Glass fiber reinforced polyvinyl composition
Assignee: HT Troplast AG
•
Filing: 1983-01-28
•
Granted: 1984-06-19
•
Expires: 2003-01-28
Abstract
Abstract A glass fiber-reinforced polyvinyl chloride composition contains, per 100 parts by weight of polyvinyl chloride of a K value of between 55 and 75, 40-100 parts by weight of glass fibers having a diameter of between 5 and 25 μm with a length of 0.5 to 12 mm, and 1-25 parts by weight of mineral filler having an average particle diameter of below 50 μm.
Inventors
- 👤 Wolfgang Budich
- 👤 Bertram Gasper
- 👤 Josef Kurth
- 👤 Karl-Gunter Scharf
- 👤 Waldemar Wissinger
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 15:42
CPC Classifications
C; C08; C08L; C08L27/00; C08L27/02; C08L27/04; C08L27/06; C08K; C08K7/00; C08K7/02; C08K7/04; C08K7/14; C08K13/00; C08K13/04
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
125 words
An extrudable glass fiber-reinforced polyvinyl chloride composition made up of polyvinyl chloride resin having a K value between 55 and 75, glass fibers, and inorganic fillers different from the glass fibers, and conventional additives, including mold release agents, stabilizers, processing aids, and colorants for the production of extruded articles, said composition containing, per 100 parts by weight of a polyvinyl chloride resin, 50-100 parts by weight of glass fibers having a diameter of between 5 and 25 μm with a length up to 12 mm, and 5-25 parts by weight of a mineral filler having an average particle diameter of below 50 μm and exhibiting a modulus of elasticity in the extrusion direction of an extruded product of at least 8,000N/mm 2 at 23° C.
Claim 2
Dependent Claim
125 words
An extrudable glass fiber-reinforced polyvinyl chloride composition made up of polyvinyl chloride resin having a K value between 55 and 75, glass fibers, and inorganic fillers different from the glass fibers, and conventional additives, including mold release agents, stabilizers, processing aids, and colorants for the production of extruded articles, said composition containing, per 100 parts by weight of a polyvinyl chloride resin, 50-100 parts by weight of glass fibers having a diameter of between 5 and 25 μm with a length up to 12 mm, and 5-25 parts by weight of a mineral filler having an average particle diameter of below 50 μm and exhibiting a modulus of elasticity in the extrusion direction of an extruded product of at least 8,000N/mm 2 at 23° C.
Claim 3
Dependent Claim
69 words
A composition according to claim 1, wherein additionally up to 30 parts by weight of polymeric modifier for enhancing the impact strength of a extruded product formed from said composition is contained therein, said composition exhibiting modulus of elasticity in the extrusion direction of the extruded product of at least 10,000N/mm 2 at 23° C. and an elongation at break in the transverse direction on the order of 2%.
Claim 4
Dependent Claim
19 words
A composition according to claim 1, wherein additionally 2.5-5.5 parts by weight of mold release agent is contained therein.
Claim 5
Dependent Claim
80 words
A composition according to claim 2, wherein said composition contains, per 100 parts by weight of the polyvinyl chloride resin, 50-80 parts by weight of glass fibers having a diameter of between 5 and 25 μm with a length of 0.5-12 mm, 5-15 parts by weight of a powdery mineral filler having an average particle diameter of below 50 μm, 2.5-5.0 parts by weight of a mold release agent, and up to 30 parts by weight of the polymeric modifier.
Claim 6
Dependent Claim
34 words
A molded article obtained by extrusion from the glass fiber-reinforced polyvinyl chloride composition according to claim 1 exhibiting a modulus of elasticity in the extrusion direction of at least 8000N/mm 2 at 23° C.
References Cited (Backward Citations)
US3632366A
Cited
US3644271A
Cited
US3766131A
Cited
US3883473A
Cited
US3932573A
Cited
GB1498450A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-06-19 | 1987-12-19 | 1988-06-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-06-19 | 1991-12-19 | 1992-06-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-06-19 | 1995-12-19 | 1996-06-19 | $7700.00 | Window Closed / Lapsed |