Method of making glass optical waveguide
Assignee: Corning Glass Works
•
Filing: 1974-06-21
•
Granted: 1976-01-13
•
Expires: 1994-06-21
Abstract
Abstract A method of forming an optical waveguide by forming a first layer of glass having a predetermined refractive index on the outside peripheral wall surface of a substantially cylindrical mandrel. Thereafter, a second layer of glass is applied to the surface of the first layer, the second layer having a refractive index less than that of the first layer. The mandrel is removed from the assembly and the resultant cylindrical, hollow assembly is heated and drawn to reduce the cross-sectional area thereof, thereby forming an intermediate fiber. At least a portion of the intermediate fiber is disposed within a hollow glass cylinder having a refractive index similar to that of the second layer of glass of the intermediate fiber. The resultant composite structure is heated and drawn to reduce the cross-sectional area thereof and to collapse the inner, first layer of glass and to cause the inner surface of the glass tube to collapse upon the outer surface of the intermediate fiber to form a fiber having a solid cross-sectional area.
Inventors
- 👤 Michael G. Blankenship
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 16:54
CPC Classifications
C; C03; C03B; C03B37/00; C03B37/01; C03B37/02; C03B37/025; C03B37/027; C03B37/02754; C03B37/012; C03B37/01205; C03B37/01211; C03B37/014; C03B37/01466; C03B37/01473; C03B37/01486; C03B37/01493; G; G02; G02B; G02B6/00; G02B6/02; G02B6/036; G02B6/03616; G02B6/03622; G02B6/03633; C03B2203/00; C03B2203/10; C03B2203/22; C03B2203/24; C03B2203/28; C03B2205/00; C03B2205/12; C03B2205/14; C03B2205/16
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
171 words
A method of forming a clad optical waveguide fiber comprising the steps of providing a substantially cylindrical mandrel, applying a first layer of glass to the outside peripheral surface of said mandrel, applying a second layer of glass having an index of refraction less than that of the glass of said first layer over the outside peripheral surface of said first layer, removing said mandrel, heating the structure so formed to the drawing temperature of the materials thereof, drawing the heated structure to reduce the cross-sectional area thereof, thereby forming an intermediate fiber, providing a glass tube having a hole extending axially therethrough, disposing at least a portion of said intermediate fiber within said tube, heating the final composite structure so formed to the drawing temperature thereof, and drawing said final composite structure to reduce the cross-sectional area thereof and to form an optical waveguide fiber having a solid cross-section, said first layer forming the core and said second layer and said tube forming the cladding of said optical waveguide fiber.
Claim 2
Independent Claim
171 words
A method of forming a clad optical waveguide fiber comprising the steps of providing a substantially cylindrical mandrel, applying a first layer of glass to the outside peripheral surface of said mandrel, applying a second layer of glass having an index of refraction less than that of the glass of said first layer over the outside peripheral surface of said first layer, removing said mandrel, heating the structure so formed to the drawing temperature of the materials thereof, drawing the heated structure to reduce the cross-sectional area thereof, thereby forming an intermediate fiber, providing a glass tube having a hole extending axially therethrough, disposing at least a portion of said intermediate fiber within said tube, heating the final composite structure so formed to the drawing temperature thereof, and drawing said final composite structure to reduce the cross-sectional area thereof and to form an optical waveguide fiber having a solid cross-section, said first layer forming the core and said second layer and said tube forming the cladding of said optical waveguide fiber.
Claim 3
Dependent Claim
53 words
A method in accordance with claim 1 wherein said first coating of glass is formed by the steps comprising depositing a coating of glass soot on the outside peripheral surface of said mandrel by flame hydrolysis, and heating said soot until it consolidates and forms a dense glass layer free from particle boundaries.
Claim 4
Dependent Claim
19 words
A method in accordance with claim 2 wherein said coating of glass soot is at least 5 mm thick.
Claim 5
Dependent Claim
18 words
A method in accordance with claim 2 wherein said mandrel is removed before said second layer is applied.
Claim 6
Dependent Claim
69 words
A method in accordance with claim 2 wherein said second layer of glass is formed by the steps comprising depositing a second coating of glass soot over the outside peripheral surface of said first layer of glass by flame hydrolysis, and heating said first layer and said second coating of glass soot until said second layer of soot consolidates and forms a dense glass layer free from particle boundaries.
Claim 7
Dependent Claim
48 words
A method in accordance with claim 1 wherein said mandrel is a hollow tube of material selected from the group consisting of glass, ceramic and glass ceramic, and said step of removing said mandrel comprises flowing acid through said tube until said tube is completely removed by etching.
Claim 8
Dependent Claim
104 words
A method in accordance with claim 1 wherein said first and second layers of glass are formed by the steps comprising depositing a first coating of glass soot on the outside peripheral surface of said mandrel by flame hydrolysis, depositing a second coating of soot over the outside peripheral surface of said first coating by flame hydrolysis, and heating the resultant assembly until each coating of glass soot consolidates and forms a dense glass layer free from particle boundaries, said first consolidated coating of soot forming said first layer of glass and said second consolidated layer of soot forming said second layer of glass.
Claim 9
Dependent Claim
49 words
A method in accordance with claim 7 wherein the step of providing a glass tube comprises depositing a coating of glass soot on the outside peripheral surface of a mandrel by flame hydrolysis, heating said soot until it consolidates and forms a dense glass layer, and removing said mandrel.
Claim 10
Dependent Claim
26 words
A method in accordance with claim 1 wherein the refractive index of said tube is equal to the refractive index of said second layer of glass.
Claim 11
Dependent Claim
26 words
A method in accordance with claim 1 wherein the refractive index of said tube is less than the refractive index of said second layer of glass.
Claim 12
Independent Claim
204 words
A method of forming a clad optical waveguide fiber for propagating a single mode of optical wave energy of wavelength λ comprising the steps of providing a substantially cylindrical mandrel, applying a first layer of glass of refractive index n 1 to the outside peripheral surface of said mandrel, applying a second layer of glass having a refractive index n 2 over the outside peripheral surface of said first layer, n 1 being greater than n 2 , removing said mandrel, heating the structure so formed to the drawing temperature of the materials thereof, drawing the heated structure to reduce the cross-sectional area thereof, thereby forming an intermediate fiber, providing a glass tube having a hole extending axially therethrough, disposing at least a portion of said intermediate fiber within said tube, heating the final composite structure so formed to the drawing temperature thereof, and drawing said final composite structure to reduce the cross-sectional area thereof and to form an optical waveguide fiber having a solid cross-section, said first layer forming a core of radius a, wherein a is determined by the equation 2πa/λ) √(n.sub.1 +n.sub.2) (n.sub.1 -n.sub.2) < 2.405 and said second layer and said tube forming the cladding of said optical waveguide fiber.
Claim 13
Independent Claim
204 words
A method of forming a clad optical waveguide fiber for propagating a single mode of optical wave energy of wavelength λ comprising the steps of providing a substantially cylindrical mandrel, applying a first layer of glass of refractive index n 1 to the outside peripheral surface of said mandrel, applying a second layer of glass having a refractive index n 2 over the outside peripheral surface of said first layer, n 1 being greater than n 2 , removing said mandrel, heating the structure so formed to the drawing temperature of the materials thereof, drawing the heated structure to reduce the cross-sectional area thereof, thereby forming an intermediate fiber, providing a glass tube having a hole extending axially therethrough, disposing at least a portion of said intermediate fiber within said tube, heating the final composite structure so formed to the drawing temperature thereof, and drawing said final composite structure to reduce the cross-sectional area thereof and to form an optical waveguide fiber having a solid cross-section, said first layer forming a core of radius a, wherein a is determined by the equation 2πa/λ) √(n.sub.1 +n.sub.2) (n.sub.1 -n.sub.2) < 2.405 and said second layer and said tube forming the cladding of said optical waveguide fiber.
Claim 14
Dependent Claim
107 words
A method in accordance with claim 11 wherein said first and second coatings of glass are formed by the steps comprising depositing a first coating of glass soot on the outside peripheral surface of said mandrel by flame hydrolysis, heating said soot until it consolidates and forms a first dense glass layer free from particle boundaries, depositing a second coating of glass soot over the outside peripheral surface of said first layer of glass by flame hydrolysis, and heating said first layer and said second coating of glass soot until said second coating of soot consolidates and forms a second dense glass layer free from particle boundaries.
Claim 15
Dependent Claim
20 words
A method in accordance with claim 12 wherein said first coating of glass soot is at least 5 mm thick.
Claim 16
Dependent Claim
104 words
A method in accordance with claim 11 wherein said first and second layers of glass are formed by the steps comprising depositing a first coating of glass soot on the outside peripheral surface of said mandrel by flame hydrolysis, depositing a second coating of soot over the outside peripheral surface of said first coating by flame hydrolysis, and heating the resultant assembly until each coating of glass soot consolidates and forms a dense glass layer free from particle boundaries, said first consolidated coating of soot forming said first layer of glass and said second consolidated layer of soot forming said second layer of glass.
Claim 17
Dependent Claim
20 words
A method in accordance with claim 14 wherein said first coating of glass soot is at least 5 mm thick.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-01-12 | 1979-07-14 | 1980-01-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-01-12 | 1983-07-14 | 1984-01-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-01-12 | 1987-07-14 | 1988-01-13 | $7700.00 | Window Closed / Lapsed |