Catalysts and catalyst carriers obtained by tableting

Claim 2

A catalyst or catalyst carrier in the form of granules having a definite geometric shape provided with at least one through-bore, the catalyst or catalyst carrier being obtained by compression-shaping a powder comprising the catalyst or catalyst carrier components, or precursors thereof, wherein at least 70% of the volume of the pores stem from pores having a radius corresponding to the peak values of the porosity distribution curve, said powder comprising Fe 2 (MoO 4 ) 3 and MoO 3 .

Claim 3

A catalyst or catalyst carrier in the form of granules having a definite geometric shape provided with at least one through-bore, having resistance to breakage and abrasion at least 10% higher than that of corresponding catalysts or catalyst carriers in the form of granules obtained by compression shaping where lubrication during formation of the granules is carried out by employing a lubricant dispersed in a quantity of 3% by weight in the bulk of the powder to be subjected to shaping to form the granules.

Claim 4

A catalyst or catalyst carrier in the form of granules having a definite geometric shape provided with at least one through-bore, having resistance to breakage and abrasion at least 10% higher than that of corresponding catalysts or catalyst carriers in the form of granules obtained by compression shaping where lubrication during formation of the granules is carried out by employing a lubricant dispersed in a quantity of 3% by weight in the bulk of the powder to be subjected to shaping to form the granules.

Claim 5

The catalyst or catalyst carrier of claim 2, wherein the resistance to breakage and abrasion is at least three times that of corresponding catalysts or catalyst carriers in the form of granules obtained by compression shaping where lubrication during formation of the granules is carried out by employing a lubricant dispersed in a quantity of 3% by weight in the bulk of the powder to be subjected to shaping to form the granules.

Claim 6

A catalyst or catalyst carrier according to claim 1, wherein the granules have a hollow cylindrical form with a circular or polygonal or multi-lobed section with through-bores which have axes which are substantially parallel between themselves and to the axis of the granule and also substantially equidistant one from the other and wherein the ratio between the surface area and the volume of the granules is higher than 2.4.

Claim 7

A catalyst or catalyst carrier according to claim 2, wherein the granules have a hollow cylindrical form with a circular or polygonal or multi-lobed section with through-bores which have axes which are substantially parallel between themselves and to the axis of the granule and also substantially equidistant one from the other and wherein the ratio between the surface area and the volume of the granules is higher than 2.4.

Claim 8

The catalyst or catalyst carrier of claim 4, wherein the granules have a substantially triangular cross-section with rounded extremities and wherein the ratio between the surface area and the volume of the granules is higher than 3.1.

Claim 9

The catalyst or catalyst carrier of claim 4, wherein the granules have a tri-lobed cross-section.

Claim 10

The catalyst or catalyst carrier of claim 2, obtained from powders comprising Fe 2 (MoO 4 ) 3 and MoO 3 .

Claim 11

The catalyst or catalyst carrier of claim 1, obtained from powders comprising alumina.

Claim 12

The catalyst or catalyst carrier of claim 2, obtained from powders comprising alumina.

Claim 13

A process for the preparation of catalysts or catalyst carriers in the form of granules having a definite geometric shape provided with at least one through-bore, the catalyst or catalyst carrier being obtained by compression-shaping a powder comprising the catalyst or catalyst carrier components, or precursors thereof, wherein at least 70% of the volume of the pores stem from pores having a radius corresponding to the peak values of the porosity distribution curve, comprising the steps of: (a) subjecting the powder or precursor to compression shaping using a lubricant, wherein the lubricant is deposited on the surface of the molding and shaping apparatus, to produce a granule; and (b) heating the granule from step (a) in order to activate the catalyst or catalyst carrier.

Claim 14

A process for the preparation of catalysts or catalyst carriers in the form of granules having a definite geometric shape provided with at least one through-bore, the catalyst or catalyst carrier being obtained by compression-shaping a powder comprising the catalyst or catalyst carrier components, or precursors thereof, wherein at least 70% of the volume of the pores stem from pores having a radius corresponding to the peak values of the porosity distribution curve, comprising the steps of: (a) subjecting the powder or precursor to compression shaping using a lubricant, wherein the lubricant is deposited on the surface of the molding and shaping apparatus, to produce a granule; and (b) heating the granule from step (a) in order to activate the catalyst or catalyst carrier.

Claim 15

The process according to claim 11, wherein the lubricant is a solid selected from the group consisting of stearic acid, palmitic acid, and alkaline salts and alkaline-earth salts of said acids.

Claim 16

The process according to claim 11, wherein the lubricant is a liquid selected from the group consisting of glycerides, paraffin oil, and perfluoropolyethers.

Claim 17

The process according to claim 11, wherein the surface of the molding and shaping apparatus is self-lubricating.

Claim 18

A process according to claim 11, wherein the powder to be molded comprises Fe 2 (MoO 4 ) 3 and MoO 3 and the granules obtained are subjected to heat treatment at temperatures from about 400° to about 600° C.

Claim 19

The catalyst or catalyst carrier of claim 2 which is substantially free of sintering.

Claim 20

The catalyst or catalyst carrier of claim 2 further comprising an axial braking load of at least 3.08.