Method of utilizing polyacrylic hot-melt adhesives
Assignee: Rohm and Haas Co
•
Filing: 1977-03-11
•
Granted: 1979-05-01
•
Expires: 1997-03-11
Abstract
Abstract Novel polyacrylic hot melt adhesives prepared by blending a polymer having a Tg of -85° to 0° C. with a polymer having a Tg of 20° to 150° C. are disclosed.
Inventors
- 👤 John D. Guerin
- 👤 Thomas W. Hutton
- 👤 John J. Miller
- 👤 Richard E. Zdanowski
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 18:20
CPC Classifications
C; C09; C09J; C09J133/00; C09J133/04; C09J133/06; C09J133/062; C08; C08F; C08F265/00; C08F265/04; C08F265/06; C08L; C08L33/00; C08L33/04; C08L33/06; C08L33/062; C08L33/14; C09J133/14; C08L2205/00; C08L2205/02; C08L2666/00; C08L2666/02; C08L2666/04; C08L33/08; Y; Y10; Y10T; Y10T428/00; Y10T428/28; Y10T428/2813; Y10T428/2817; Y10T428/2826; Y10T428/31504; Y10T428/31855; Y10T428/31935
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
220 words
A method of making a hot-melt adhesive coated article comprising fusing a composition comprising a blend or sequential polymerizate of: (A) from about 5 to about 95 parts by weight of an addition copolymer having a T g in the range of from 0° to -85° C. comprising: (1) from about 85 to about 99.5 parts by weight of a monomer or monomers selected from an alkyl (C 2 - 18 ) or alkoxyalkyl acrylate and (2) from about 0.5 to about 15 parts by weight of an ethylenically unsaturated amine, carboxylic acid or sulfonic acid or mixtures thereof with (B) from about 5 to about 95 parts by weight of an addition copolymer having a T g in the range of from about 20° to about 150° C. comprising: (1) from about 95 to about 99.5 parts by weight of a monomer or monomers of the formula: ##STR4## wherein R is hydrogen or methyl and R 1 is lower alkyl, lower cycloalkyl or isobornyl and (2) from about 0.5 to about 15 parts by weight of an ethylenically unsaturated amine, carboxylic or sulfonic acid or mixtures thereof. said components being compatible, one of the polymers A and B having acid groups and the other having amine groups, applying the molten material to the article, and cooling the coated article.
Claim 2
Independent Claim
220 words
A method of making a hot-melt adhesive coated article comprising fusing a composition comprising a blend or sequential polymerizate of: (A) from about 5 to about 95 parts by weight of an addition copolymer having a T g in the range of from 0° to -85° C. comprising: (1) from about 85 to about 99.5 parts by weight of a monomer or monomers selected from an alkyl (C 2 - 18 ) or alkoxyalkyl acrylate and (2) from about 0.5 to about 15 parts by weight of an ethylenically unsaturated amine, carboxylic acid or sulfonic acid or mixtures thereof with (B) from about 5 to about 95 parts by weight of an addition copolymer having a T g in the range of from about 20° to about 150° C. comprising: (1) from about 95 to about 99.5 parts by weight of a monomer or monomers of the formula: ##STR4## wherein R is hydrogen or methyl and R 1 is lower alkyl, lower cycloalkyl or isobornyl and (2) from about 0.5 to about 15 parts by weight of an ethylenically unsaturated amine, carboxylic or sulfonic acid or mixtures thereof. said components being compatible, one of the polymers A and B having acid groups and the other having amine groups, applying the molten material to the article, and cooling the coated article.
Claim 3
Dependent Claim
32 words
The method of making a pressure sensitive adhesive coated article in accordance with claim 1 in which the composition contains from about 15 to about 30 parts by weight of copolymer (B).
Claim 4
Dependent Claim
27 words
The method of claim 1 for making a non-tacky adhesive coated article in which said composition contains greater than about 30 parts by weight of copolymer (B).
Claim 5
Dependent Claim
23 words
The method of making a laminate comprising the step of laminating the article made by the method of claim 1 to another material.
Claim 6
Dependent Claim
25 words
The method of making a laminate from a coated article in accordance with claim 2 comprising the step of laminating the article to another material.
Claim 7
Dependent Claim
28 words
The method of making a laminate utilizing the adhesive coated article made by the method of claim 3, comprising the step of laminating the article to another material.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-04-30 | 1982-10-30 | 1983-05-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-04-30 | 1986-10-30 | 1987-05-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-04-30 | 1990-10-30 | 1991-05-01 | $7700.00 | Window Closed / Lapsed |