Abstract
Abstract A method and apparatus for the control of reactive sputtering deposition of oxide-containing films, including the monitoring of and maintaining the constancy of the deposition rate and total pressure of the system by adjustment of the oxygen and argon input flow rates. Deposition rate is monitored by an activated quartz crystal, and behave as a sensitive function of actual oxygen partial pressure. Stoichiometry, optical and electrical properties of the oxide-containing films are therefore controllable by maintaining constant oxygen partial pressure.
Inventors
- 👤 F. Howard Gillery
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 10:42
CPC Classifications
C; C03; C03C; C03C17/00; C03C17/34; C03C17/36; C03C17/3602; C03C17/3613; C03C17/22; C03C17/23; C03C17/245; C03C17/2456; C03C17/3649; C03C17/3652; C03C17/3655; C03C17/3681; C23; C23C; C23C14/00; C23C14/0021; C23C14/0036; C23C14/0042; C03C2217/00; C03C2217/20; C03C2217/21; C03C2217/212; C03C2217/23; C03C2217/231; C03C2217/90; C03C2217/94; C03C2218/00; C03C2218/10; C03C2218/15; C03C2218/154; C03C2218/155
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
123 words
A method of producing a transparent electroconductive article comprising the steps of: a. magnetically sputtering an inner transparent film of titanium oxide onto a transparent substrate surface, said magnetic sputtering conducted in an evacuated environment having partial pressures of oxygen and a chemically inert gas to produce a film having an optical extinction coefficient in the range between about 0.03 and about 0.3; b. depositing a substantially transparent electroconductive film onto the inner titanium oxide film; and c. magnetically sputtering an outer transparent film of titanium oxide onto said electroconductive film, said outer film magnetically sputtered in an evacuated environment having partial pressures of oxygen and a chemically inert gas to produce a film having an optical extinction coefficient less than about 0.3.
Claim 2
Independent Claim
123 words
A method of producing a transparent electroconductive article comprising the steps of: a. magnetically sputtering an inner transparent film of titanium oxide onto a transparent substrate surface, said magnetic sputtering conducted in an evacuated environment having partial pressures of oxygen and a chemically inert gas to produce a film having an optical extinction coefficient in the range between about 0.03 and about 0.3; b. depositing a substantially transparent electroconductive film onto the inner titanium oxide film; and c. magnetically sputtering an outer transparent film of titanium oxide onto said electroconductive film, said outer film magnetically sputtered in an evacuated environment having partial pressures of oxygen and a chemically inert gas to produce a film having an optical extinction coefficient less than about 0.3.
Claim 3
Dependent Claim
29 words
The method as set forth in claim 1 further comprising the step of: maintaining a constant predetermined deposition rate, sputtering power, and atmosphere pressure during steps a and c.
Claim 4
Independent Claim
30 words
The method as set forth in claims 1 or 2 further comprising the step of: monitoring the luminous transmittance of said transparent electroconductive article during steps a, b, and c.
Claim 5
Dependent Claim
23 words
The method as set forth in claim 3 wherein said electroconductive film has a surface resistance less than about 10 ohms per square.
Claim 6
Dependent Claim
28 words
The method as set forth in claim 4 wherein said electroconductive film comprises a metal selected from the group of silver, gold, copper, tin, aluminum, magnesium, or platinum.
Claim 7
Dependent Claim
110 words
The method as set forth in claim 5 wherein said electroconductive film is silver and further comprising the steps of: terminating the step of sputtering said inner transparent film when the monitored luminous transmittance of the article is between about 80% and 85% of the luminous transmittance of the uncoated substrate; terminating the step of depositing said electroconductive film when the monitored luminous transmittance of the article has decreased an additional amount between about 10% and 12% of the luminous transmittance of the uncoated substrate; and terminating the step of sputtering said outer transparent film when the monitored luminous transmittance of said article has increased to about a peak value.
Claim 8
Dependent Claim
33 words
The method as set forth in claim 6 wherein said outer transparent film terminating step is practiced when the monitored luminous transmittance of said article has increased to about its first peak value.
Claim 9
Independent Claim
122 words
A method of producing a transparent electroconductive article comprising the steps of: a. magnetically sputtering an inner transparent film of titanium oxide onto a transparent substrate surface, said magnetic sputtering conducted in an evacuated environment having partial pressures of oxygen and a chemically inert gas controlled to produce a film having greater than 1.7 but less than 2.0 parts oxygen to parts titanium. b. depositing a transparent electroconductive film onto the inner titanium oxide film; and c. magnetically sputtering an outer transparent film of titanium oxide onto said electroconductive film, said outer film magnetically sputtered in an evacuated environment having partial pressures of oxygen and a chemically inert gas to produce a film having an optical extinction coefficient less than about 0.3.
Claim 10
Independent Claim
122 words
A method of producing a transparent electroconductive article comprising the steps of: a. magnetically sputtering an inner transparent film of titanium oxide onto a transparent substrate surface, said magnetic sputtering conducted in an evacuated environment having partial pressures of oxygen and a chemically inert gas controlled to produce a film having greater than 1.7 but less than 2.0 parts oxygen to parts titanium. b. depositing a transparent electroconductive film onto the inner titanium oxide film; and c. magnetically sputtering an outer transparent film of titanium oxide onto said electroconductive film, said outer film magnetically sputtered in an evacuated environment having partial pressures of oxygen and a chemically inert gas to produce a film having an optical extinction coefficient less than about 0.3.
Claim 11
Dependent Claim
29 words
The method as set forth in claim 8 further comprising the step of: maintaining a constant predetermined deposition rate, sputtering power, and atmosphere pressure during steps a and c.
Claim 12
Independent Claim
29 words
The method as set forth in claims 8 or 9 further comprising step of: monitoring the luminous transmittance of said transparent electroconductive article during steps a, b, and c.
Claim 13
Dependent Claim
23 words
The method as set forth in claim 10 wherein said electroconductive film has a surface resistance less than about 10 ohms per square.
Claim 14
Dependent Claim
28 words
The method as set forth in claim 11 wherein said electroconductive film comprises a metal selected from the group of silver, gold, copper, tin, aluminum, magnesium, or platinum.
Claim 15
Dependent Claim
110 words
The method as set forth in claim 12 wherein said electroconductive film is silver and further comprising the steps of: terminating the step of sputtering said inner transparent film when the monitored luminous transmittance of the article is between about 80% and 85% of the luminous transmittance of the uncoated substrate; terminating the step of depositing said electroconductive film when the monitored luminous transmittance of the article has decreased an additional amount between about 10% and 12% of the luminous transmittance of the uncoated substrate; and terminating the step of sputtering said outer transparent film when the monitored luminous transmittance of said article has increased to about its peak value.
Claim 16
Dependent Claim
31 words
The method as set forth in claim 13 wherein said outer transparent film terminating step is practiced when the monitored luminous transmittance of said article has reached its first peak value.
References Cited (Backward Citations)
US3477936A
Cited
US3698946A
Cited
US4094763A
Cited
US3907660A
Cited
US4102768A
Cited
US3878085A
Cited
US3962488A
Cited
US3956093A
Cited
US4027192A
Cited
US4043889A
Cited
US4111775A
Cited
US4194022A
Cited
US4141621A
Cited
US4113599A
Cited
US4116806A
Cited
US4201649A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-04-04 | 1986-10-04 | 1987-04-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-04-04 | 1990-10-04 | 1991-04-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-04-04 | 1994-10-04 | 1995-04-05 | $7700.00 | Window Closed / Lapsed |