Ionized-cluster deposited on a substrate and method of depositing ionized cluster on a substrate
Assignee: Futaba Corp
•
Filing: 1975-10-23
•
Granted: 1979-05-01
•
Expires: 1995-10-23
Abstract
Abstract The present ion source called "Vaporized-Metal Cluster Ion Source" is adapted to produce ionized vapor aggregate (ionized cluster) instead of atomic or molecular ions in conventional ion sources. Clusters consisting of 10 2 -10 3 atoms are formed by the adiabatic expansion due to the ejection into a high vacuum region through a nozzle of a heated crucible and ionized by electron bombardment. By "Ionized-Cluster Beam Deposition" using the ion source, fine-quality deposited films of many kinds of materials can be obtained on metal, semiconductor and insulator substrate with strong adhesion and with a fairly high deposition rate.
Inventors
- 👤 Toshinori Takagi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-22 18:39
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/22; C23C14/221; H; H01; H01J; H01J2237/00; H01J2237/06; H01J2237/08; H01J2237/0812; Y; Y10; Y10T; Y10T428/00; Y10T428/249921
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
174 words
A method of depositing a film on a substrate which comprises the steps of positioning in a high vacuum region at least one container for holding the material to be vaporized, an ion extraction electrode containing an electron emission source and a substrate on which the film of said material is to be deposited, applying an acceleration voltage between the container and the extraction electrode, said container having a positive potential and the extraction electrode having a negative potential, vaporizing the material disposed within the container by heating said material so that the vapor pressure within the container is at least ten times greater than that of the high vacuum region, ejecting the vapor from said container into the high vacuum region, thereby forming aggregates or clusters of atoms or molecules by adiabatic expansion, irradiating the aggregates or clusters with an electron beam from the electron emission source contained within the ion extractor electrode to form aggregate or cluster ions and accelerating the cluster ions toward the substrate to form a deposited film thereon.
Claim 2
Independent Claim
174 words
A method of depositing a film on a substrate which comprises the steps of positioning in a high vacuum region at least one container for holding the material to be vaporized, an ion extraction electrode containing an electron emission source and a substrate on which the film of said material is to be deposited, applying an acceleration voltage between the container and the extraction electrode, said container having a positive potential and the extraction electrode having a negative potential, vaporizing the material disposed within the container by heating said material so that the vapor pressure within the container is at least ten times greater than that of the high vacuum region, ejecting the vapor from said container into the high vacuum region, thereby forming aggregates or clusters of atoms or molecules by adiabatic expansion, irradiating the aggregates or clusters with an electron beam from the electron emission source contained within the ion extractor electrode to form aggregate or cluster ions and accelerating the cluster ions toward the substrate to form a deposited film thereon.
Claim 3
Dependent Claim
16 words
The method of claim 1, wherein the material in the container is heated by resistive heating.
Claim 4
Dependent Claim
16 words
The method of claim 1, wherein the material in the container is heated by electron bombardment.
Claim 5
Dependent Claim
16 words
The method of claim 1, wherein the material in the container is heated by high-frequency energy.
Claim 6
Dependent Claim
32 words
The method of claim 1, wherein the material in the container is heated by forming a discharge arc above the surface of the material, thereby increasing the surface temperature of the material.
Claim 7
Dependent Claim
20 words
The method of claim 1, wherein the material to be vaporized is continuously supplied to the interior of the container.
Claim 8
Dependent Claim
48 words
The method of claim 1, wherein the high vacuum region is held at a gas pressure of between 10 -3 and 10 -6 mm Hg (Torr.) while the vapor pressure of the material within the crucible is equal to or greater than about 10 -2 mm Hg (Torr.).
Claim 9
Dependent Claim
23 words
The method of claim 1, wherein the vapor is ejected from the container through at least one nozzle into the high vacuum region.
Claim 10
Dependent Claim
62 words
The method of claim 1, wherein the container is made of a material having electron emission capability so that when the container is heated it emits electrons from the surface of the container, said electrons being accelerated by a magnetic field or an electric field to reach the substrate together with the vapor clusters, thereby fabricating the deposited film on said substrate.
Claim 11
Dependent Claim
16 words
The method of claim 8, wherein the vapor is transported from the container to the nozzle.
Claim 12
Dependent Claim
29 words
The method of claim 10, wherein the vapor is heated while transported from the container to the nozzle in order to keep the vapor particles as fine as possible.
Claim 13
Dependent Claim
20 words
The method of claim 1, wherein the acceleration voltage is in the range of several hundred V to several KV.
Claim 14
Dependent Claim
17 words
The method of claim 1, wherein the substrate is made of metal, an insulator, or a semiconductor.
Claim 15
Dependent Claim
75 words
The method of claim 1, wherein an ion accelerator electrode assembly is disposed in the high vacuum region and a filament is contained within or disposed independently of the electrode assembly, said ion accelerator electrode assembly being supplied with high voltage effective to focus and accelerate electrons derived from the filament, the cluster ions formed by irradiation with the thus focused and accelerated electrons being accelerated in a direction opposite to that of these electrons.
Claim 16
Dependent Claim
10 words
The method of claim 1, wherein the container is sealed.
Claim 17
Dependent Claim
21 words
The method of claim 1, wherein the ejection of the vapor from the container forces the material into a supercooled state.
Claim 18
Dependent Claim
28 words
The method of claim 1, wherein the ionization of only one atom constituting the material vapor aggregates or clusters permits the entirety of the clusters to be ionized.
Claim 19
Dependent Claim
25 words
The method of claim 8, wherein a plurality of nozzles are utilized, and vapor ejected from each nozzle being combined to form a common stream.
Claim 20
Dependent Claim
16 words
A deposited film fabricated in accordance with the ionized cluster beam deposition method of claim 1.
Claim 21
Independent Claim
185 words
A method of depositing a film on a substrate which comprises the steps of positioning in a high vacuum region maintained at a gas pressure of less then 10 -4 Torr at least one container for holding the material to be vaporized, an ion extraction electrode containing an electron emission source and a substrate on which the film of said material is to be deposited, applying an acceleration voltage between the container and the extraction electrode, said container having a positive potential and the extraction electrode having a negative potential, vaporizing the material disposed within the container by heating said material so that the vapor pressure within the container is at least ten times greater than that of the high vacuum region, ejecting the vapor from said container into the high vacuum region, thereby forming aggregates or clusters of atoms or molecules by adiabatic expansion, irradiating the aggregates or clusters with an electron beam from the electron emission source contained within the ion extractor electrode to form aggregate or cluster ions and accelerating the cluster ions toward the substrate to form a deposited film thereon.
Claim 22
Independent Claim
185 words
A method of depositing a film on a substrate which comprises the steps of positioning in a high vacuum region maintained at a gas pressure of less then 10 -4 Torr at least one container for holding the material to be vaporized, an ion extraction electrode containing an electron emission source and a substrate on which the film of said material is to be deposited, applying an acceleration voltage between the container and the extraction electrode, said container having a positive potential and the extraction electrode having a negative potential, vaporizing the material disposed within the container by heating said material so that the vapor pressure within the container is at least ten times greater than that of the high vacuum region, ejecting the vapor from said container into the high vacuum region, thereby forming aggregates or clusters of atoms or molecules by adiabatic expansion, irradiating the aggregates or clusters with an electron beam from the electron emission source contained within the ion extractor electrode to form aggregate or cluster ions and accelerating the cluster ions toward the substrate to form a deposited film thereon.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-04-30 | 1982-10-30 | 1983-05-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-04-30 | 1986-10-30 | 1987-05-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-04-30 | 1990-10-30 | 1991-05-01 | $7700.00 | Window Closed / Lapsed |