Self-lubricating heat-resistant material and process for manufacturing same
Assignee: Individual
•
Filing: 1975-04-23
•
Granted: 1978-12-12
•
Expires: 1995-04-23
Abstract
Abstract A self-lubricating heat-resistant material which, in accordance with the invention, comprises from 20 to 90 percent by weight of a polymer binder, viz. poly(butadiene) with a degree of cross-linking from 30 to 95 percent, and from 10 to 80 percent by weight of an antifriction filler, viz. molybdenum disulphide, graphite, boron nitride or a mixture thereof; said material is produced, in accordance with the invention, by pressing a composition consisting of from 20 to 90 percent by weight of poly(butadiene) of molecular weight between 20,000 and 800,000 and from 10 to 80 percent by weight of said antifriction filler, the process being effected at a temperature in the range from 200° to 330° C. and a pressure of from 1,000 to 7,000 kg/sq.cm. The self-lubricating heat-resistant material of the invention exhibits thermal stability at temperatures of up to 350° C., a stable coefficient of friction and excellent wear resistance in the temperature range from -150° to +350° C.
Inventors
- 👤 Nikolai S. Nametkin
- 👤 Georgy V. Vinogradov
- 👤 Jury Y. Podolsky
- 👤 Nina T. Pavlovskaya
- 👤 Ernest I. Frenkin
- 👤 Jury G. Yanovsky
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 10:21
CPC Classifications
F; F16; F16C; F16C33/00; F16C33/02; F16C33/04; F16C33/20; F16C33/201; C; C08; C08K; C08K3/00; C08K3/02; C08K3/04; C08K3/30; C08K3/38
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
59 words
A self-lubricating heat-resistant material, consisting of from 20 to 90 percent by weight of poly(butadiene) with a degree of cross-linking in the final product of from 30 to 95 percent, and from 10 to 80 percent by weight of an antifriction filler selected from the group consisting of molybdenum disulphide, graphite, boron nitride and a mixture of said compunds.
Claim 2
Dependent Claim
59 words
A self-lubricating heat-resistant material, consisting of from 20 to 90 percent by weight of poly(butadiene) with a degree of cross-linking in the final product of from 30 to 95 percent, and from 10 to 80 percent by weight of an antifriction filler selected from the group consisting of molybdenum disulphide, graphite, boron nitride and a mixture of said compunds.
Claim 3
Dependent Claim
47 words
A self-lubricating heat-resistant material as set forth in claim 1, which comprises from 30 to 50 percent by weight of poly(butadiene) with a degree of cross-linking in the final product of from 30 to 95 percent and from 50 to 70 percent by weight of molybdenum disulphide.
Claim 4
Dependent Claim
69 words
A self-lubricating heat-resistant material, consisting of from 20 to 70 percent by weight of poly(butadiene) with a degree of cross-linking in the final product of from 30 to 95 percent, from 10 to 60 percent by weight of an antifriction filler selected from the group consisting of molybdenum disulphide, graphite, boron nitride and a mixture of said compounds, and from 20 to 40 percent by weight of powdered copper.
Claim 5
Dependent Claim
69 words
A self-lubricating heat-resistant material, consisting of from 20 to 70 percent by weight of poly(butadiene) with a degree of cross-linking in the final product of from 30 to 95 percent, from 10 to 60 percent by weight of an antifriction filler selected from the group consisting of molybdenum disulphide, graphite, boron nitride and a mixture of said compounds, and from 20 to 40 percent by weight of powdered copper.
Claim 6
Dependent Claim
139 words
A process for manufacturing a self-lubricating heat-resistant material consisting of from 20 to 90 percent by weight of poly (butadiene) with a degree of cross-linking in the final product of from 30 to 95 percent, and from 10 to 80 percent by weight of an antifriction filler selected from the group consisting of molybdenum disulphide, graphite, boron nitride and a mixture of said compounds, which comprises pressing a composition consisting of from 20 to 90 percent by weight of poly(butadiene) of molecular weight from 20,000 to 800,000 and from 10 to 80 percent by weight of an antifriction filler selected from the group consisting of molybdenum disulphide, graphite, boron nitride and a mixture of said compounds, the pressing procedure being effected at a temperature of from 200° to 330° C. and a pressure of from 1,000 to 7,000 kg/sq.cm.
Claim 7
Dependent Claim
139 words
A process for manufacturing a self-lubricating heat-resistant material consisting of from 20 to 90 percent by weight of poly (butadiene) with a degree of cross-linking in the final product of from 30 to 95 percent, and from 10 to 80 percent by weight of an antifriction filler selected from the group consisting of molybdenum disulphide, graphite, boron nitride and a mixture of said compounds, which comprises pressing a composition consisting of from 20 to 90 percent by weight of poly(butadiene) of molecular weight from 20,000 to 800,000 and from 10 to 80 percent by weight of an antifriction filler selected from the group consisting of molybdenum disulphide, graphite, boron nitride and a mixture of said compounds, the pressing procedure being effected at a temperature of from 200° to 330° C. and a pressure of from 1,000 to 7,000 kg/sq.cm.
Claim 8
Dependent Claim
159 words
A process for manufacturing a self-lubricating heat-resistant material consisting of from 20 to 70 percent by weight of poly(butadiene) with a degree of cross-linking in the final product of from 30 to 95 percent, from 10 to 60 percent by weight of an antifriction filler selected from the group consisting of molybdenum disulphide, graphite, boron nitride and a mixture of said compounds, and from 20 to 40 percent by weight of powdered copper, which comprises pressing a composition made up of from 20 to 70 percent by weight of poly(butadiene) of molecular weight from 20,000 to 80,000, from 10 to 60 percent by weight of an antifriction filler selected from the group consisting of molybdenum disulphide, graphite, boron nitride and a mixture of said compounds, and from 20 to 40 percent by weight of powdered copper, the pressing procedure being effected at a temperature of from 200° to 330° C. and a pressure of from 1,000 to 7,000 kg/sq.cm.
Claim 9
Dependent Claim
159 words
A process for manufacturing a self-lubricating heat-resistant material consisting of from 20 to 70 percent by weight of poly(butadiene) with a degree of cross-linking in the final product of from 30 to 95 percent, from 10 to 60 percent by weight of an antifriction filler selected from the group consisting of molybdenum disulphide, graphite, boron nitride and a mixture of said compounds, and from 20 to 40 percent by weight of powdered copper, which comprises pressing a composition made up of from 20 to 70 percent by weight of poly(butadiene) of molecular weight from 20,000 to 80,000, from 10 to 60 percent by weight of an antifriction filler selected from the group consisting of molybdenum disulphide, graphite, boron nitride and a mixture of said compounds, and from 20 to 40 percent by weight of powdered copper, the pressing procedure being effected at a temperature of from 200° to 330° C. and a pressure of from 1,000 to 7,000 kg/sq.cm.
References Cited (Backward Citations)
US1901044A
Cited
US2871216A
Cited
US3438933A
Cited
US3400091A
Cited
US3779918A
Cited
GB1213940A
Cited
US3756982A
Cited
US3867333A
Cited
US3985660A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-12-11 | 1982-06-12 | 1982-12-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-12-11 | 1986-06-12 | 1986-12-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-12-11 | 1990-06-12 | 1990-12-12 | $7700.00 | Window Closed / Lapsed |