Fe--Cr--Co Magnets by powder metallurgy processing
Assignee: AT&T Inc
•
Filing: 1981-12-07
•
Granted: 1983-08-30
•
Expires: 2001-12-07
Abstract
Abstract Fe--Cr--Co alloys have found application in the manufacture of permanent magnets on account of magnetic properties such as, high coercive force, remanent magnetization, and energy product. A method is disclosed for producing magnetic articles comprising Fe, Cr, and Co from powders comprising elemental or pre-alloyed particles. A powder is mixed with an essentially noncarbonizing organic binder, compressed, heated to remove binder, sintered, and aged. Heating results in essentially complete removal of binder prior to sintering. Magnetic bodies produced according to the disclosed method typically comprise less than 1 weight percent of undesirable nonmagnetic phases and have a maximum energy product of at least 1 million gauss oersted.
Inventors
- 👤 Martin L. Green
- 👤 Richard C. Sherwood
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 17:26
CPC Classifications
H; H01; H01F; H01F1/00; H01F1/01; H01F1/03; H01F1/032; H01F1/04; H01F1/06; H01F1/08; H01F1/086; B; B22; B22F; B22F1/00; B22F1/09; C; C22; C22C; C22C33/00; C22C33/02; C22C33/0257; C22C33/0278; C22C33/0285
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
117 words
Method for producing a magnetic body, said method comprising sintering and aging a compact, said compact having been obtained by compressing a mixture, said mixture comprising metallic particles and a binder material, said method comprising heating prior to sintering to remove said binder from said compact, said mixture comprising at least 50 weight percent Fe, at least 10 weight percent Cr, at least 1 percent Co, and at least 0.1 weight percent of said binder, and said binder consisting essentially of at least one binder material which is selected from the group consisting of fatty acids, amides of fatty acids, and esters of fatty acids, whereby the presence of detrimental nonmagnetic phases in said body is minimized.
Claim 2
Dependent Claim
117 words
Method for producing a magnetic body, said method comprising sintering and aging a compact, said compact having been obtained by compressing a mixture, said mixture comprising metallic particles and a binder material, said method comprising heating prior to sintering to remove said binder from said compact, said mixture comprising at least 50 weight percent Fe, at least 10 weight percent Cr, at least 1 percent Co, and at least 0.1 weight percent of said binder, and said binder consisting essentially of at least one binder material which is selected from the group consisting of fatty acids, amides of fatty acids, and esters of fatty acids, whereby the presence of detrimental nonmagnetic phases in said body is minimized.
Claim 3
Dependent Claim
26 words
Method of claim 1 in which said binder material is present in said mixture in an amount of less than or equal to 10 weight percent.
Claim 4
Dependent Claim
26 words
Method of claim 1 in which said binder material is present in said mixture in an amount of less than or equal to 6 weight percent.
Claim 5
Dependent Claim
35 words
Method of claim 1 in which metallic particles in said mixture predominantly are pre-alloyed particles and in which said binder material is present in said mixture in an amount of at least 1 weight percent.
Claim 6
Dependent Claim
44 words
Method of claim 1 in which said body has a maximum energy product which is greater than or equal to 1 million gauss oersted and in which said detrimental nonmagnetic phases are present in combination in an amount of less than 1 weight percent.
Claim 7
Dependent Claim
14 words
Method of claim 1 in which said particles pass through a 50 mesh sieve.
Claim 8
Dependent Claim
22 words
Method of claim 1 in which compressing said mixture is at a pressure which is greater than or equal to 20 kpsi.
References Cited (Backward Citations)
US2546047A
Cited
US3901742A
Cited
US3954519A
Cited
US3970485A
Cited
US4075437A
Cited
US4174983A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-08-29 | 1987-02-28 | 1987-08-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-08-29 | 1991-02-28 | 1991-08-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-08-29 | 1995-02-28 | 1995-08-30 | $7700.00 | Window Closed / Lapsed |