Process for the production of insulating coatings on electrical conductors
Assignee: Axalta Coating Systems Germany GmbH and Co KG
•
Filing: 1974-02-06
•
Granted: 1976-01-06
•
Expires: 1994-02-06
Abstract
Abstract The invention relates to a process for the insulative coating of electrical conductors with thermosetting resins. According to the invention, the resins used are thermosetting ester resins produced from polyhydric alcohols, carboxylic acids with two or more carboxyl groups attached to an aromatic ring and, as optional components, an aliphatic carboxylic acid and amino group-containing compounds. Low molecular weight resins are used containing from 0.85 to 1 mol of polyhydric alcohols per equivalent of co-condensed carboxylic acid. The resins used have a melt viscosity of at most 40,000 m Pa s at 120 DEG C. Coating is preferably carried out using a solvent-free composition, and at a low temperature.
Inventors
- 👤 Karl-Heinz Risken
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 16:16
CPC Classifications
H; H01; H01B; H01B13/00; H01B13/06; H01B3/00; H01B3/18; H01B3/30; H01B3/303; H01B3/306; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2933; Y10T428/294
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
190 words
In a process for the production of an insulating coating on an electrical conductor comprising coating the conductor by passing the conductor through a bath of a thermosetting polyester-based stoving resin comprising a condensation product of a polyvalent aromatic carboxylic acid with a polyhydric alcohol and a stoving catalyst and thereafter heating the coated conductor to an elevated temperature sufficient to cure the condensation product, the improvement which comprises said polyester-based resin being a low molecular weight resin having from about 0.85 to 1 mole of polyhydric alcohol in co-condensed form per equivalent of polycarboxylic acid and having a melt viscosity of from 1,000 to 40,000 m Pa s at a temperature between room temperature and 120° C., said polyester-based resin containing a co-condensed carboxylic acid compound containing a five-membered imide ring and said coating being carried out by passing the conductor through a melt of said resin at a melt temperature between room temperature and 120° C., said melt being substantially free of solvents which do not take part in the reaction by which the polyester resins are produced and containing less than about 10% content of said solvent.
Claim 2
Dependent Claim
190 words
In a process for the production of an insulating coating on an electrical conductor comprising coating the conductor by passing the conductor through a bath of a thermosetting polyester-based stoving resin comprising a condensation product of a polyvalent aromatic carboxylic acid with a polyhydric alcohol and a stoving catalyst and thereafter heating the coated conductor to an elevated temperature sufficient to cure the condensation product, the improvement which comprises said polyester-based resin being a low molecular weight resin having from about 0.85 to 1 mole of polyhydric alcohol in co-condensed form per equivalent of polycarboxylic acid and having a melt viscosity of from 1,000 to 40,000 m Pa s at a temperature between room temperature and 120° C., said polyester-based resin containing a co-condensed carboxylic acid compound containing a five-membered imide ring and said coating being carried out by passing the conductor through a melt of said resin at a melt temperature between room temperature and 120° C., said melt being substantially free of solvents which do not take part in the reaction by which the polyester resins are produced and containing less than about 10% content of said solvent.
Claim 3
Dependent Claim
18 words
A process as defined by claim 1, wherein coating is carried out in the absence of said solvents.
Claim 4
Dependent Claim
21 words
A process as defined by claim 1, wherein the coating composition contains a stoving residue of at least 70% by weight.
Claim 5
Dependent Claim
33 words
A process as defined by claim 1, wherein the polyester resins have a resin melt viscosity of between 1,000 and 30,000 m Pa s at a temperature between room temperature and 120° C.
Claim 6
Dependent Claim
27 words
A process as defined by claim 1, wherein the polyester resins are low molecular weight resins having a number average molecular weight of from 250 to 700.
Claim 7
Dependent Claim
27 words
A process as defined by claim 5, wherein the polyesters contain from 0.95 to 1 mol of polyhydric alcohols in co-condensed form per equivalent of carboxylic acid.
Claim 8
Dependent Claim
23 words
A process as defined by claim 1, wherein the polyester additionally contains co-condensed carboxylic acids or alcohols having a functionality greater than 2.
Claim 9
Dependent Claim
38 words
A process as defined by claim 7, wherein there are from about 5 to about 300 equivalents of said carboxylic acids or alcohols having a functionality greater than 2 per 100 equivalents of dicarboxylic acid in the polyesters.
Claim 10
Dependent Claim
38 words
A process as defined by claim 8, wherein there are from about 50 to about 100 equivalents of said carboxylic acids or alcohols having a functionality greater than 2 per 100 equivalents of dicarboxylic acid in the polyesters.
Claim 11
Dependent Claim
25 words
A process as defined by claim 7, wherein the carboxylic acids or alcohols having a functionality greater than 2 contain 3 or 4 functional groups.
Claim 12
Dependent Claim
26 words
The process as defined by claim 1, wherein said polyester-based stoving resin additionally contains up to about 25 mole % of a co-condensed aliphatic polycarboxylic acid.
Claim 13
Dependent Claim
26 words
The process as defined by claim 1, wherein said polyester-based stoving resin additionally contains up to about 25 mole % of a co-condensed amino group-containing compound.
Claim 14
Dependent Claim
21 words
The process as defined by claim 3, wherein the coating composition contains a stoving residue of at least 80% by weight.
Claim 15
Dependent Claim
21 words
The process as defined by claim 13, wherein the coating composition contains a stoving residue of at least 85% by weight.
Claim 16
Dependent Claim
19 words
The process as defined by claim 1, wherein said melt temperature is between room temperature and about 100° C.
Claim 17
Dependent Claim
19 words
The process as defined by claim 15, wherein said melt temperature is between room temperature and about 60° C.
Claim 18
Dependent Claim
14 words
The process as defined by claim 16, wherein said melt temperature is room temperature.
Claim 19
Dependent Claim
28 words
The process as defined by claim 1, wherein said carboxylic acid compound containing a five-membered imide ring is derived from trimellitic acid or trimellitic anhydride and a diamine.
Claim 20
Dependent Claim
29 words
The process as defined by claim 1, wherein said polyhydric alcohol is selected from the group consisting of glycerin, butylene glycol, propylene glycol, ethylene glycol, tris-(β-hydroxyethyl)-isocyanurate, trimethylolpropane and trimethylolethane.
Claim 21
Dependent Claim
35 words
The process as defined by claim 1, wherein said polycarboxylic acid is selected from the group consisting of terephthalic acid, isophthalic acid, orthophthalic acid, trimellitic acid, pyromellitic acid, esters thereof, anhydrides thereof and tris-(2 carboxyethyl)-isocyanurate.
Claim 22
Dependent Claim
26 words
The process as defined by claim 12, wherein said amino group-containing compound is selected from the group consisting of ethanolamine, ethylene diamine, amino-methylolpropane and p-aminobenzyl alcohol.
References Cited (Backward Citations)
US2216234A
Cited
US2512722A
Cited
US2683100A
Cited
US2671744A
Cited
US2686740A
Cited
US2936296A
Cited
US3058948A
Cited
US3118861A
Cited
US3668275A
Cited
US3707403A
Cited
US3746570A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-01-05 | 1979-07-07 | 1980-01-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-01-05 | 1983-07-07 | 1984-01-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-01-05 | 1987-07-07 | 1988-01-06 | $7700.00 | Window Closed / Lapsed |