Fabrication of electrical conductor by replacement of metallic powder in polymer with more noble metal
Assignee: Von Roll Isola USA Inc
•
Filing: 1980-12-29
•
Granted: 1983-09-13
•
Expires: 2000-12-29
Abstract
Abstract A low-cost conductor, e.g. a printed circuit, is prepared by applying a mixture of a metallic powder and polymer on a substrate and curing the polymer, followed by an augmentation replacement reaction being effected to replace some of the metallic powder with a more noble metal in such a way that the total volume of deposited metal on the surface exceeds that of the original metal powder at that surface. This procedure produces contiguous layer of conducting metal on the substrate. The conductors thus formed can easily be soldered without leaching using a conventional tin-lead solders.
Inventors
- 👤 Charles W. Eichelberger
- 👤 Robert J. Wojnarowski
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 02:11
CPC Classifications
H; H05; H05K; H05K3/00; H05K3/22; H05K3/24; H05K3/245; H05K3/246; H05K1/00; H05K1/02; H05K1/09; H05K1/092; H05K1/095
Claims Analysis
Total Claims: 100
Claim 1
Independent Claim
199 words
A method for forming an electrical conductor in desired areas of a substrate, which comprises the steps of: applying a desired design to said substrate with an ink composition comprising a finely divided metallic powder having at least a first metal therein and a curable polymer; at least partially curing said curable polymer to cause volumetric shrinkage thereof; adjusting the amount of the finely divided powder to be about 60-80% by volume of said ink composition after the ink is at least partially cured; and contacting the at least partially cured ink composition of the desired design with a metal salt solution of a second metal in which the second metal cation is more noble that at least the first metal of finely divided powder and the anion of said metal salt forms soluble salts with both said cation and at least the first metal of said finely divided powder, to cause said second metal of said metal salt solution to plate out as a contiguous layer on the surface of said ink composition and with a volume of said second metal on said surface greater than the volume of the metal of said powder removed from said surface.
Claim 2
Independent Claim
199 words
A method for forming an electrical conductor in desired areas of a substrate, which comprises the steps of: applying a desired design to said substrate with an ink composition comprising a finely divided metallic powder having at least a first metal therein and a curable polymer; at least partially curing said curable polymer to cause volumetric shrinkage thereof; adjusting the amount of the finely divided powder to be about 60-80% by volume of said ink composition after the ink is at least partially cured; and contacting the at least partially cured ink composition of the desired design with a metal salt solution of a second metal in which the second metal cation is more noble that at least the first metal of finely divided powder and the anion of said metal salt forms soluble salts with both said cation and at least the first metal of said finely divided powder, to cause said second metal of said metal salt solution to plate out as a contiguous layer on the surface of said ink composition and with a volume of said second metal on said surface greater than the volume of the metal of said powder removed from said surface.
Claim 3
Dependent Claim
20 words
The method of claim 1, wherein said finely divided metal has a particle size of less than about 50 microns.
Claim 4
Dependent Claim
19 words
The method of claim 2, wherein said finely divided metallic powder has a particle size of about 3-25 microns.
Claim 5
Dependent Claim
20 words
The method of claim 3, wherein said finely divided metallic powder has a particle size of less than 10 microns.
Claim 6
Dependent Claim
17 words
The method of claim 1, wherein said polymer is adapted to thermally cure at about 140°-200° C.
Claim 7
Dependent Claim
16 words
The method of claim 1, wherein said finely divided metallic powder is about 70% by volume.
Claim 8
Dependent Claim
27 words
The method of claim 1, further including the step of drying and curing said ink composition before contacting the cured ink composition with said metal salt solution.
Claim 9
Dependent Claim
24 words
The method of claim 1, in which said metal salt solution is an inorganic solution containing 0.1 molar to saturation of said metal salt.
Claim 10
Dependent Claim
20 words
The method of claim 8, wherein said metal salt solution is an aqueous solution containing about 0.5-2.0 molar metal salt.
Claim 11
Dependent Claim
13 words
The method of claim 9, wherein said metal salt solution is 1 molar.
Claim 12
Dependent Claim
14 words
The method of claim 1, wherein said finely divided metallic powder comprises iron .
Claim 13
Dependent Claim
37 words
The method of claim 11, wherein said finely divided metallic powder comprises about 25-40% by weight of iron, about 10-25% by weight of aluminum, about 15-30% by weight of tin and about 20-35% by weight of copper.
Claim 14
Dependent Claim
37 words
The method of claim 12, wherein said finely divided metallic powder comprises about 30-35% by weight of iron, about 15-20% by weight of aluminum, about 20-25% by weight of tin and about 25-30% by weight of copper.
Claim 15
Dependent Claim
25 words
The method of claim 1, wherein said finely divided metallic powder comprises about 15-45% by weight of zinc and about 55-85% by weight of nickel.
Claim 16
Dependent Claim
25 words
The method of claim 14, wherein said finely divided metallic powder comprises about 25% by weight of zinc and about 75% by weight of nickel.
Claim 17
Dependent Claim
20 words
The method of claim 1, in which a third metal is applied to said contiguous layer of said second metal.
Claim 18
Dependent Claim
11 words
The method of claim 16, wherein said third metal is tin.
Claim 19
Independent Claim
14 words
The method of claims 1 or 17, in which said second metal is copper.
Claim 20
Dependent Claim
29 words
The method of claim 1, wherein the surface of said at least partially cured polymer is abraded not later than the step of contacting with said metal salt solution.
Claim 21
Dependent Claim
33 words
The method of claim 19, wherein said metal salt solution is an aqueous copper sulfate solution and wherein said surface is abraded with an amount of copper sulfate beyond the solution saturation amount.
Claim 22
Dependent Claim
35 words
The method of claim 1, wherein a resistive material is applied on said substrate in contact with said at least partially cured polymer before the step of contacting said substrate with said metal salt solution.
Claim 23
Dependent Claim
45 words
The method of claim 21, in which said resistive material is a thick film resistor and said ink composition is applied to said substrate so as to overlap a portion of said resistor to form an electrical junction therebetween as a consequence of said contacting.
Claim 24
Dependent Claim
47 words
The method of claim 21, wherein said resistive material is a thick film resistor and is applied to said substrate so as to partially overlap a portion of said at least partially cured curable polymer to form an electrical junction therebetween as a consequence of said contacting.
Claim 25
Dependent Claim
26 words
The method of claim 23, wherein said thick film resistor contains a metal which is less noble than said metal cation of said metal salt solution.
Claim 26
Dependent Claim
21 words
The method of claim 1, wherein an electrically conductive member is positioned in said polymer before said polymer is completely cured.
Claim 27
Dependent Claim
12 words
The method of claim 1, wherein said ink composition includes a solvent.
Claim 28
Dependent Claim
18 words
The method of claim 26, wherein said solvent has a viscosity of about 15,000-200,000 centipoises at room temperature.
Claim 29
Dependent Claim
17 words
The method of claim 27, wherein said solvent has a viscosity of 50,000-150,000 centipoises at room temperature.
Claim 30
Dependent Claim
27 words
The method of claim 26, further including the step of drying and curing said ink composition before contacting the cured ink composition with said metal salt solution.
Claim 31
Dependent Claim
40 words
The method of claim 29, wherein said curable polymer is a polyester thermally curable at about 150°-180° C.; said solvent is a diethylene glycol monobutyl ether; and wherein said drying is effected at about 70°-150° C. for about 0.1-1.0 hour.
Claim 32
Dependent Claim
18 words
The method of claim 30, wherein said drying is effected at about 110°-130° C. for about 0.25-0.50 hour.
Claim 33
Dependent Claim
17 words
The method of claim 26, wherein said polymer is adapted to thermally cure at about 140°-200° C.
Claim 34
Dependent Claim
16 words
The method of claim 26, wherein said finely divided metallic powder is about 70% by volume.
Claim 35
Independent Claim
71 words
A method for forming an electrical conductor in desired areas of a substrate, comprising the steps of: (a) adhering to said substrate in a desired pattern a polymer containing a finely-divided powdered metal, said finely-divided powdered metal comprising about 60-80% by volume of the total of said polymer and said powdered metal; and (b) replacing a portion of said finely-divided powdered metal with another metal more noble than said powdered metal.
Claim 36
Independent Claim
71 words
A method for forming an electrical conductor in desired areas of a substrate, comprising the steps of: (a) adhering to said substrate in a desired pattern a polymer containing a finely-divided powdered metal, said finely-divided powdered metal comprising about 60-80% by volume of the total of said polymer and said powdered metal; and (b) replacing a portion of said finely-divided powdered metal with another metal more noble than said powdered metal.
Claim 37
Dependent Claim
46 words
The method of claim 34, wherein step (a) comprises the steps of: applying to said substrate a desired pattern of an ink composition comprising said finely-divided powdered metal and a curable polymer; and at least partially curing said curable polymer to cause a volumetric shrinkage thereof.
Claim 38
Independent Claim
73 words
The method of claims 34 or 35, wherein step (b) comprises the step of contacting said polymer with a solution of a salt of said another metal for sufficient time such that said portion of said finely-divided powdered metal enters into said solution from said polymer, is replaced therein with said another metal, and a contiguous layer of an additional quantity of said second metal is formed upon a surface of said polymer.
Claim 39
Dependent Claim
12 words
The method of claim 36, wherein said ink composition includes a solvent.
Claim 40
Dependent Claim
18 words
The method of claim 37, wherein said solvent has a viscosity of about 15,000-200,000 centipoises at room temperature.
Claim 41
Dependent Claim
17 words
The method of claim 38, wherein said solvent has a viscosity of 50,000-150,000 centipoises at room temperature.
Claim 42
Dependent Claim
17 words
The method of claim 37, wherein said polymer is adapted to thermally cure at about 140°-200° C.
Claim 43
Dependent Claim
15 words
The method of claim 37, wherein said finely-divided powdered metal is about 70% by volume.
Claim 44
Dependent Claim
28 words
The method of claim 37, further including the step of drying and curing said polymer before replacing said portion of said finely-divided powdered metal with said another metal.
Claim 45
Dependent Claim
39 words
The method of claim 42, wherein said curable polymer is a polyester thermally curable at about 150°-180° C.; said solvent is a diethylene glycol monobutyl ether; and wherein said drying is effected at about 70°-150° C. for 0.1-1.0 hour.
Claim 46
Dependent Claim
18 words
The method of claim 43, wherein said drying is effected at about 100°-130° C. for about 0.25-0.50 hour.
Claim 47
Dependent Claim
23 words
The method of claim 36, wherein said metal salt solution is an organic solution containing 0.1 molar to saturation of said metal salt.
Claim 48
Dependent Claim
20 words
The method of claim 45, wherein said metal salt solution is an aqueous solution containing about 0.5-2.0 molar metal salt.
Claim 49
Dependent Claim
13 words
The method of claim 46, wherein said metal salt solution is 1 molar.
Claim 50
Dependent Claim
12 words
The method of claim 36, wherein said finely-divided powdered metal comprises iron.
Claim 51
Dependent Claim
36 words
The method of claim 48, wherein said finely-divided powdered metal comprises about 25-40% by weight of iron, about 10-25% by weight of aluminum, about 15-30% by weight of tin and about 20-35% by weight of copper.
Claim 52
Dependent Claim
36 words
The method of claim 49, wherein said finely-divided powdered metal comprises about 30-35% by weight of iron, about 15-20% by weight of aluminum, about 20-25% by weight of tin and about 25-30% by weight of copper.
Claim 53
Dependent Claim
25 words
The method of claim 36, wherein said finely divided powdered metal comprises about 15-45% by weight of zinc and about 55-85% by weight of nickel.
Claim 54
Dependent Claim
25 words
The method of claim 51, wherein said finely divided powdered metal comprises about 25% by weight of zinc and about 75% by weight of nickel.
Claim 55
Dependent Claim
19 words
The method of claim 36, wherein a third metal is applied to said additional quantity of said another metal.
Claim 56
Dependent Claim
11 words
The method of claim 53, wherein said third metal is tin.
Claim 57
Dependent Claim
11 words
The method of claim 54, wherein said another metal is copper.
Claim 58
Dependent Claim
11 words
The method of claim 36, wherein said another metal is copper.
Claim 59
Dependent Claim
33 words
The method of claim 56, wherein said metal salt solution is an aqueous copper sulfate solution and wherein said polymer is abraded with an amount of copper sulfate beyond the solution saturation amount.
Claim 60
Dependent Claim
25 words
The method of claim 36, wherein the surface of said polymer is abraded not later than the step of contacting with said metal salt solution.
Claim 61
Dependent Claim
32 words
The method of claim 36, wherein a resistive material is applied to said substrate in contact with said polymer, prior to the step of contacting said substrate with said metal salt solution.
Claim 62
Dependent Claim
43 words
The method of claim 59, wherein said resistive material is a thick-film resistor and said ink composition is applied to said substrate so as to overlap a portion of said resistor to form an electrical junction therebetween as a consequence of said contacting.
Claim 63
Dependent Claim
41 words
The method of claim 59, wherein said resistive material is a thick-film resistor and is applied to said substrate so as to partially overlap a portion of said polymer to form an electrical junction therebetween as a consequence of said contacting.
Claim 64
Dependent Claim
24 words
The method of claim 61, wherein said thick film resistor contains a metal which is less noble than the cation of said another metal.
Claim 65
Dependent Claim
21 words
The method of claim 36, wherein an electrically conductive member is positioned in said polymer before said polymer is completely cured.
Claim 66
Dependent Claim
21 words
The method of claim 34, wherein said finely divided powdered metal has a particle size of less than about 50 microns.
Claim 67
Dependent Claim
19 words
The method of claim 64, wherein said finely divided powdered metal has a particle size of about 3-35 microns.
Claim 68
Dependent Claim
20 words
The method of claim 65, wherein said finely divided powdered metal has a particle size of less than 10 microns.
Claim 69
Independent Claim
109 words
A method for providing selected areas of greater electrical conductivity on the surface of a substrate of lesser electrical conductivity, comprising the steps of: (a) applying only to said selected areas a coating of a polymeric insulation material containing a dispersion of powdered metal of about 60-80% by volume of said coating; and (b) contacting said coating with a solution containing a metal more noble than the effective ingredients of said powdered metal and forming a film of the more noble metal contiguous with the surface of said polymeric insulating material, with a contiguous conductive film of said more noble metal overlying only the selected areas of said substrate.
Claim 70
Independent Claim
109 words
A method for providing selected areas of greater electrical conductivity on the surface of a substrate of lesser electrical conductivity, comprising the steps of: (a) applying only to said selected areas a coating of a polymeric insulation material containing a dispersion of powdered metal of about 60-80% by volume of said coating; and (b) contacting said coating with a solution containing a metal more noble than the effective ingredients of said powdered metal and forming a film of the more noble metal contiguous with the surface of said polymeric insulating material, with a contiguous conductive film of said more noble metal overlying only the selected areas of said substrate.
Claim 71
Dependent Claim
12 words
The method of claim 67, wherein said coating further includes a solvent.
Claim 72
Dependent Claim
18 words
The method of claim 68, wherein said solvent has a viscosity of about 15,000-200,000 centipoises at room temperature.
Claim 73
Dependent Claim
17 words
The method of claim 69, wherein said solvent has a viscosity of 50,000-150,000 centipoises at room temperature.
Claim 74
Dependent Claim
18 words
The method of claim 68, wherein said polymeric insulating material is curable and undergoes volumetric shrinking upon curing.
Claim 75
Dependent Claim
19 words
The method of claim 68, wherein said polymeric insulating material is adapted to thermally cure at about 140°-200° C.
Claim 76
Dependent Claim
14 words
The method of claim 68, wherein said powdered metal is about 70% by volume.
Claim 77
Dependent Claim
23 words
The method of claim 68, further including the step of simultaneously drying and curing said coating before contacting said coating with said solution.
Claim 78
Dependent Claim
40 words
The method of claim 74, wherein said curable polymer is a polyester thermally curable at about 150°-180° C.; said solvent is a diethylene glycol monobutyl ether; and wherein said drying is effected at about 70°-150° C. for about 0.1-1.0 hour.
Claim 79
Dependent Claim
18 words
The method of claim 75, wherein said drying is effected at about 110°-130° C. for about 0.25-0.50 hour.
Claim 80
Dependent Claim
19 words
The method of claim 67, wherein said powdered metal has a particle size of less than about 50 microns.
Claim 81
Dependent Claim
17 words
The method of claim 77, wherein said powdered metal has a particle size of about 3-25 microns.
Claim 82
Dependent Claim
18 words
The method of claim 78, wherein said powdered metal has a particle size of less than 10 microns.
Claim 83
Dependent Claim
25 words
The method of claim 67, in which said metal solution is an inorganic solution containing 0.1 molar to saturation of a salt of said metal.
Claim 84
Dependent Claim
20 words
The method of claim 80, wherein said second metal salt solution is aqueous solution containing about 0.5-2.0 molar metal salt.
Claim 85
Dependent Claim
13 words
The method of claim 81, wherein said metal salt solution is 1 molar.
Claim 86
Dependent Claim
11 words
The method of claim 67, wherein said powdered metal comprises iron.
Claim 87
Dependent Claim
35 words
The method of claim 83, wherein said powdered metal comprises about 25-40% by weight of iron, about 10-25% by weight of aluminum, about 15-30% by weight of tin and about 20-35% by weight of copper.
Claim 88
Dependent Claim
35 words
The method of claim 84, wherein said powdered metal comprises about 30-35% by weight of iron, about 15-20% by weight of aluminum, about 20-25% by weight of tin and about 25-30% by weight of copper.
Claim 89
Dependent Claim
23 words
The method of claim 67, wherein said powdered metal comprises about 15-45% by weight of zinc and about 55-85% by weight of nickel.
Claim 90
Dependent Claim
23 words
The method of claim 86, wherein said powdered metal comprises about 25% by weight of zinc and about 75% by weight of nickel.
Claim 91
Dependent Claim
22 words
The method of claim 67, further comprising the step of applying another metal to the conductive film of said more noble metal.
Claim 92
Dependent Claim
11 words
The method of claim 88, wherein said another metal is tin.
Claim 93
Dependent Claim
14 words
The method of claim 67 or 89, wherein said more noble metal is copper.
Claim 94
Dependent Claim
24 words
The method of claim 67, wherein the surface of said coating is abraded not later than the step of contacting with said metal solution.
Claim 95
Dependent Claim
32 words
The method of claim 91, wherein said metal solution is an aqueous copper sulfate solution and wherein said coating is abraded with an amount of copper sulfate beyond the solution saturation amount.
Claim 96
Dependent Claim
30 words
The method of claim 67, wherein a resistive material is applied on said substrate in contact with said coating before the step of contacting said coating with said metal solution.
Claim 97
Dependent Claim
43 words
The method of claim 93, wherein said resistive material is a thick film resistor and said coating is applied to said substrate so as to overlap a portion of said resistor to form an electrical junction therebetween as a consequence of said contacting.
Claim 98
Dependent Claim
42 words
The method of claim 93, wherein said resistive material is a thick film resistor and is applied to said substrate so as to partially overlap a portion of said coating to form an electrical junction therebetween as a consequence of said contacting.
Claim 99
Dependent Claim
21 words
The method of claim 95, wherein said thick film resistor contains another metal which is less noble than said second metal.
Claim 100
Dependent Claim
21 words
The method of claim 67, wherein an electrically conducting member is positioned in said coating before said coating is completely cured.
References Cited (Backward Citations)
US3226256A
Cited
US3332860A
Cited
US3576662A
Cited
US3764280A
Cited
US3801364A
Cited
US4284665A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-09-12 | 1987-03-14 | 1987-09-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-09-12 | 1991-03-14 | 1991-09-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-09-12 | 1995-03-14 | 1995-09-13 | $7700.00 | Window Closed / Lapsed |