US4194022A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Transparent, colorless, electrically conductive coating
Assignee: PPG Industries Inc
•
Filing: 1978-08-21
•
Granted: 1980-03-18
•
Expires: 1998-08-21
Abstract
Abstract A method for making an optically clear, colorless, transparent, electrically conductive coating by vacuum deposition is disclosed. The method involves depositing a first layer of titanium suboxide, a second layer of silver or gold, and a third layer of titanium suboxide, and treating the coating with an oil, wax, or other organic material before exposure to an ordinary atmosphere of air in order to control the rate of subsequent oxidation of the titanium suboxide. The coating deposited on a rigid transparent substrate such as glass or plastic, or on a flexible transparent plastic substrate subsequently laminated to a rigid transparent substrate, is useful for electrically heating windows.
Inventors
- 👤 Frank H. Gillery
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 12:01
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/06; C23C14/12; C03; C03C; C03C17/00; C03C17/34; C03C17/36; C03C17/3602; C03C17/3613; C03C17/3644; C03C17/3652; C03C17/3655; C23C14/0021; C23C14/08; C23C14/083; C23C14/14; C23C14/18; C23C14/58; C23C14/5806; C23C14/5846; C23C14/5853
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
170 words
A method for making a transparent, colorless, electroconductive coated article comprising the steps of: a. evacuating a vacuum chamber containing a transparent substrate to be coated; b. vacuum depositing in a partial pressure of oxygen a transparent film of titanium oxide, TiO x wherein x has a value greater than 1.0 and less than 2.0; c. vacuum depositing on the titanium oxide film a continuous, transparent, electroconductive film of a metal selected from the group consisting of gold and silver; d. vacuum depositing in a partial pressure of oxygen a second transparent film of titanium oxide, TiO x wherein x has a value of greater than 1.0 and less than 2.0, on the electroconductive film; e. establishing in the vacuum chamber an atmosphere comprising the vapor of a material selected from the group consisting of oils, waxes, heavy organic acids, alcohols and amines capable of decreasing the rate of oxidation of titanium oxide; f. exposing said films to said atmosphere; and g. oxidizing the titanium oxide constituents of the coating.
Claim 2
Independent Claim
170 words
A method for making a transparent, colorless, electroconductive coated article comprising the steps of: a. evacuating a vacuum chamber containing a transparent substrate to be coated; b. vacuum depositing in a partial pressure of oxygen a transparent film of titanium oxide, TiO x wherein x has a value greater than 1.0 and less than 2.0; c. vacuum depositing on the titanium oxide film a continuous, transparent, electroconductive film of a metal selected from the group consisting of gold and silver; d. vacuum depositing in a partial pressure of oxygen a second transparent film of titanium oxide, TiO x wherein x has a value of greater than 1.0 and less than 2.0, on the electroconductive film; e. establishing in the vacuum chamber an atmosphere comprising the vapor of a material selected from the group consisting of oils, waxes, heavy organic acids, alcohols and amines capable of decreasing the rate of oxidation of titanium oxide; f. exposing said films to said atmosphere; and g. oxidizing the titanium oxide constituents of the coating.
Claim 3
Dependent Claim
35 words
The method according to claim 1, wherein the titanium oxide films are deposited by the evaporation of titanium metal and the partial pressure of oxygen is in the range of 1.0 to 3.0×10 -4 Torr.
Claim 4
Dependent Claim
34 words
The method according to claim 1 wherein the material capable of decreasing the rate of oxidation of the titanium oxide is selected from the group consisting of paraffin wax, tetraethylene glycol and tetraethylene pentamine.
Claim 5
Dependent Claim
23 words
The method according to claim 1, wherein the substrate is selected from the group consisting of rigid transparent materials and flexible transparent plastics.
Claim 6
Dependent Claim
11 words
The method according to claim 4 wherein the substrate is glass.
Claim 7
Dependent Claim
12 words
The method according to claim 4, wherein the substrate is a polyester.
Claim 8
Dependent Claim
37 words
The method according to claim 1, wherein the thickness of the titanium oxide layers are from about 200 to 500 Angstroms and the electroconductive film is a silver film having a thickness of 60 to 250 Angstroms.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-03-18 | 1983-09-17 | 1984-03-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-03-18 | 1987-09-17 | 1988-03-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-03-18 | 1991-09-17 | 1992-03-18 | $7700.00 | Window Closed / Lapsed |