for treating the surface of a ferrous metal workpiece comprising: providing a fluidized bed furnace having a bed of metallurgically non-reactive particulate material which is thermally conductive in a fluidized state; heating said bed to a temperature of about 600° F. to 1250° F.; fluidizing said heated bed of particulate material with a gas atmosphere consisting essentially of a source of nascent nitrogen and a source of carbon with the remainder of said atmosphere being non-reactive gas and unavoidable impurities; disposing said ferrous metal workpiece to be treated in said heated fluidized bed; whereby said nitrogen and carbon react with the surface of said ferrous metal workpiece disposed in said heated fluidized bed to provide a compound layer and an underlying diffusion zone on the surface of said workpiece.
Claim 2
Independent Claim
131 words
A method for treating the surface of a ferrous metal workpiece comprising: providing a fluidized bed furnace having a bed of metallurgically non-reactive particulate material which is thermally conductive in a fluidized state; heating said bed to a temperature of about 600° F. to 1250° F.; fluidizing said heated bed of particulate material with a gas atmosphere consisting essentially of a source of nascent nitrogen and a source of carbon with the remainder of said atmosphere being non-reactive gas and unavoidable impurities; disposing said ferrous metal workpiece to be treated in said heated fluidized bed; whereby said nitrogen and carbon react with the surface of said ferrous metal workpiece disposed in said heated fluidized bed to provide a compound layer and an underlying diffusion zone on the surface of said workpiece.
Claim 3
Dependent Claim
23 words
A method as recited in claim 1 wherein said gas atmosphere consists essentially of a hydrocarbon gas and ammonia gas and unavoidable impurities.
Claim 4
Dependent Claim
23 words
A method as recited in claim 1 wherein said gas atmosphere consists essentially of a hydrocarbon gas, ammonia, non-reactive gas and unavoidable impurities.
Claim 5
Dependent Claim
22 words
A method as recited in claim 3 wherein said non-reactive gas is selected from the group consisting of nitrogen, argon and helium.
Claim 6
Dependent Claim
13 words
A method as recited in claim 4 wherein said non-reactive gas is nitrogen.
Claim 7
Dependent Claim
28 words
A method as recited in claim 1 wherein said workpiece is disposed in said heated bed fluidized by said gas atmosphere for about 0.5 hours to 2.5 hours.
Claim 8
Dependent Claim
14 words
A method as recited in claim 1 wherein said particulate material is aluminum oxide.
Claim 9
Dependent Claim
40 words
A method as recited in claim 1 wherein said gas atmosphere consists essentially of about 30% to 100% by volume ammonia gas and about 0% to 70% by volume hydrocarbon gas with the remainder being non-reactive gas and unavoidable impurities.
Claim 10
Dependent Claim
34 words
A method as recited in claim 8 wherein said compound layer has a thickness of about 0.001 to 0.003 inch and said diffusion zone layer has a thickness of about 0.025 to 0.050 inch.
Claim 11
Dependent Claim
16 words
A method as recited in claim 9 wherein said compound layer is characterized by file hardness.
Claim 12
Dependent Claim
40 words
A method as recited in claim 1 wherein said gas atmosphere consists essentially of about 10% to 50% by volume ammonia gas and about 10% to 75% by volume hydrocarbon gas with the remainder being non-reactive gas and unavoidable impurities.
Claim 13
Dependent Claim
17 words
A method as recited in claim 8 wherein said workpiece surface has an improved impact loading resistance.
Claim 14
Dependent Claim
17 words
A method as recited in claim 1 wherein said temperature is about 950° F. to 1150° F.
Claim 15
Dependent Claim
19 words
A method as recited in claim 8 wherein the hardness of said compound layer is at least about 68Rc.
Claim 16
Dependent Claim
19 words
A method as recited in claim 11 wherein the hardness of said compound layer is about 60Rc to 67Rc.
Claim 17
Dependent Claim
28 words
A method as recited in claim 9 wherein said workpiece is disposed in said heated bed fluidized by said gas atmosphere for about 0.5 hours to 2.5 hours.
Claim 18
Dependent Claim
27 words
A method as recited in claim 11 wherein said workpiece is disposed in said heated bed fluidized by said gas atmosphere for about 0.5 to 2.5 hours.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-07-24 | 1988-01-23 | 1988-07-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-07-24 | 1992-01-23 | 1992-07-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-07-24 | 1996-01-23 | 1996-07-24 | $7700.00 | Window Closed / Lapsed |