Pyrogenic silica or titania or alpha-alumina cuprous chloride catalyst of hydrogen chloride/oxygen reaction
Assignee: Honeywell International Inc
•
Filing: 1977-02-02
•
Granted: 1978-10-31
•
Expires: 1997-02-02
Abstract
Abstract Catalyst of cuprous chloride, as a first layer, on a carrier of particles of pyrogenic anhydrous silica or titania, or alpha-alumina produced from pyrogenic gamma-alumina, having as a second layer an alkali metal chloride especially KCl, and preferably also a rare earth metal chloride; especially LaCl3; formed by impregnation using non-aqueous solvents, especially CuCl in acetonitrile followed by KCl/LaCl3 in formic acid. The catalyst is effective at desirable reaction rates at temperatures well below 400 DEG C., such as 200 DEG -300 DEG C. and even below 200 DEG C., under certain conditions, for oxyhydrochlorination of organic materials such as methane; and is also effective for production of chlorine by the Deacon process at relatively low temperatures. Problems due to catalyst volatility and melting are substantially mitigated.
Inventors
- 👤 Wim J. M. Pieters
- 👤 Emery J. Carlson
- 👤 William E. Gates
- 👤 William C. Conner, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 11:32
CPC Classifications
B; B01; B01J; B01J27/00; B01J27/06; B01J27/08; B01J27/122; B01J23/00; B01J23/70; B01J23/72; B01J37/00; B01J37/02; B01J37/024
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
237 words
An improved copper chloride/alkali metal chloride catalyst on silica, titania or alpha-alumina carrier, effective for production of chlorine or chlorination of organic material by vapor phase reaction between hydrogen chloride and elemental oxygen, which catalyst is essentially anhydrous and consists essentially of granules composed of a relatively low bulk density carrier of open structure and active catalyst; the carrier being between about 30% and about 85% by weight of the total catalyst and being silica, titania or alpha-alumina particles, which particles are non-porous and have diameters in the range of about 50 to 1000 A, and said carrier having surface area of at least about 50 square meters per gram measured by the BET method using nitrogen gas; the catalyst granules having voids within the granules such that at least 20% of the voids have radius greater than 200 A as measured by nitrogen sorption isotherms; and the surface of said granules being occupied by active catalyst composed of a first layer of copper chloride, essentially in the cuprous form, being at least about 10% by weight of the total catalyst and of a second layer of at least one alkali metal chloride, permissibly also containing at least one rare earth metal chloride, said copper chloride being the largest molecular proportion of said active ingredients and the amount of active ingredients being at least sufficient theoretically to cover the carrier particles with a coating one molecule thick.
Claim 2
Dependent Claim
237 words
An improved copper chloride/alkali metal chloride catalyst on silica, titania or alpha-alumina carrier, effective for production of chlorine or chlorination of organic material by vapor phase reaction between hydrogen chloride and elemental oxygen, which catalyst is essentially anhydrous and consists essentially of granules composed of a relatively low bulk density carrier of open structure and active catalyst; the carrier being between about 30% and about 85% by weight of the total catalyst and being silica, titania or alpha-alumina particles, which particles are non-porous and have diameters in the range of about 50 to 1000 A, and said carrier having surface area of at least about 50 square meters per gram measured by the BET method using nitrogen gas; the catalyst granules having voids within the granules such that at least 20% of the voids have radius greater than 200 A as measured by nitrogen sorption isotherms; and the surface of said granules being occupied by active catalyst composed of a first layer of copper chloride, essentially in the cuprous form, being at least about 10% by weight of the total catalyst and of a second layer of at least one alkali metal chloride, permissibly also containing at least one rare earth metal chloride, said copper chloride being the largest molecular proportion of said active ingredients and the amount of active ingredients being at least sufficient theoretically to cover the carrier particles with a coating one molecule thick.
Claim 3
Dependent Claim
74 words
Catalyst of claim 1 consisting essentially of non-porous particles of pyrogenic silica of surface area, by the BET method, of 100 to 400 square meters per gram as carrier; the active ingredients being alkali metal chloride and rare earth metal chloride deposited over a layer of copper chloride, in an amount sufficient theoretically to form a layer of active ingredients covering the carrier particles to an average thickness between one and about ten molecules.
Claim 4
Dependent Claim
23 words
Catalyst of claim 2 wherein a rare earth metal chloride is a minor molecular proportion of the alkali metal/rare earth metal chloride constituent.
Claim 5
Dependent Claim
73 words
Catalyst of claim 3 wherein the alkali metal chloride is potassium chloride, the content of the rare earth metal chloride constituent is at least about 5% by weight of the total catalyst, the potassium chloride constituent is at least equal in weight to the rare earth metal chloride constituent, and the copper chloride constituent forms essentially the balance of the catalyst and is at least about 10% by weight of the total catalyst.
Claim 6
Dependent Claim
13 words
Catalyst of claim 4 wherein the rare earth metal chloride comprises lanthanum chloride.
Claim 7
Dependent Claim
148 words
Process of preparing an improved copper chloride/alkali metal chloride catalyst on silica, titania or alpha-alumina carrier in accordance with claim 1, which comprises impregnating pyrogenic silica or titania, or alpha-alumina particles obtained by heating pyrogenic gamma-alumina, using essentially anhydrous solvents, first with a solution of cuprous chloride in a volatile organic solvent, and drying; then with a solution or colloidal dispersion consisting essentially of potassium chloride and lanthanum chloride in a volatile organic solvent, and drying; and activating the catalyst by heating with hydrogen chloride or hydrogen or with the reactants for oxyhydrochlorination of an organic compound, whereby the catalyst is active at temperatures of 300° C. for oxyhydrochlorination of methane; the proportions of carrier and active ingredients being chosen to give, by weight in the total catalyst, 30% to 85% carrier, and to make the cuprous chloride at least about 10% by weight of the total catalyst.
Claim 8
Dependent Claim
73 words
Process of claim 6 wherein pyrogenic silica is used as the catalyst carrier; the solvent used for cuprous chloride is acetonitrile and the solvent used for potassium chloride/lanthanum chloride is formic acid; and the proportions of carrier and active ingredients are chosen to give, by weight in the total catalyst, 30% to 85% silica, at least about 5% lanthanum chloride and potassium chloride at least about equal in weight to the lanthanum chloride.
References Cited (Backward Citations)
US2734874A
Cited
US3210158A
Cited
US3210431A
Cited
US3260678A
Cited
US3240827A
Cited
US3235508A
Cited
US3468968A
Cited
US3527819A
Cited
US3634330A
Cited
US3717670A
Cited
US3657367A
Cited
US3709950A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-10-30 | 1982-05-01 | 1982-10-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-10-30 | 1986-05-01 | 1986-10-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-10-30 | 1990-05-01 | 1990-10-31 | $7700.00 | Window Closed / Lapsed |