Assignee: Yield10 Bioscience Inc
•
Filing: 1994-06-01
•
Granted: 1998-08-04
•
Expires: 2014-06-01
Abstract
Abstract PCT No. PCT/GB94/01181 Sec. 371 Date Apr. 5, 1996 Sec. 102(e) Date Apr. 5, 1996 PCT Filed Jun. 1, 1994 PCT Pub. No. WO94/28047 PCT Pub. Date Dec. 8, 1994Method of retarding age embrittlement of polyester comprising heat treating the polyester after preparation by cooling below 90 DEG C. and then heating at 90 DEG C. to 160 DEG C. within 24 hours of preparation, and a polyester composition in which ageing is substantially retarded compared to the non-heat treated polyester. The invention encompasses the polyester composition which has been subjected to the method.
Inventors
- 👤 John Jamieson Liggat
- 👤 Gregory O'Brien
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 04:04
CPC Classifications
C; C08; C08G; C08G63/00; C08G63/88; B; B29; B29C; B29C71/00; B29C71/02; C08G63/02; C08G63/06; B29K; B29K2067/00; Y; Y10; Y10S; Y10S264/00; Y10S264/90; Y10S264/901; Y10S264/904
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
117 words
In a process of producing a shaped article at least partly made of a polyhydroxyalkanoate selected from the group consisting of poly-(R)-3-hydroxybutyrate and poly-(R)-3-hydroxybutyrate-co-(R)-valerate by the steps of: (a) shaping by injection molding, compression molding, melting, sintering, extrusion of fiber or film or profile, gas-current spinning, tack spinning, coating of melt onto substrate, coating latex onto substrate, or shaping solution in volatile solvent; (b) allowing the shaped article to cool below 90 deg C.; and (c) heat treating at 90-160 deg C. without substantial change of shape; the improvement wherein step (c) is performed within 24 hours of the end of step (a), whereby the resulting shaped article is characterized by its resistance to brittleness on aging.
Claim 2
Dependent Claim
117 words
In a process of producing a shaped article at least partly made of a polyhydroxyalkanoate selected from the group consisting of poly-(R)-3-hydroxybutyrate and poly-(R)-3-hydroxybutyrate-co-(R)-valerate by the steps of: (a) shaping by injection molding, compression molding, melting, sintering, extrusion of fiber or film or profile, gas-current spinning, tack spinning, coating of melt onto substrate, coating latex onto substrate, or shaping solution in volatile solvent; (b) allowing the shaped article to cool below 90 deg C.; and (c) heat treating at 90-160 deg C. without substantial change of shape; the improvement wherein step (c) is performed within 24 hours of the end of step (a), whereby the resulting shaped article is characterized by its resistance to brittleness on aging.
Claim 3
Dependent Claim
11 words
Process according to claim 1 in which the PHA contains plasticiser.
Claim 4
Dependent Claim
18 words
Process according to claim 1 in which the temperature of step (c) is in the range 100°-140° C.
Claim 5
Dependent Claim
15 words
Process according to claim 1 in which the PHA contains 4-20 mol % of valerate.
Claim 6
Dependent Claim
15 words
Process according to claim 1 in which step (c) takes 5 sec to 20 h.
Claim 7
Dependent Claim
55 words
Process according to claim 1 in which steps (a), (b) and (c) are carried out in immediate succession, the articles formed in step (a) being run through heating zones on a continuous belt and heat being supplied to step (c) by infra red radiation for a period in the range 30 seconds to 15 minutes.
Claim 8
Dependent Claim
42 words
A shaped article made by the process of claim 1 and being at least partly made of poly-(R)-3-hydroxybutyrate-co-(R)-valerate copolymer containing 70-98 mol % of such butyrate units, characterised by not being defective for brittleness for at least one month after being formed.
Claim 9
Dependent Claim
102 words
In a process of producing a shaped article at least partly made of poly-(R)-3-hydroxybutyrate-co-(R)-valerate by the steps of: (a) shaping by injection molding, compression molding, melting, sintering, extrusion of fibre or film or profile, gas-current spinning, tack spinning, coating of melt onto substrate, coating latex onto substrate, or shaping solution in volatile solvent; (b) allowing to cool below 90° C.; and (c) heat treating at 90°-160° C. without substantial change of shape; the improvement which comprises performing step (c) within 24 hours of the end of step (a) whereby the resulting shaped article is characterised by its resistance to brittleness on ageing.
Claim 10
Dependent Claim
102 words
In a process of producing a shaped article at least partly made of poly-(R)-3-hydroxybutyrate-co-(R)-valerate by the steps of: (a) shaping by injection molding, compression molding, melting, sintering, extrusion of fibre or film or profile, gas-current spinning, tack spinning, coating of melt onto substrate, coating latex onto substrate, or shaping solution in volatile solvent; (b) allowing to cool below 90° C.; and (c) heat treating at 90°-160° C. without substantial change of shape; the improvement which comprises performing step (c) within 24 hours of the end of step (a) whereby the resulting shaped article is characterised by its resistance to brittleness on ageing.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-08-03 | 2002-02-02 | 2002-08-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-08-03 | 2006-02-02 | 2006-08-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-08-03 | 2010-02-02 | 2010-08-04 | $7700.00 | Window Closed / Lapsed |