Blister-free direct bonding of metals to ceramics and metals
Assignee: Intersil Corp
•
Filing: 1981-04-16
•
Granted: 1983-10-11
•
Expires: 2001-04-16
Abstract
Abstract Large-area, blister-free assemblies of direct-bonded metal to a ceramic or metal substrate are obtained by providing venting channels in the metal-substrate interface. The channels may be formed in the metal or substrate surface to be bonded. The channels in the metal may be formed by etching, while the channels in the ceramic may be formed by mechanical techniques, such as grinding. The metal-to-substrate direct bond may be formed by any conventional processes employing an eutectic melt composition to bond the metal to the substrate.
Inventors
- 👤 Eric P. Jochym
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 18:10
CPC Classifications
B; B32; B32B; B32B15/00; B32B15/04; B23; B23K; B23K35/00; B23K35/001; C; C04; C04B; C04B35/00; C04B35/622; C04B35/626; C04B35/63; C04B35/6303; C04B35/653; C04B37/00; C04B37/02; C04B37/021; H; H05; H05K; H05K3/00; H05K3/38; H10; H10W; H10W70/00; H10W70/01; H10W70/04; H10W70/047; B32B2315/00; B32B2315/02; C04B2235/00; C04B2235/65; C04B2235/656; C04B2237/00; C04B2237/30; C04B2237/32; C04B2237/34; C04B2237/341; C04B2237/343; C04B2237/40; C04B2237/402; C04B2237/403; C04B2237/405; C04B2237/406; C04B2237/407; C04B2237/408; C04B2237/50; C04B2237/52; C04B2237/525; C04B2237/62; C04B2237/70; C04B2237/704; C04B2237/706; H05K1/00; H05K1/02; H05K1/03; H05K1/0306; H05K2201/00; H05K2201/03; H05K2201/0332; H05K2201/0335; H05K2201/0355; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12229; Y10T428/12292; Y10T428/12493; Y10T428/12771; Y10T428/12861; Y10T428/12903; Y10T428/1291; Y10T428/24; Y10T428/24479; Y10T428/24521; Y10T428/24537; Y10T428/2457; Y10T428/24628; Y10T428/24661
Claims Analysis
Total Claims: 34
Claim 1
Independent Claim
93 words
A large area, blister-free assembly formed by direct bonding a metal to a substrate comprising: a first substrate having two major surfaces; and a first metallic sheet direct bonded to one of the major surfaces of said first substrate and having a thickness of less than about 0.010 inch, the interface between said first metallic sheet and said first substrate including an eutectic composition, at least one of the surfaces forming said interface including therein a first plurality of channels providing means for venting gases from said interface during the direct bonding operation.
Claim 2
Dependent Claim
93 words
A large area, blister-free assembly formed by direct bonding a metal to a substrate comprising: a first substrate having two major surfaces; and a first metallic sheet direct bonded to one of the major surfaces of said first substrate and having a thickness of less than about 0.010 inch, the interface between said first metallic sheet and said first substrate including an eutectic composition, at least one of the surfaces forming said interface including therein a first plurality of channels providing means for venting gases from said interface during the direct bonding operation.
Claim 3
Dependent Claim
67 words
The assembly of claim 1 including a second metallic sheet direct bonded to the other major surface of said first substrate, the interface between said second metallic sheet and said first substrate including an eutectic composition, at least one of the surfaces forming the last-mentioned interface including therein a second plurality of channels providing means for venting gases from the last-mentioned interface during the direct bonding operation.
Claim 4
Dependent Claim
31 words
The assembly of claim 2 wherein said first and second metallic sheets each comprises a metal selected from the group consisting of aluminum, copper, nickel, cobalt, iron, silver, chromium, and molybdenum.
Claim 5
Dependent Claim
23 words
The assembly of claim 3 wherein said first and second pluralities of channels are formed in said first and second metallic members, respectively.
Claim 6
Dependent Claim
12 words
The assembly of claim 4 wherein said first substrate comprises a metal.
Claim 7
Dependent Claim
12 words
The assembly of claim 4 wherein said first substrate comprises a ceramic.
Claim 8
Dependent Claim
39 words
The assembly of claim 6 wherein said ceramic comprises a material selected from the group consisting of alumina (Al 2 O 3 ), beryllia (BeO), zinc oxide (ZnO), silicon dioxide (SiO 2 ), and barium titanate (BatiO 3 ).
Claim 9
Dependent Claim
25 words
The assembly of claim 2, wherein said first and second pluralities of channels are formed in each of the major surfaces of said first substrate.
Claim 10
Dependent Claim
12 words
The assembly of claim 8 wherein said first substrate comprises a ceramic.
Claim 11
Dependent Claim
39 words
The assembly of claim 9 wherein said ceramic comprises a material selected from the group consisting of alumina (Al 2 O 3 ), beryllia (BeO), zinc oxide (ZnO), silicon dioxide (SiO 2 ), and barium titanate (BaTiO 3 ).
Claim 12
Dependent Claim
31 words
The assembly of claim 9 wherein said first and second metallic sheets each comprises a metal selected from the group consisting of aluminum, copper, nickel, cobalt, iron, silver, chromium, and molybdenum.
Claim 13
Dependent Claim
61 words
The assembly of claim 2 including a second substrate direct bonded to the outer surface of said first metallic sheets, the interface between said second substrate and said first metallic sheet including an eutectic composition, at least one of the surfaces forming the last-mentioned interface including therein a third plurality of channels providing means for venting gases from the last-mentioned interface.
Claim 14
Dependent Claim
27 words
The assembly of claim 12 wherein said first metallic comprises a metal selected from the group consisting of aluminum, copper, nickel, cobalt, iron, silver, chromium, and molybdenum.
Claim 15
Dependent Claim
35 words
The assembly of claim 13 wherein said first and third pluralities of channels are formed on each of the surfaces of said first metallic sheet forming an interface with said first and second substrates, respectively.
Claim 16
Dependent Claim
15 words
The assembly of claim 13 wherein said first and second substrates each comprises a ceramic.
Claim 17
Dependent Claim
39 words
The assembly of claim 15 wherein said ceramic comprises a material selected from the group consisting of alumina (Al 2 O 3 ), beryllia (BeO), zinc oxide (ZnO), silicon dioxide (SiO 2 ), and barium titanate (BaTiO 3 ).
Claim 18
Dependent Claim
35 words
The assembly of claim 16 wherein said first and third pluralities of channels are formed on each of the major surfaces of said first and second substrates forming an interface with said first metallic sheet.
Claim 19
Dependent Claim
51 words
The assembly of claim 1 wherein said first metallic sheet comprises copper, said first substrate comprises a ceramic selected from the group consisting of alumina (Al 2 O 3 ) and beryllia (BeO), and wherein said first plurality of channels is photoetched on the inner surface of said first metallic sheet.
Claim 20
Dependent Claim
162 words
In a method for direct bonding a metal sheet to a substrate wherein said metal sheet has a thickness of less than about 0.010 inch, said method being of the type employing a bonding agent compatible with said substrate so as to form an eutectic with said metal sheet, said eutectic consisting predominantly of said metal sheet and exhibiting an eutectic temperature lower than the melting point of said metal sheet such that heating said metal sheet having an eutectic formed thereon, while said metal sheet is in close contact with said substrate, to at least the eutectic temperature but below the melting point of said metal sheet causes said eutectic to wet said substrate and form a direct bond therewith upon cooling, the improvement comprising the step of: forming a plurality of channels in at least one of the surfaces forming said direct bond, said channels providing means for venting gases from the interface between said metal sheet and said substrate.
Claim 21
Dependent Claim
162 words
In a method for direct bonding a metal sheet to a substrate wherein said metal sheet has a thickness of less than about 0.010 inch, said method being of the type employing a bonding agent compatible with said substrate so as to form an eutectic with said metal sheet, said eutectic consisting predominantly of said metal sheet and exhibiting an eutectic temperature lower than the melting point of said metal sheet such that heating said metal sheet having an eutectic formed thereon, while said metal sheet is in close contact with said substrate, to at least the eutectic temperature but below the melting point of said metal sheet causes said eutectic to wet said substrate and form a direct bond therewith upon cooling, the improvement comprising the step of: forming a plurality of channels in at least one of the surfaces forming said direct bond, said channels providing means for venting gases from the interface between said metal sheet and said substrate.
Claim 22
Dependent Claim
25 words
The method of claim 19 wherein said metal sheet comprises one of the group consisting of aluminum, copper, nickel, cobalt, iron, silver, chromium, and molybdenum.
Claim 23
Dependent Claim
11 words
The method of claim 20 wherein said substrate comprises a metal.
Claim 24
Dependent Claim
11 words
The method of claim 20 wherein said substrate comprises a ceramic.
Claim 25
Dependent Claim
39 words
The method of claim 22 wherein said ceramic comprises a material selected from the group consisting of alumina (Al 2 O 3 ), beryllia (BeO), zinc oxide (ZnO), silicon dioxide (SiO 2 ), and barium titanate (BaTiO 3 ).
Claim 26
Dependent Claim
17 words
The method of claim 23 wherein said channels are formed by being photoetched in said metal sheet.
Claim 27
Dependent Claim
14 words
The method of claim 23 wherein said channels are formed in said ceramic substrate.
Claim 28
Dependent Claim
26 words
The methods of claims 24 or 25 wherein said eutectic is formed by heating said metal sheet in a reactive atmosphere which includes said bonding agent.
Claim 29
Dependent Claim
17 words
The method of claim 26 wherein said metal sheet comprises copper and said reactive atmosphere comprises oxygen.
Claim 30
Dependent Claim
27 words
The method of claim 26 wherein said metal sheet comprises electrolyte tough pitch copper having sufficient oxygen dissolved or precipitated therein to form said eutectic upon heating.
Claim 31
Independent Claim
38 words
The method of claims 24 or 25 wherein said direct bonding agent is selectively applied to said metal sheet and wherein said eutectic is formed upon heating said metal sheet and said bonding agent in an inert atmosphere.
Claim 32
Dependent Claim
25 words
The method of claim 29 wherein said bonding agent is applied to the side of said metal sheet opposite the side which forms the interface.
Claim 33
Dependent Claim
20 words
The method of claim 30 wherein said metal sheet comprises copper and said bonding agent comprises a chemical oxidizing agent.
Claim 34
Dependent Claim
30 words
The method of claim 29 wherein said metal sheet comprises electrolyte tough pitch copper having a sufficient quantity of oxygen dissolved or precipitated therein to form said eutectic upon heating.
References Cited (Backward Citations)
DE1127179B
Cited
US3284176A
Cited
US3337947A
Cited
US3541225A
Cited
US3766634A
Cited
US3911553A
Cited
US3994430A
Cited
US4061263A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-10-10 | 1987-04-11 | 1987-10-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-10-10 | 1991-04-11 | 1991-10-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-10-10 | 1995-04-11 | 1995-10-11 | $7700.00 | Window Closed / Lapsed |