US4039714A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Pretreatment of plastic materials for metal plating
Assignee: DR -ING MAX SCHLOETTER
•
Filing: 1974-06-11
•
Granted: 1977-08-02
•
Expires: 1994-06-11
Abstract
Abstract Plastics and articles made therefrom are metal plated by conditioning their surface by a treatment with sulfur trioxide vapor or a sulfur trioxide containing atmosphere. The thus conditioned plastics or plastic articles are then metal plated, if required, after sensibilization, nucleation or activation, and treatment with a reducing solution. Metal plating is effected by chemical deposition of the metal or by electroplating. The resulting metal layer is reenforced, if required, also by chemical plating or electroplating. The resulting metal coating has a surprisingly high adhesive strength.
Inventors
- 👤 Jiri Roubal
- 👤 Joachim Korpiun
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 08:25
CPC Classifications
C; C23; C23C; C23C18/00; C23C18/16; C23C18/18; C23C18/20; C23C18/22; C23C18/24; C23C18/2006; Y; Y10; Y10T; Y10T428/00; Y10T428/26; Y10T428/263; Y10T428/264; Y10T428/265
Claims Analysis
Total Claims: 38
Claim 1
Independent Claim
117 words
In a process for metal plating a natural or synthetic resinous material, including the steps of: a. conditioning the surface of the natural or synthetic resinous material; b. activating the conditioned surface by providing a noble metal thereon; and c. depositing a metal coating upon the activated surface from an electroless plating bath, wherein the improvement comprises said conditioning step consisting essentially of exposing the natural or synthetic resinous material to the action of a gaseous sulfur trioxide-containing atmosphere containing between about 1 mg/l and 100%, by volume, of sulfur trioxide for a period of time between about 0.5 seconds and 20 minutes sufficient to condition the surface of the material without substantially physically affecting the material.
Claim 2
Dependent Claim
117 words
In a process for metal plating a natural or synthetic resinous material, including the steps of: a. conditioning the surface of the natural or synthetic resinous material; b. activating the conditioned surface by providing a noble metal thereon; and c. depositing a metal coating upon the activated surface from an electroless plating bath, wherein the improvement comprises said conditioning step consisting essentially of exposing the natural or synthetic resinous material to the action of a gaseous sulfur trioxide-containing atmosphere containing between about 1 mg/l and 100%, by volume, of sulfur trioxide for a period of time between about 0.5 seconds and 20 minutes sufficient to condition the surface of the material without substantially physically affecting the material.
Claim 3
Dependent Claim
50 words
The process as defined by claim 1, wherein said step of activating the surface of the natural or synthetic resinous material comprises immersing said material into a solution containing a nobel metal ion, and subsequently immersing said material into a solution containing a reducing agent for the noble metal ion.
Claim 4
Dependent Claim
49 words
The process as defined by claim 1, wherein said step of activating the surface of the natural or synthetic resinous material comprises sensitizing the surface by immersing the article into an acidified solution of stannous chloride, and subsequently immersing said material into a solution containing a noble metal ion.
Claim 5
Dependent Claim
31 words
The process as defined by claim 1, further comprising the step of reinforcing the metal layer deposited from said electroless plating bath by depositing additional metal plating on said material electrolytically.
Claim 6
Dependent Claim
22 words
The process as defined by claim 1, wherein said noble metal is selected from the group consisting of palladium, silver and gold.
Claim 7
Dependent Claim
22 words
The process as defined by claim 2, wherein said reducing agent is selected from the group consisting of N-diethylamino borazane and formaldehyde.
Claim 8
Dependent Claim
22 words
The process as defined by claim 1, wherein said electroless plating bath is a copper plating bath or a nickel plating bath.
Claim 9
Dependent Claim
21 words
The process as defined by claim 1, wherein the sulfur trioxide containing atmospheres contains at least 10 mg./l of sulfur trioxide.
Claim 10
Dependent Claim
27 words
The process as defined by claim 1, wherein the sulfur trioxide containing atmosphere comprises the vapor phase over oleum of a concentration up to 65% sulfur trioxide.
Claim 11
Dependent Claim
30 words
The process as defined by claim 1, wherein said conditioning step is carried out at a gaseous atmosphere temperature at which the natural or synthetic resinous material is thermally stable.
Claim 12
Dependent Claim
18 words
The process as defined by claim 10, wherein said temperature is between about -30° C. and 130° C.
Claim 13
Dependent Claim
14 words
The process as defined by claim 2, wherein said temperature is approximately room temperature.
Claim 14
Dependent Claim
60 words
The process as defined by claim 4, wherein said natural or synthetic resinous material is exposed to the gaseous sulfur trioxide-containing atmosphere for a period of time sufficient to provide a bonding strength to said surface of at least about 2 kp./2.5 cm. for a 30 μm layer of deposited metal when tested according to DIN 40802 Sheet 1 method.
Claim 15
Dependent Claim
26 words
The process as defined by claim 1, wherein said gaseous sulfur trioxide-containing atmosphere comprises sulfur trioxide and a gas inert to and unreactive with sulfur trioxide.
Claim 16
Dependent Claim
26 words
The process as defined by claim 14, wherein said inert gas is selected from the group consisting of air, nitrogen, carbon dioxide and a noble gas.
Claim 17
Dependent Claim
76 words
The process as defined by claim 1, wherein said natural or synthetic resinous material is selected from the group consisting of polyethylene, polypropylene, polyvinylchloride, polystyrene, the copolymerization product of styrene and acrylonitrile, the copolymerization product of acrylonitrile, styrene and butadiene, a phenol-formaldehyde condensation product, an epoxy resin, an elastomer, a polysulfone, a polycarbonate, a polyamide, a polyacetal, a polyphenylene oxide, a urea-formaldehyde-condensation product, a melamine-formaldehyde condensation product, a polyester resin, acrylic acid ester polymers, and polyvinylacetate.
Claim 18
Dependent Claim
22 words
The process as defined by claim 1, wherein said natural or synthetic resinous material comprises paper impregnated with a phenol-formaldehyde condensation product.
Claim 19
Dependent Claim
25 words
The process as defined by claim 1, wherein said natural or synthetic resinous material comprises a plate for printed circuits provided with an adhesive lacquer.
Claim 20
Dependent Claim
21 words
The process as defined by claim 1, wherein said natural or synthetic resinous material comprises said material containing a filler material.
Claim 21
Dependent Claim
22 words
The process as defined by claim 19, wherein said filler is selected from the group consisting of glass fibers and cellulose fibers.
Claim 22
Dependent Claim
18 words
The process as defined by claim 1, wherein said natural or synthetic or synthetic resinous material comprises rubber.
Claim 23
Dependent Claim
37 words
The process as defined by claim 1, wherein said step of metal coating said article in an electroless coating bath is carried out to provide a metal layer having a thickness between about 0.2 and 1 micron.
Claim 24
Dependent Claim
33 words
The process as defined by claim 4, wherein said step of electrolytically depositing a metal coating upon said material is carried out to provide a metal coating of up to about 30 microns.
Claim 25
Dependent Claim
26 words
The process as defined by claim 4, further comprising the step of heat treating the metal coated material by exposing said material to an elevated temperature.
Claim 26
Dependent Claim
72 words
A metal plated article of natural or synthetic resinous material, comprising a substrate of said natural or synthetic resinous material, said substrate having a surface which is macroscopically smooth, a layer of metal deposited upon said surface, said layer of metal being bonded to said surface by a strength of at least about 2 kp/2.5 cm., said metal plated article having been produced in accordance with the process defined by claim 1.
Claim 27
Dependent Claim
68 words
A metal plated article of a natural or synthetic resinous material, comprising a substrate of said natural or synthetic resinous material, said substrate having a surface which is macroscopically smooth, and a metal layer deposited upon said surface, said metal layer being bonded to said surface by strength of at least about 5 kp/2.5 cm., said article having been produced according to the process defined by claim 24.
Claim 28
Dependent Claim
28 words
The metal plated article as defined by claim 25, wherein said material is an acrylonitrile-butadiene-styrene copolymer and said bonding strength is between about 2.8 and 3.2 kp/2.5 cm.
Claim 29
Dependent Claim
25 words
The metal plated article as defined by claim 25, wherein said material is polyvinylchloride and said bonding strength is greater than about 5 kp/2.5 cm.
Claim 30
Dependent Claim
26 words
The metal plated article as defined by claim 26, wherein said material is a styrene-acrylonitrile copolymer, and said adhesive bonding strength is about 3.5 kp/2.5 cm.
Claim 31
Dependent Claim
14 words
The metal plated article as defined by claim 25, wherein said material is polypropylene.
Claim 32
Dependent Claim
14 words
The metal plated article as defined by claim 25, wherein said material is polyethylene.
Claim 33
Dependent Claim
75 words
The process as defined by claim 1, wherein said natural or synthetic resinous material is selected from the group consisting of polypropylene, polyvinylchloride, polystyrene, the copolymerization product of styrene and acrylonitrile, the copolymerization product of acrylonitrile, styrene and butadiene, a phenol-formaldehyde condensation product, an epoxy resin, an elastomer, a polysulfone, a polycarbonate, a polyamide, a polyacetal, a polyphenylene oxide, a urea-formaldehyde-condensation product, a melamine-formladehyde condensation product, a polyester resin, acrylic acid ester polymers, and polyvinylacetate.
Claim 34
Dependent Claim
18 words
The process as defined by claim 1, wherein said natural or synthetic resinous material is an ABS polymer.
Claim 35
Dependent Claim
17 words
The process as defined by claim 1, wherein said natural or synthetic resinous material is polyvinyl chloride.
Claim 36
Dependent Claim
16 words
The process as defined by claim 1, wherein said natural or synthetic resinous material is polypropylene.
Claim 37
Dependent Claim
16 words
The process as defined by claim 1, wherein said natural or synthetic resinous material is polystyrene.
Claim 38
Dependent Claim
16 words
The process as defined by claim 1, wherein said natural or synthetic resinous material is polyethylene.
References Cited (Backward Citations)
US2937066A
Cited
US3033703A
Cited
US3442683A
Cited
US3475194A
Cited
US3466229A
Cited
US3607350A
Cited
US3578484A
Cited
US3684554A
Cited
US3682786A
Cited
US3740252A
Cited
US3940520A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-08-01 | 1981-01-31 | 1981-08-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-08-01 | 1985-01-31 | 1985-08-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-08-01 | 1989-01-31 | 1989-08-02 | $7700.00 | Window Closed / Lapsed |