US4284438A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Manufacture of steel products
Assignee: ASW Ltd
•
Filing: 1979-11-13
•
Granted: 1981-08-18
•
Expires: 1999-11-13
Abstract
Abstract A process for the production of a high strength steel rod or bar which is capable of being substantially cold drawn without any intermediate heat treatment. The steel is hot rolled in a continuous rolling mill and exits from the last stand at a temperature greater than 1000° C. It is then cooled in water to an equalization temperature of between 300° C. and 700° C., and is immediately layed in flat overlapping non-concentric rings on a moving conveyor which allows the rod to be cooled in air as it passes along the conveyor. The rings are collected at the end of the conveyor and formed into coils.
Inventors
- 👤 Donald Barwick
- 👤 Malcolm Brownlee
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 15:48
CPC Classifications
C; C21; C21D; C21D8/00; C21D8/06; C21D8/08; C21D9/00; C21D9/52; C21D9/525
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
122 words
A process for producing hot rolled semi-killed or killed carbon-manganese steel rod having a manganese content of not more than about 0.8% including the steps of hot rolling the steel in a continuous rolling mill, the rod exiting from the last stand of the mill having a temperature in excess of 1000° C., superficially cooling the rod in water from a temperature of above 1000° C. to an equalisation temperature of between 300° C. and 700° C., to produce a martensitic surface layer, laying the rod on a moving conveyor so that the rod forms flat overlapping non-concentric rings, allowing the rod to be cooled in air as it passes along the conveyor and then collecting the non-concentric rings to form coils.
Claim 2
Dependent Claim
122 words
A process for producing hot rolled semi-killed or killed carbon-manganese steel rod having a manganese content of not more than about 0.8% including the steps of hot rolling the steel in a continuous rolling mill, the rod exiting from the last stand of the mill having a temperature in excess of 1000° C., superficially cooling the rod in water from a temperature of above 1000° C. to an equalisation temperature of between 300° C. and 700° C., to produce a martensitic surface layer, laying the rod on a moving conveyor so that the rod forms flat overlapping non-concentric rings, allowing the rod to be cooled in air as it passes along the conveyor and then collecting the non-concentric rings to form coils.
Claim 3
Dependent Claim
27 words
A process according to claim 1 in which the rod is substantially cooled in water to a n equalisation temperature of between 400° C. and 700° C.
Claim 4
Dependent Claim
23 words
A process according to claim 1 or claim 2 in which the rod is cooled on the moving conveyor in substantially still air.
Claim 5
Dependent Claim
24 words
A process according to claim 1 in which the rod consists of a carbon-manganese steel with a carbon content of between 0.05% and 1.00%.
Claim 6
Dependent Claim
19 words
A process according to claim 4 in which the carbon content of the rod is between 0.08% and 1.00%.
Claim 7
Dependent Claim
32 words
A process according to claim 1 in which the non-concentric rings are re-formed into coils at a temperature of at least 100° C. less than the temperature at which they were laid.
Claim 8
Dependent Claim
20 words
A process according to claim 1 in which projections are formed on the rod inthe rolling process prior to cooling.
Claim 9
Dependent Claim
22 words
A process according to claim 1 in which the cooled rod is subsequently cold-drawn without any intermediate heat treatment to form wire.
References Cited (Backward Citations)
US3231432A
Cited
US3666572A
Cited
US3756870A
Cited
US3810793A
Cited
US4016015A
Cited
DE2345738B1
Cited
US4108695A
Cited
US3939015A
Cited
US4016009A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-08-17 | 1985-02-16 | 1985-08-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-08-17 | 1989-02-16 | 1989-08-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-08-17 | 1993-02-16 | 1993-08-18 | $7700.00 | Window Closed / Lapsed |