Doped amorphous and crystalline gallium oxides, alkaline earth gallates and doped zinc germanate phosphors as electroluminescent materials
Assignee: Nanolumens Acquisition Inc
•
Filing: 1996-07-03
•
Granted: 1998-03-10
•
Expires: 2016-07-03
Abstract
Abstract New oxide phosphors based on doped gallium oxides, alkaline earth gallates and germanates for electroluminescent display materials. Bright orange red electroluminescence has been obtained in amorphous and crystalline oxides Ga2O3:Eu for the first time. SrGa2O4 and SrGa4O9 doped with 1-8 mole % of Eu and Tb, CaGa2O4, Ca3Ga2O6 and CaGa4O7 doped with 1-4 mole % of Eu, Tb, Pr and Dy, BaGa2O4 doped with 1-2 mole % of Eu and Tb, have been prepared using RF magnetron sputtering onto ceramic dielectric substrates and annealed at 600 DEG C.-950 DEG C. in air or Ar for 1-2 hours. Bright electroluminescent (EL) emission was obtained with wavelengths covering the visible spectrum from 400 to 700 nm, and infrared emission above 700 nm with spectral peaks characteristic of rare earth transitions. The films of CaGa2O4 with 1 mole % Eu achieved 22 fL (75 cd/m2) at 60 Hz and had a maximum efficiency of 0.2 lm/w for red emission. An amorphous thin film of Ca3Ga2O6 with 2 mole % Eu achieved 34 fL in red EL at 60 Hz when annealed at 600 DEG C. SrGa2O4 with 1 mole % Eu and 4 mole % Tb yielded "white" phosphor having red, green and blue emission (13 fL at 60 Hz), and SrGa2O4 with 8 mole % Tb resulted in a blue and green phosphor measuring 30 fL at 60 Hz. Zn2Si0.5Ge0.5O4 containing Mn was sputtered using magnetron RF sputtering onto ceramic dielectric substrates and annealed at 700 DEG C. for 1 hour in air or argon. Bright green (540 nm) emission was obtained in electroluminescence: 110 fL (377 cd/m2) at 60 Hz with a maximum efficiency of 0.9 l/w. Moderately bright red emission (640 nm) was also obtained.
Inventors
- 👤 Adrian H. Kitai
- 👤 Tian Xiao
- 👤 Guo Liu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 13:41
CPC Classifications
H; H05; H05B; H05B33/00; H05B33/12; H05B33/14; C; C09; C09K; C09K11/00; C09K11/08; C09K11/66; C09K11/661; C09K11/662; C09K11/666; C09K11/77; C09K11/7701; C09K11/7703; C09K11/7728; C09K11/7729; C09K11/7731; C09K11/7743; C09K11/7744; C09K11/7746; C09K11/7766; C09K11/7767; C09K11/7768; C09K11/7783; C09K11/7784; C09K11/7786; H05B33/10
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
75 words
A phosphor having the formula CaGa 2 O 4 :n%RE wherein RE is a rare earth dopant selected from the group consisting of Eu, Tb, Pr and combinations thereof, n % is the mole percent of RE present in CaGa 2 O 4 , and spans the range in which said rare earths are soluble in CaGa 2 O 4 , said phosphor characterized by electroluminescence when an effective voltage is applied across said phosphor.
Claim 2
Dependent Claim
75 words
A phosphor having the formula CaGa 2 O 4 :n%RE wherein RE is a rare earth dopant selected from the group consisting of Eu, Tb, Pr and combinations thereof, n % is the mole percent of RE present in CaGa 2 O 4 , and spans the range in which said rare earths are soluble in CaGa 2 O 4 , said phosphor characterized by electroluminescence when an effective voltage is applied across said phosphor.
Claim 3
Dependent Claim
81 words
A phosphor having the formula Ca 3 Ga 2 O 6 :n%RE wherein RE is a rare earth dopant selected from the group consisting of Eu and Tb and combinations thereof, n % is the mole percent of RE present in Ca 3 Ga 2 O 6 , and spans the range in which said rare earths are soluble in Ca 3 Ga 2 O 6 , said phosphor characterized by electroluminescence when an effective voltage is applied across said phosphor.
Claim 4
Dependent Claim
81 words
A phosphor having the formula Ca 3 Ga 2 O 6 :n%RE wherein RE is a rare earth dopant selected from the group consisting of Eu and Tb and combinations thereof, n % is the mole percent of RE present in Ca 3 Ga 2 O 6 , and spans the range in which said rare earths are soluble in Ca 3 Ga 2 O 6 , said phosphor characterized by electroluminescence when an effective voltage is applied across said phosphor.
Claim 5
Dependent Claim
75 words
A phosphor having the formula CaGa 4 O 7 :n%RE wherein RE is a rare earth dopant selected from the group consisting of Eu, Dy, Tb and combinations thereof, n % is the mole percent of RE present in CaGa 4 O 7 , and spans the range in which said rare earths are soluble in CaGa 4 O 7 , said phosphor characterized by electroluminescence when an effective voltage is applied across said phosphor.
Claim 6
Dependent Claim
75 words
A phosphor having the formula CaGa 4 O 7 :n%RE wherein RE is a rare earth dopant selected from the group consisting of Eu, Dy, Tb and combinations thereof, n % is the mole percent of RE present in CaGa 4 O 7 , and spans the range in which said rare earths are soluble in CaGa 4 O 7 , said phosphor characterized by electroluminescence when an effective voltage is applied across said phosphor.
Claim 7
Dependent Claim
52 words
A phosphor having the formula Sr 3 Ga 4 O 9 :n%Tb, wherein n % is the mole percent of Tb and spans the range in which Tb is soluble in Sr 3 Ga 4 O 9 , said phosphor characterized by electroluminescence when an effective voltage is applied across said phosphor.
Claim 8
Dependent Claim
52 words
A phosphor having the formula Sr 3 Ga 4 O 9 :n%Tb, wherein n % is the mole percent of Tb and spans the range in which Tb is soluble in Sr 3 Ga 4 O 9 , said phosphor characterized by electroluminescence when an effective voltage is applied across said phosphor.
Claim 9
Dependent Claim
81 words
A compound having a formula Ga 2 O 3 :n 1 %Eu,n 2 %Cd, wherein n 1 % is the mole percent amount of Eu present in Ga 2 O 3 and spans the range in which Eu is soluble in Ga 2 O 3 , and n 2 % is the mole percent amount of Cd present in Ga 2 O 3 and spans the range in which Cd is soluble in Ga 2 O 3 but not exceeding 14.3%.
Claim 10
Dependent Claim
81 words
A compound having a formula Ga 2 O 3 :n 1 %Eu,n 2 %Cd, wherein n 1 % is the mole percent amount of Eu present in Ga 2 O 3 and spans the range in which Eu is soluble in Ga 2 O 3 , and n 2 % is the mole percent amount of Cd present in Ga 2 O 3 and spans the range in which Cd is soluble in Ga 2 O 3 but not exceeding 14.3%.
Claim 11
Dependent Claim
63 words
A compound having a formula SrGa 2 O 4 :n%RE, wherein RE is a rare earth selected from the group consisting of Tb and a combination of Tb and Eu, and wherein n % is the mole percent of RE present in SrGa 2 O 4 and spans the range in which said rare earths are soluble in SrGa 2 O 4 .
Claim 12
Dependent Claim
63 words
A compound having a formula SrGa 2 O 4 :n%RE, wherein RE is a rare earth selected from the group consisting of Tb and a combination of Tb and Eu, and wherein n % is the mole percent of RE present in SrGa 2 O 4 and spans the range in which said rare earths are soluble in SrGa 2 O 4 .
Claim 13
Dependent Claim
63 words
A compound having a formula BaGa 2 O 4 :n%RE, wherein RE is a rare earth selected from the group consisting of Tb and a combination of Tb and Eu, and wherein n % is the mole percent of RE present in BaGa 2 O 4 and spans the range in which said rare earths are soluble in BaGa 2 O 4 .
Claim 14
Dependent Claim
63 words
A compound having a formula BaGa 2 O 4 :n%RE, wherein RE is a rare earth selected from the group consisting of Tb and a combination of Tb and Eu, and wherein n % is the mole percent of RE present in BaGa 2 O 4 and spans the range in which said rare earths are soluble in BaGa 2 O 4 .
Claim 15
Dependent Claim
67 words
A compound having a formula Ca 3 Ga 2 O 6 :n%RE, wherein RE is a rare earth selected from the group consisting of Eu and Tb and combinations thereof, wherein n % is the mole percent of RE present in Ca 3 Ga 2 O 6 , and spans the range in which said rare earths are soluble in Ca 3 Ga 2 O 6 .
Claim 16
Dependent Claim
67 words
A compound having a formula Ca 3 Ga 2 O 6 :n%RE, wherein RE is a rare earth selected from the group consisting of Eu and Tb and combinations thereof, wherein n % is the mole percent of RE present in Ca 3 Ga 2 O 6 , and spans the range in which said rare earths are soluble in Ca 3 Ga 2 O 6 .
Claim 17
Dependent Claim
61 words
A compound having a formula CaGa 4 O 7 :n%RE, wherein RE is a rare earth selected from the group consisting of Eu, Dy, Tb and combinations thereof, wherein n % is the mole percent of RE present in CaGa 4 O 7 , and spans the range in which said rare earths are soluble in CaGa 4 O 7 .
Claim 18
Dependent Claim
61 words
A compound having a formula CaGa 4 O 7 :n%RE, wherein RE is a rare earth selected from the group consisting of Eu, Dy, Tb and combinations thereof, wherein n % is the mole percent of RE present in CaGa 4 O 7 , and spans the range in which said rare earths are soluble in CaGa 4 O 7 .
Claim 19
Dependent Claim
40 words
A compound having a formula SrGa 4 O 9 :n%Tb, wherein n % is the mole percent of Tb in SrGa 4 O 9 , and spans the range in which Tb is soluble in SrGa 4 O 9 .
Claim 20
Dependent Claim
40 words
A compound having a formula SrGa 4 O 9 :n%Tb, wherein n % is the mole percent of Tb in SrGa 4 O 9 , and spans the range in which Tb is soluble in SrGa 4 O 9 .
Claim 21
Dependent Claim
61 words
A compound having a formula CaGa 2 O 4 :n%RE, wherein RE is a rare earth selected from the group consisting of Eu, Tb, Pr and combinations thereof, wherein n % is the mole percent of RE present in CaGa 2 O 4 , and spans the range in which said rare earths are soluble in CaGa 2 O 4 .
Claim 22
Dependent Claim
61 words
A compound having a formula CaGa 2 O 4 :n%RE, wherein RE is a rare earth selected from the group consisting of Eu, Tb, Pr and combinations thereof, wherein n % is the mole percent of RE present in CaGa 2 O 4 , and spans the range in which said rare earths are soluble in CaGa 2 O 4 .
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-03-09 | 2001-09-08 | 2002-03-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-03-09 | 2005-09-08 | 2006-03-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-03-09 | 2009-09-08 | 2010-03-10 | $7700.00 | Window Closed / Lapsed |