Ultra high temperature chemical reactions with metals
Assignee: Individual
•
Filing: 1974-05-01
•
Granted: 1976-03-16
•
Expires: 1994-05-01
Abstract
Abstract A method for treating metals and metal surfaces is disclosed. The method includes the use of a plasma gas generated by an induction plasma system. In one embodiment, a cutting tool, such as a saw blade or razor blade is passed into contact with the plasma to produce an extremely hard blade surface. The method includes stabilization of the plasma prior to use, and the electrical insulating of metallic parts of the treating equipment in order to prevent arcing. Very high feed speeds may be employed, up to 150 feet per minute.
Inventors
- 👤 Francis Lee Jones
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 08:25
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/44; C23C16/50; C23C16/513; C21; C21D; C21D1/00; C21D1/06; C21D1/09; C23C8/00; C23C8/06; C23C8/36
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
141 words
A method for treating metal structures to harden the surface thereof which comprises: a. generating a plasma gas selected from the group consisting of propane, a mixture of nitrogen and propane and a mixture of nitrogen and boron trifluoride by an induction plasma system; b. stabilizing the plasma gas generated by the induction plasma system; c. providing an electrically insulated feed system for passing the metal structure through the plasma gas; d. passing the metal structure consisting essentially of a metal selected from the group consisting of steel compositions, cast iron, aluminum, titanium and alloys of said metals through the plasma gas at a speed of from 60 to 150 feet per minute; and e. quenching the surface of the metal structure with a fluid immediately after the metal structure has passed through the plasma gas to harden the surface thereof.
Claim 2
Independent Claim
141 words
A method for treating metal structures to harden the surface thereof which comprises: a. generating a plasma gas selected from the group consisting of propane, a mixture of nitrogen and propane and a mixture of nitrogen and boron trifluoride by an induction plasma system; b. stabilizing the plasma gas generated by the induction plasma system; c. providing an electrically insulated feed system for passing the metal structure through the plasma gas; d. passing the metal structure consisting essentially of a metal selected from the group consisting of steel compositions, cast iron, aluminum, titanium and alloys of said metals through the plasma gas at a speed of from 60 to 150 feet per minute; and e. quenching the surface of the metal structure with a fluid immediately after the metal structure has passed through the plasma gas to harden the surface thereof.
Claim 3
Dependent Claim
33 words
The method of claim 1 wherein the surface of the metal is hardened by said treatment to a value of up to Rc 80 and to a depth of up to 0.010 inches.
Claim 4
Dependent Claim
16 words
The method of claim 1 wherein the plasma gas comprises a mixture of propane and nitrogen.
Claim 5
Dependent Claim
32 words
The method of claim 2 wherein the metal structure is a saw blade and wherein the saw blade is passed through the plasma at a speed of from 60 to 100 ft./min.
Claim 6
Dependent Claim
32 words
The method of claim 2 wherein the metal structure is a razor blade and wherein the razor blade is passed through the plasma at a speed of from 100 to 150 ft./min.
Claim 7
Dependent Claim
46 words
The method of claim 1 wherein the step of passing the metal structure through the plasma gas includes mounting the induction plasma system, a quench system and drive means for the feed system on a platform which is mounted for movement relative to the metal structure.
Claim 8
Dependent Claim
48 words
The method of claim 1 wherein the plasma gas contains 10 volume % boron trifluoride and 80 volume % nitrogen, and wherein said plasma reacts with a tool steel structure to provide a layer of boron nitride, 0.001 inches in thickness, at the surface of said steel structure.
Claim 9
Dependent Claim
11 words
A hardened metal structure obtained by the method of claim 2.
Claim 10
Dependent Claim
31 words
The method of claim 3 wherein a titanium coating is sputtered onto the surface of the metal stucture for reaction with said mixture of propane and nitrogen to produce titanium carbide.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-03-16 | 1979-09-15 | 1980-03-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-03-16 | 1983-09-15 | 1984-03-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-03-16 | 1987-09-15 | 1988-03-16 | $7700.00 | Window Closed / Lapsed |