Permanent dental restorative material
Assignee: BTG International Inc
•
Filing: 1982-08-26
•
Granted: 1984-02-28
•
Expires: 2002-08-26
Abstract
Abstract Wear-resistant, high compressive strength permanent dental restorations are prepared from novel compositions comprising (a) a liquid monomer system comprised of one or more monoethylenically unsaturated monomers and one or more polyethylenically unsaturated monomers, (b) a solid particulate system insoluble in the liquid monomer system (a) comprised of a mixture of both organic and inorganic particulate substances, and (c) a free radical initiator system.
Inventors
- 👤 Robert P. Fellman
- 👤 Marvin J. Hurwitz
- 👤 Robert M. Myers
- 👤 Gerald F. Slack
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 16:48
CPC Classifications
C; C08; C08F; C08F259/00; C08F259/08; A; A61; A61K; A61K6/00; A61K6/80; A61K6/884; A61K6/887; C08F283/00; C08F283/04; C08F283/06
Claims Analysis
Total Claims: 31
Claim 1
Independent Claim
155 words
Composition useful for preparing permanent dental restorations having high compressive strength, wear resistance and a coefficient of friction of not greater than 0.3 comprising: (a) about 10 to 60 parts by weight of a liquid monomer system comprised of one or more monoethylenically unsaturated monomers and about 10% to 80% by weight, based on said liquid monomer system, of one or more polyethylenically unsaturated crosslinking monomers, said monomer system, containing at least 70%, by weight of said monomer system, of acrylic monomer; (b) about 40 to 90 parts by weight of a mixture of (1) organic polymeric particulate substance insoluble in said liquid monomer system selected from the class consisting of poly(ethylene-co-chlorotrifluoroethylene), poly(vinylidene fluoride), nylon and polyacetal and (2) inorganic particulate substance insoluble in said liquid monomer system wherein the weight ratio of the organic particulate substance to inorganic particulate substance is from about 2:1 to about 10:1; and (c) a free radical initiator system.
Claim 2
Dependent Claim
155 words
Composition useful for preparing permanent dental restorations having high compressive strength, wear resistance and a coefficient of friction of not greater than 0.3 comprising: (a) about 10 to 60 parts by weight of a liquid monomer system comprised of one or more monoethylenically unsaturated monomers and about 10% to 80% by weight, based on said liquid monomer system, of one or more polyethylenically unsaturated crosslinking monomers, said monomer system, containing at least 70%, by weight of said monomer system, of acrylic monomer; (b) about 40 to 90 parts by weight of a mixture of (1) organic polymeric particulate substance insoluble in said liquid monomer system selected from the class consisting of poly(ethylene-co-chlorotrifluoroethylene), poly(vinylidene fluoride), nylon and polyacetal and (2) inorganic particulate substance insoluble in said liquid monomer system wherein the weight ratio of the organic particulate substance to inorganic particulate substance is from about 2:1 to about 10:1; and (c) a free radical initiator system.
Claim 3
Dependent Claim
29 words
A composition according to claim 1 wherein at least about 97 percent, by weight of the total inorganic particulate substance has a Moh hardness of up to about 5.
Claim 4
Dependent Claim
14 words
A composition according to claim 1 wherein said monoethylenically unsaturated monomer is methyl methacrylate.
Claim 5
Dependent Claim
42 words
A composition according to claim 1 wherein said monoethylenically unsaturated monomer or monomers are selected from the group consisting of those having glass transition temperatures of about 50° to about 120° C. if polymerized in the absence of said polyethylenically unsaturated monomer.
Claim 6
Dependent Claim
19 words
A composition according to claim 4 wherein said glass transition temperature is from about 65° to about 110° C.
Claim 7
Dependent Claim
35 words
A composition according to claim 1 wherein said mixture of (1) organic polymeric particulate substance and (2) inorganic particulate substance is present in an amount of from about 50 to about 70 parts by weight.
Claim 8
Dependent Claim
25 words
A composition according to claim 1 wherein said inorganic particulate substance has an average particle diameter of from about 0.1 micron to about 75 microns.
Claim 9
Dependent Claim
41 words
A composition according to claim 1 wherein said inorganic particulate substance is selected from the group consisting of calcium hydroxyapatite, calcium carbonate, stearate coated calcium carbonate, calcium metasilicate, talc, clay, calcium sulfate, quartz, silica, glass beads, glass fibers, and combinations thereof.
Claim 10
Dependent Claim
26 words
A composition according to claim 1 wherein the average particle diameter of said organic polymeric particulate substance is from about 0.1 micron to about 75 microns.
Claim 11
Dependent Claim
17 words
A composition according to claim 1 wherein said free radical initiator system is a redox initiator system.
Claim 12
Dependent Claim
17 words
A composition according to claim 1 wherein said free radical initiator system is a photochemical initiator system.
Claim 13
Dependent Claim
17 words
A composition according to claim 1 wherein said free radical initiator system is a peroxydicarbonate activated system.
Claim 14
Dependent Claim
21 words
A composition according to claim 10 wherein said redox initiator system is a combination of benzoyl peroxide and an aromatic amine.
Claim 15
Dependent Claim
20 words
A composition according to claim 1 wherein said polyethylenically unsaturated monomer is a polyfunctional acrylate or methacrylate or mixtures thereof.
Claim 16
Dependent Claim
52 words
A composition according to claim 1 wherein said polyethylenically unsaturated monomer is selected from the group consisting of trimethylolpropane trimethacrylate, ethylene glycol dimethacrylate, diethylene glycol dimethacrylate, triethylene glycol dimethacrylate, poly(ethylene glycol) dimethacrylate, butylene glycol dimethacrylate, 1,6-hexanediol dimethacrylate, 1,10-decamethylene glycol dimethacrylate, butylene diacrylate, pentaerythritol tetraacrylate, bis-GMA, divinyl benzene, diallyl maleate, and ethoxylated bis-phenol-A-dimethacrylate.
Claim 17
Dependent Claim
24 words
A composition according to claim 1 wherein said polyethylenically unsaturated monomer comprises about 20 to about 80%, by weight, of the liquid monomer system.
Claim 18
Dependent Claim
26 words
A composition according to claim 1 wherein up to about 80%, by weight of the inorganic particulate substance, has a Moh hardness in excess of 5.
Claim 19
Dependent Claim
35 words
A composition according to claim 1 wherein said monoethylenically unsaturated monomer is selected from the class consisting of ethyl methacrylate, octafluoropentyl methacrylate, hydroxyethyl methacrylate, hexafluoroisopropyl methacrylate, pentafluoropropyl acrylate, pentafluoropropyl methacrylate, heptafluorobutyl acrylate and heptafluorobutyl methacrylate.
Claim 20
Dependent Claim
31 words
A composition according to claim 1 further including one or more of (a) suspension polymers in bead form; (b) finely ground dental restorative resin; and (c) emulsion polymer in bead form.
Claim 21
Dependent Claim
122 words
A composition according to claim 1 wherein said free radical initiator is selected from the class consisting of thermal initiators, redox initiators and photochemical initiators and said redox initiator includes an oxidizing agent and a reducing agent and one of said agents is present in said liquid monomer system and the second agent is present in said mixture of organic particulate substance and inorganic particulate substance, and, when said free radical initiator is a thermal initiator, said thermal initiator is present in said mixture of organic particulate substance and inorganic particulate substance, and when said initiator is a photochemical initiator, said photochemical initiator is present in either the liquid monomer system or the mixture of organic particulate substance and inorganic particulate substance.
Claim 22
Dependent Claim
39 words
A permanent dental restoration having a compressive strength of at least 30,000 psi and a rotary wear value of at least 200 hours/mil made from the composition of any one of claims 1 through 16 and 18 through 20.
Claim 23
Dependent Claim
46 words
A method of making a permanent dental restoration having a compressive strength of at least 20,000 psi and a rotary wear value of at least 200 hours/mil comprising filling a mold with the composition of claim 1, allowing the composition to set, and then to cure.
Claim 24
Independent Claim
264 words
A method of making permanent dental crowns having high compressive strength, wear resistance and a coefficient of friction of not greater than 0.3 comprising (I) mixing (a) a first component comprising about 10 to 60 parts by weight of a liquid monomer system comprised of one or more monoethylenically unsaturated monomers and about 10% to about 80% by weight, based on said liquid monomer system, of one or more polyethylenically unsaturated crosslinking monomers, said monomer system containing at least about 70%, by weight of said monomer system, of acrylic monomer, with (b) a second component comprising about 40 to 90 parts by weight of a mixture of (1) organic polymeric particulate substance insoluble in said liquid monomer system and selected from the class consisting of poly(ethylene-co-chlorotrifluoroethylene), poly(vinylidene fluoride), nylon and polyacetal and (2) inorganic particulate substance insoluble in said liquid monomer system wherein the weight ratio of the organic particulate substance to the inorganic particulate substance is from about 2:1 to about 10:1, said mixing taking place in the presence of a free radical initiator, (II) allowing the resultant mixture to achieve a suitable viscosity, (III) filling a tooth-shaped preformed mold or impression tray with the resultant thickened mixture, and (IV) applying the filled mold or tray to the prepared tooth to which the crown is to be affixed, (V) allowing the composition to set, (VI) removing the resultant set crown from the mouth and then from the mold or impression tray, (VII) finishing and polishing the crown, (VIII) filling the crown with dental cement and placing the dental crown on the prepared tooth.
Claim 25
Independent Claim
264 words
A method of making permanent dental crowns having high compressive strength, wear resistance and a coefficient of friction of not greater than 0.3 comprising (I) mixing (a) a first component comprising about 10 to 60 parts by weight of a liquid monomer system comprised of one or more monoethylenically unsaturated monomers and about 10% to about 80% by weight, based on said liquid monomer system, of one or more polyethylenically unsaturated crosslinking monomers, said monomer system containing at least about 70%, by weight of said monomer system, of acrylic monomer, with (b) a second component comprising about 40 to 90 parts by weight of a mixture of (1) organic polymeric particulate substance insoluble in said liquid monomer system and selected from the class consisting of poly(ethylene-co-chlorotrifluoroethylene), poly(vinylidene fluoride), nylon and polyacetal and (2) inorganic particulate substance insoluble in said liquid monomer system wherein the weight ratio of the organic particulate substance to the inorganic particulate substance is from about 2:1 to about 10:1, said mixing taking place in the presence of a free radical initiator, (II) allowing the resultant mixture to achieve a suitable viscosity, (III) filling a tooth-shaped preformed mold or impression tray with the resultant thickened mixture, and (IV) applying the filled mold or tray to the prepared tooth to which the crown is to be affixed, (V) allowing the composition to set, (VI) removing the resultant set crown from the mouth and then from the mold or impression tray, (VII) finishing and polishing the crown, (VIII) filling the crown with dental cement and placing the dental crown on the prepared tooth.
Claim 26
Dependent Claim
164 words
Composition useful for preparing permanent dental restorations having high compressive strength, resistance and a coefficient of friction of not greater than 0.3 comprising: (a) about 25 to 60 parts, by weight, of a liquid monomer system comprised of one or more monoethylenically unsaturated monomers and about 15 to 50% by weight, based on said liquid monomer system, of a polyethylenically unsaturated crosslinking monomer; (b) about 40 to 75 parts by weight, of a mixture of (1) organic polymeric particulate substance insoluble in said liquid monomer system and selected from the class consisting of poly(ethylene-co-chlorotrifluoroethylene), poly(vinylidene fluoride), nylon and polyacetal and (2) inorganic particulate substance insoluble in said liquid monomer system wherein the weight ratio of the organic to inorganic particulate substance is from about 2:1 to about 10:1 respectively and said inorganic particulate substance is selected from the group consisting of hydroxyapatite, calcium carbonate, stearate coated calcium carbonate, calcium sulfate, calcium metasilicate, talc, clay, and combinations thereof; and (c) a free radical initiator system.
Claim 27
Dependent Claim
164 words
Composition useful for preparing permanent dental restorations having high compressive strength, resistance and a coefficient of friction of not greater than 0.3 comprising: (a) about 25 to 60 parts, by weight, of a liquid monomer system comprised of one or more monoethylenically unsaturated monomers and about 15 to 50% by weight, based on said liquid monomer system, of a polyethylenically unsaturated crosslinking monomer; (b) about 40 to 75 parts by weight, of a mixture of (1) organic polymeric particulate substance insoluble in said liquid monomer system and selected from the class consisting of poly(ethylene-co-chlorotrifluoroethylene), poly(vinylidene fluoride), nylon and polyacetal and (2) inorganic particulate substance insoluble in said liquid monomer system wherein the weight ratio of the organic to inorganic particulate substance is from about 2:1 to about 10:1 respectively and said inorganic particulate substance is selected from the group consisting of hydroxyapatite, calcium carbonate, stearate coated calcium carbonate, calcium sulfate, calcium metasilicate, talc, clay, and combinations thereof; and (c) a free radical initiator system.
Claim 28
Dependent Claim
14 words
A composition according to claim 24 wherein said monoethylenically unsaturated monomers is methyl methacrylate.
Claim 29
Dependent Claim
20 words
A composition according to claim 24 wherein said inorganic particulate substance has a Moh hardness of up to about 5.
Claim 30
Dependent Claim
42 words
A composition according to claim 24 wherein up to about 3% by weight, based on the weight of inorganic particulate substance present, includes an inorganic particulate substance selected from the class consisting of glass beads, quartz, silica, glass fibers, and combinations thereof.
Claim 31
Dependent Claim
42 words
A composition according to claim 24 wherein up to about 80% by weight, based on the weight of inorganic particulate substance present, includes an inorganic particulate substance selected from the class consisting of glass beads, quartz, silica, glass fibers and combinations thereof.
References Cited (Backward Citations)
US2558139A
Cited
GB982814A
Cited
US3923740A
Cited
US3647498A
Cited
US4197234A
Cited
US4302376A
Cited
US4288221A
Cited
US4340532A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-02-27 | 1987-08-29 | 1988-02-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-02-27 | 1991-08-29 | 1992-02-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-02-27 | 1995-08-29 | 1996-02-28 | $7700.00 | Window Closed / Lapsed |