Optical information storage material and method of making it
Assignee: Panasonic Holdings Corp
•
Filing: 1974-08-26
•
Granted: 1976-07-27
•
Expires: 1994-08-26
Abstract
Abstract An optical information storage material having a transparent base and a film deposited on the base, the state of which can be changed between a low optical density state and a high optical density state by the application of electrical, optical or thermal energy. The film is a tellurium oxide having the composition TeO x1 in which 0<x1<2.0, or a mixture of such a tellurium oxide and vanadium oxide for making it easier to change the state of the film material, or tellurium oxide and lead oxide for increasing the sensitivity of the film. The material is made by vacuum evaporating and depositing the tellurium oxide or the mixture of tellurium oxide with the vanadium or lead oxide from TeO 2 or a solid solution of TeO 2 and lead or vanadium oxide.
Inventors
- 👤 Takeo Ohta
- 👤 Mutsuo Takenaga
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 16:45
CPC Classifications
G; G11; G11B; G11B7/00; G11B7/24; G11B7/26; G03; G03C; G03C1/00; G03C1/705; G11B7/241; G11B7/242; G11B7/243; G11B2007/24302; G11B2007/24304; G11B2007/24312; G11B2007/24316; G11B2007/24318; G11B2007/2432; G11B7/004; G11B7/0045; G11B7/00454; G11B7/252; G11B7/253; G11B7/2533; G11B7/2535; Y; Y10; Y10S; Y10S428/00; Y10S428/913; Y10T; Y10T428/00; Y10T428/31504; Y10T428/3154; Y10T428/31544; Y10T428/31786
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
59 words
In an optical information storage material having a base and a film deposited on said base the state of which can be changed between the low optical density state and the high optical density state by the application of electrical, optical or thermal energy, the improvement wherein said film comprises TeO x1 in which 0 < x1 < 2.0.
Claim 2
Dependent Claim
59 words
In an optical information storage material having a base and a film deposited on said base the state of which can be changed between the low optical density state and the high optical density state by the application of electrical, optical or thermal energy, the improvement wherein said film comprises TeO x1 in which 0 < x1 < 2.0.
Claim 3
Dependent Claim
61 words
The improvement as claimed in claim 1, wherein said film further comprises vanadium oxide as an additive for making it easy to transform the physical state of the film, said vanadium oxide being VO x2 and the film having a composition of (TeO x1 ).sub. 1 -y (VO x2 ) Y in which 0 <x2 <2.5 and 0 < Y <0.6.
Claim 4
Dependent Claim
57 words
The improvement as claimed in claim 1, wherein said film further comprises lead oxide as an additive for increasing the sensitivity of the film, said lead oxide being PbO x3 and said film having a composition of (TeO x1 ) 1 -z (x3) z in which 0 < X3 < 1.0 and 0 < z < 0.5.
Claim 5
Dependent Claim
16 words
The improvement as claimed in claim 1, further comprising a transparent protective layer on said film.
Claim 6
Dependent Claim
19 words
An optical information storage device as recited in claim 1, wherein said film further comprises a transition metal oxide.
Claim 7
Dependent Claim
48 words
The improvement as claimed in claim 5, wherein said transition metal oxide is a material selected from the group consisting of CrO x4 , MnO x5 , and CoO x7 , wherein 0 < x4 < 1.5, 0 < x5 < 2, and 0 < x7 < 1.5.
Claim 8
Dependent Claim
56 words
An optical information storage material comprising a transparent base and a film deposited on said base the state of which can be changed between the low optical density state and the high optical density state by the application of electrical, optical or thermal energy, said film comprising TeO x1 in which 0 < x1 < 2.0.
Claim 9
Dependent Claim
56 words
An optical information storage material comprising a transparent base and a film deposited on said base the state of which can be changed between the low optical density state and the high optical density state by the application of electrical, optical or thermal energy, said film comprising TeO x1 in which 0 < x1 < 2.0.
Claim 10
Independent Claim
46 words
A method of making an optical information storage material having a base and a film deposited on said base which is comprised of TeO x1 in which 0 < x1 < 2.0, comprising evaporating TeO 2 under deoxidizing conditions and depositing the vapor on the base.
Claim 11
Independent Claim
46 words
A method of making an optical information storage material having a base and a film deposited on said base which is comprised of TeO x1 in which 0 < x1 < 2.0, comprising evaporating TeO 2 under deoxidizing conditions and depositing the vapor on the base.
Claim 12
Dependent Claim
33 words
The method as claimed in claim 8 in which the step of evaporating under deoxidizing conditions comprises vacuum evaporating at a vacuum on the order of 5 × 10 - 5 mm Hg.
Claim 13
Independent Claim
102 words
A method of making an optical information storage material having a base and a film deposited on said base which is comprised of TeO x1 , in which 0 <X1 <2.0, and an oxide taken from the group consisting of VO x2 and PbO x3 , in which 0 < X2 < 2.5 and 0 < X3 < 1.0, comprising the steps of: preparing a solid solution of a tellurium oxide and an oxide taken from the group consisting of a vanadium oxide and a lead oxide; and evaporating the solid solution under deoxiding conditions and depositing the vapor of the base.
Claim 14
Independent Claim
102 words
A method of making an optical information storage material having a base and a film deposited on said base which is comprised of TeO x1 , in which 0 <X1 <2.0, and an oxide taken from the group consisting of VO x2 and PbO x3 , in which 0 < X2 < 2.5 and 0 < X3 < 1.0, comprising the steps of: preparing a solid solution of a tellurium oxide and an oxide taken from the group consisting of a vanadium oxide and a lead oxide; and evaporating the solid solution under deoxiding conditions and depositing the vapor of the base.
Claim 15
Dependent Claim
58 words
A method as claimed in claim 10 in which the step of preparing the solid solution comprises mixing powdered TeO 2 and the other oxide in powdered form, heating the mixture of powders to the melting temperature thereof and holding the melted mixture at the melting temperature for from 3 to 4 hours, and quenching the melted mixture.
References Cited (Backward Citations)
US3455724A
Cited
US3406085A
Cited
US3445271A
Cited
US3516720A
Cited
US3565671A
Cited
US3831165A
Cited
US3665483A
Cited
US3704467A
Cited
JPS475951U
Cited
US3761942A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-07-27 | 1980-01-26 | 1980-07-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-07-27 | 1984-01-26 | 1984-07-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-07-27 | 1988-01-26 | 1988-07-27 | $7700.00 | Window Closed / Lapsed |