US4035007A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Heat recoverable metallic coupling
Assignee: Advanced Metal Components Inc
•
Filing: 1973-10-29
•
Granted: 1977-07-12
•
Expires: 1993-10-29
Abstract
Abstract A coupling for tubes, pipes or the like, fabricated of heat recoverable metal that is treated so that it will contract when heated above its transition temperature spontaneously expand when cooled to its transition temperature to permit it to be installed or removed from the pipes.
Inventors
- 👤 John D. Harrison
- 👤 James E. Jervis
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 05:21
CPC Classifications
F; F16; F16L; F16L13/00; F16L13/004; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49826; Y10T29/49863; Y10T29/49865
Claims Analysis
Total Claims: 29
Claim 1
Independent Claim
104 words
An article comprising restraining means and a hollow, generally tubular heat recoverable member formed of a metallic material which exists in the austenitic phase at a first temperature and the martensitic phase at a second temperature, which member is capable, without the application of external force, of changing dimension in a first, radially inward direction when heated so as to pass from the martensitic to the austenitic state, and in an opposite, radially outward direction when then cooled to martensitic transition temperature, the restraint imposed by said means being such as to direct said change of dimension radially outward when temperature is so reduced.
Claim 2
Dependent Claim
104 words
An article comprising restraining means and a hollow, generally tubular heat recoverable member formed of a metallic material which exists in the austenitic phase at a first temperature and the martensitic phase at a second temperature, which member is capable, without the application of external force, of changing dimension in a first, radially inward direction when heated so as to pass from the martensitic to the austenitic state, and in an opposite, radially outward direction when then cooled to martensitic transition temperature, the restraint imposed by said means being such as to direct said change of dimension radially outward when temperature is so reduced.
Claim 3
Dependent Claim
31 words
The coupling of claim 1 wherein said metallic material is an alloy consisting essentially of about 50 atomic percent titanium, about 47 atomic percent nickel and about 3 atomic percent iron.
Claim 4
Dependent Claim
42 words
The coupling of claim 1 wherein said metallic material is an alloy consisting essentially of about 50 atomic percent nickel, about 0.75 atomic percent to about 1.0 atomic percent aluminum and correspondingly about 49.25 atomic percent to about 49 atomic percent titanium.
Claim 5
Dependent Claim
26 words
The coupling of claim 1 wherein said metallic material is an alloy consisting essentially of about 51.5 atomic percent nickel and about 48.5 atomic percent titanium.
Claim 6
Dependent Claim
31 words
The coupling of claim 1 wherein said metallic material is an alloy consisting essentially of about 2 atomic percent manganese, about 48 atomic percent nickel and about 50 atomic percent titanium.
Claim 7
Dependent Claim
26 words
The coupling of claim 1 wherein the inner surface of said tubular member is provided with an enlarged inside diameter near the center of said member.
Claim 8
Dependent Claim
26 words
The coupling of claim 1 wherein the inner surface of said tubular member is provided with an enlarged inside diameter near each end of said member.
Claim 9
Dependent Claim
26 words
The coupling of claim 1 wherein the outer surface of said tubular member is provided with a reduced outside diameter at each end of said member.
Claim 10
Dependent Claim
30 words
The coupling of claim 1 wherein the wall thickness at an end of said coupling is about one-fourth to one-fifth of the wall thickness at the center of said coupling.
Claim 11
Dependent Claim
31 words
An article according to claim 1 in which radially outward expansion is occasioned by internal stresses imparted to said member at a temperature at or above the temperature of heat recovery.
Claim 12
Dependent Claim
29 words
An article according to claim 1 in which radially outward expansion is occasioned by internal stresses imparted to said member at a temperature below the temperature of heat recovery.
Claim 13
Dependent Claim
43 words
An article according to claim 1 in which said restraint is imposed by a generally cylindrical object about which said member has been recovered, which object is greater in diameter than the internal diameter of said member when in its heat stable configuration.
Claim 14
Dependent Claim
22 words
An article according to claim 1, said member having been in its annealed form at the time heat recoverability was imparted thereto.
Claim 15
Dependent Claim
40 words
An article according to claim 12 in which said object is a pipe joint comprising first and second pipes in end-to-end relationship, said member tightly engaging the adjacent ends of said pipes so as to couple them, one to another.
Claim 16
Dependent Claim
58 words
A generally tubular article comprising a heat recoverable metallic material above its transition temperature, the article being maintained in a radially expanded, heat-unstable state by a constrained member within its bore, the article being capable, without the application of external force, of expanding radially when cooled to the transition temperature so as to free said member from constraint.
Claim 17
Dependent Claim
58 words
A generally tubular article comprising a heat recoverable metallic material above its transition temperature, the article being maintained in a radially expanded, heat-unstable state by a constrained member within its bore, the article being capable, without the application of external force, of expanding radially when cooled to the transition temperature so as to free said member from constraint.
Claim 18
Dependent Claim
13 words
The article of claim 15 wherein said member is at least partially elastic.
Claim 19
Dependent Claim
21 words
The article of claim 15 wherein said metallic material has a transition temperature between about -196° C and about -75° C.
Claim 20
Dependent Claim
30 words
The article of claim 15 wherein the material is an alloy consisting essentially of about 50 atomic percent titanium, about 47 atomic percent nickel and about 3 atomic percent iron.
Claim 21
Dependent Claim
41 words
The article of claim 15 wherein the material is an alloy consisting essentially of about 50 atomic percent nickel, about 0.75 atomic percent to about 1.0 atomic percent aluminum and correspondingly about 49.25 atomic percent to bout 49 atomic percent titanium.
Claim 22
Dependent Claim
25 words
The article of claim 15 wherein the material is an alloy consisting essentially of about 51.5 atomic percent nickel and about 48.5 atomic percent titanium.
Claim 23
Dependent Claim
30 words
The article of claim 15 wherein the material is an alloy consisting essentially of about 2 atomic percent manganese, about 48 atomic percent nickel and about 50 atomic percent titanium.
Claim 24
Independent Claim
86 words
A method of forming a heat recoverable metal article comprising forming said article in a desired configuration from a material capable of having the property of heat recoverability imparted thereto, cooling said article to below the transition temperature of said material, expanding said article while below said transition temperature to an enlarged configuration, said expansion being sufficient to introduce stresses into said material due to non-thermally recoverable plastic deformation, and maintaining said article in an enlarged condition while heating said article to above the transition temperature.
Claim 25
Independent Claim
86 words
A method of forming a heat recoverable metal article comprising forming said article in a desired configuration from a material capable of having the property of heat recoverability imparted thereto, cooling said article to below the transition temperature of said material, expanding said article while below said transition temperature to an enlarged configuration, said expansion being sufficient to introduce stresses into said material due to non-thermally recoverable plastic deformation, and maintaining said article in an enlarged condition while heating said article to above the transition temperature.
Claim 26
Dependent Claim
27 words
The method of claim 22 wherein said article is tubular and is maintained in said enlarged condition by inserting a member in the bore of said article.
Claim 27
Dependent Claim
10 words
The method of claim 23 wherein said member is elastic.
Claim 28
Independent Claim
142 words
A method of forming a butt joint between two pipes, which comprises expanding a tubular metallic member formed of a material capable of having the property of heat recoverability imparted thereto, expansion occuring at or below the transition temperature of said material to an extent which causes both thermally recoverable and non-thermally recoverable plastic deformation, inserting a mandrel within the member, raising the temperature of the member above the said transition temperature whereby the member shrinks about the mandrel, cooling the member to or below the transition temperature of said material whereby the member spontaneously expands, removing the member from the mandrel, positioning said member about the pipes at their junction, raising the temperature of the member above the transition temperature of said material to cause said member to heat recover on said pipes and maintaining said member above said transition temperature.
Claim 29
Independent Claim
142 words
A method of forming a butt joint between two pipes, which comprises expanding a tubular metallic member formed of a material capable of having the property of heat recoverability imparted thereto, expansion occuring at or below the transition temperature of said material to an extent which causes both thermally recoverable and non-thermally recoverable plastic deformation, inserting a mandrel within the member, raising the temperature of the member above the said transition temperature whereby the member shrinks about the mandrel, cooling the member to or below the transition temperature of said material whereby the member spontaneously expands, removing the member from the mandrel, positioning said member about the pipes at their junction, raising the temperature of the member above the transition temperature of said material to cause said member to heat recover on said pipes and maintaining said member above said transition temperature.
References Cited (Backward Citations)
US2992021A
Cited
US3012882A
Cited
US3139468A
Cited
US3174851A
Cited
US3315986A
Cited
US3351463A
Cited
US3513429A
Cited
US3579805A
Cited
US3498648A
Cited
US3622941A
Cited
US3558369A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-07-11 | 1981-01-10 | 1981-07-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-07-11 | 1985-01-10 | 1985-07-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-07-11 | 1989-01-10 | 1989-07-12 | $7700.00 | Window Closed / Lapsed |