US4310354A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for producing a shape memory effect alloy having a desired transition temperature
Assignee: ALLEGHENY INTERNATIONAL ACCEPTANCE Corp
•
Filing: 1980-01-10
•
Granted: 1982-01-12
•
Expires: 2000-01-10
Abstract
Abstract A process for producing a shape memory effect alloy having a desired transition temperature. The process includes the steps of: providing at least one prealloyed powder of a shape memory effect alloy having a chemistry similar to that of the to be produced alloy and a transition temperature below the desired transition temperature of the to be produced alloy; providing at least one other prealloyed powder of a shape memory effect alloy having a chemistry similar to that of the to be produced alloy and a transition temperature in excess of the desired transition temperature of the to be produced alloy; blending said prealloyed powders; consolidating said blended powders; and thermally diffusing said consolidated powders so as to provide a substantially homogeneous alloy of the desired transition temperature.
Inventors
- 👤 Richard W. Fountain
- 👤 William J. Boesch
- 👤 Steven H. Reichman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 09:10
CPC Classifications
C; C22; C22C; C22C1/00; C22C1/04; C22C1/0433; B; B22; B22F; B22F1/00; B22F1/09; C22F; C22F1/00; C22F1/006
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
127 words
A process for producing a shape memory effect alloy having a desired transition temperature, which comprises the steps of: providing at least one prealloyed powder of a shape memory effect alloy having a chemistry similar to that of the to be produced alloy and a transition temperature below the desired transition temperature of the to be produced alloy; providing at least one other prealloyed powder of a shape memory effect alloy having a chemistry similar to that of the to be produced alloy and a transition temperature in excess of the desired transition temperature of the to be produced alloy; blending said prealloyed powders; consolidating said blended powders; and thermally diffusing said consolidated powders so as to provide a substantially homogeneous alloy of the desired transition temperature.
Claim 2
Dependent Claim
127 words
A process for producing a shape memory effect alloy having a desired transition temperature, which comprises the steps of: providing at least one prealloyed powder of a shape memory effect alloy having a chemistry similar to that of the to be produced alloy and a transition temperature below the desired transition temperature of the to be produced alloy; providing at least one other prealloyed powder of a shape memory effect alloy having a chemistry similar to that of the to be produced alloy and a transition temperature in excess of the desired transition temperature of the to be produced alloy; blending said prealloyed powders; consolidating said blended powders; and thermally diffusing said consolidated powders so as to provide a substantially homogeneous alloy of the desired transition temperature.
Claim 3
Dependent Claim
14 words
A process according to claim 1, including the step of producing said prealloyed powders.
Claim 4
Dependent Claim
24 words
A process according to claim 1, wherein said prealloyed powders contain at least 45 wt. % nickel and at least 30 wt. % titanium.
Claim 5
Dependent Claim
22 words
A process according to claim 1, wherein said prealloyed powders are nickel-titanium binary alloys containing from 53 to 62 wt. % nickel.
Claim 6
Dependent Claim
19 words
A shape memory effect alloy having a desired transition temperature, made in accordance with the process of claim 1.
References Cited (Backward Citations)
US3012882A
Cited
US3174851A
Cited
US3529958A
Cited
US3700434A
Cited
US3775101A
Cited
US4035007A
Cited
US3716354A
Cited
US4037324A
Cited
US4144057A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-01-11 | 1985-07-13 | 1986-01-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-01-11 | 1989-07-13 | 1990-01-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-01-11 | 1993-07-13 | 1994-01-12 | $7700.00 | Window Closed / Lapsed |