Dehydration of hydrogels
Assignee: Howmedica Osteonics Corp
•
Filing: 1995-06-02
•
Granted: 1998-01-06
•
Expires: 2015-06-02
Abstract
Abstract A method of dehydration of bulky hydrogel samples of polyvinyl alcohol (i.e., PVA) and a method of preparation of prosthetic nuclei for vertebral discs are given. A method of gamma irradiation sterilization of PVA gel samples which does not incur the side effects of discoloration and of increased crystallinity (i.e., further reduction of water content) is also given. A method of dehydrating bulky hydrogel samples of polyvinyl alcohol (i.e., PVA) so that no significant distortion in the samples results, comprises: (a) subjecting the sample to a solvent system comprising at least one organic solvent which (1) has a solubility for PVA which is less than the solubility of water for PVA and (2) is miscible with water for a length of time generally from about 2 to about 10 days so that the dehydration rate of the hydrogel samples is sufficiently slow so as not to cause any distortions on the dehydrated samples.
Inventors
- 👤 Qi-Bin Bao
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 07:21
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/28; C08F; C08F6/00; C08F6/24; C08J7/00; C08J7/02; C08J2329/00; C08J2329/02; C08J2329/04; Y; Y10; Y10S; Y10S524/00; Y10S524/916
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
128 words
A method of dehydrating a bulky hydrogel sample of polyvinyl alcohol (PVA) so that no significant distortion in the sample results, said method comprising subjecting said bulky hydrogel sample which has already been formed to a solvent system comprising at least one organic solvent (1) having a solubility for PVA which is less than the solubility of water for PVA and (2) being miscible with water and (3) being such that any mixture of water and said organic solvent has a solubility for PVA less than the solubility of water for PVA, wherein the water content of the PVA hydrogel sample is within the critical range from about 75 to about 65 weight percent water, and the dehydration rate is sufficiently slow so that no significant distortions occur.
Claim 2
Independent Claim
128 words
A method of dehydrating a bulky hydrogel sample of polyvinyl alcohol (PVA) so that no significant distortion in the sample results, said method comprising subjecting said bulky hydrogel sample which has already been formed to a solvent system comprising at least one organic solvent (1) having a solubility for PVA which is less than the solubility of water for PVA and (2) being miscible with water and (3) being such that any mixture of water and said organic solvent has a solubility for PVA less than the solubility of water for PVA, wherein the water content of the PVA hydrogel sample is within the critical range from about 75 to about 65 weight percent water, and the dehydration rate is sufficiently slow so that no significant distortions occur.
Claim 3
Dependent Claim
49 words
A method according to claim 1, wherein said at least one organic solvent consists essentially of a solvent selected from the group consisting of ethanol, methanol, ethylene glycol, and mixtures thereof and wherein the dehydration rate is at or below about 0.2 weight percent water content decrease per hour.
Claim 4
Dependent Claim
26 words
A method according to claim 2, wherein said solvent system consists of a single solvent selected from the group consisting of ethanol, methanol and ethylene glycol.
Claim 5
Dependent Claim
23 words
A method according to claim 2, wherein said sample size before dehydration is within the range from about 6 to about 7 grams.
Claim 6
Dependent Claim
21 words
A method according to claim 4, wherein said water content before dehydration of said sample is about 86 weight percent water.
Claim 7
Dependent Claim
34 words
A method according to claim 5, wherein said sample is subjected to dehydration by use of an organic solvent system for a time period within the range from about 2 to about 10 days.
Claim 8
Dependent Claim
25 words
A method according to claim 6, wherein said sample has a surface area to volume ratio within the range from about 2.5 to about 5.
Claim 9
Dependent Claim
107 words
A method according to claim 1, wherein said at least one organic solvent is selected from the group consisting of acetonitrile, 2-propanol, acetone and glycerol, and mixtures thereof and wherein said at least one organic solvent is mixed with water so as to provide an initial organic solvent concentration less than or equal to about 60 weight percent organic solvent in water, for a period of time of at least about 2 days, for a sample size of about 6 to about 7 grams, and for a PVA hydrogel nucleus implant of initial water content within the range from about 75 to about 65 weight percent water.
Claim 10
Independent Claim
145 words
A method of dehydrating a polyvinyl alcohol (PVA) hydrogel sample so as to preserve the original shape of said sample and so as to preserve the rehydration capability of said sample, that is, the ability of the sample to return to its original water content and thus not to have its crystallinity affected, said method comprising wherein the water content of the PVA hydrogel sample which has already been formed is within the critical range from about 75 to 65 weight percent water, subjecting said sample to a solvent system comprising at least one organic solvent (1) having a solubility for PVA which is less than the solubility of water for PVA and (2) being miscible with water, for a length of time from about 2 to about 10 days, so as to produce a dehydration rate sufficiently slow so that no significant distortions occur.
Claim 11
Independent Claim
145 words
A method of dehydrating a polyvinyl alcohol (PVA) hydrogel sample so as to preserve the original shape of said sample and so as to preserve the rehydration capability of said sample, that is, the ability of the sample to return to its original water content and thus not to have its crystallinity affected, said method comprising wherein the water content of the PVA hydrogel sample which has already been formed is within the critical range from about 75 to 65 weight percent water, subjecting said sample to a solvent system comprising at least one organic solvent (1) having a solubility for PVA which is less than the solubility of water for PVA and (2) being miscible with water, for a length of time from about 2 to about 10 days, so as to produce a dehydration rate sufficiently slow so that no significant distortions occur.
Claim 12
Dependent Claim
49 words
A method according to claim 9, wherein said at least one organic solvent consists essentially of a solvent selected from the group consisting of ethanol, methanol, ethylene glycol, and mixtures thereof and wherein the dehydration rate is at or below about 0.2 weight percent water content decrease per hour.
Claim 13
Dependent Claim
26 words
A method according to claim 10, wherein said solvent system consists of a single solvent selected from the group consisting of ethanol, methanol and ethylene glycol.
Claim 14
Dependent Claim
107 words
A method according to claim 11, wherein said at least one organic solvent is selected from the group consisting of acetonitrile, 2-propanol, acetone and glycerol, and mixtures thereof and wherein said at least one organic solvent is mixed with water so as to provide an initial organic solvent concentration less than or equal to about 60 weight percent organic solvent in water, for a period of time of at least about 2 days, for a sample size of about 6 to about 7 grams, and for a PVA hydrogel nucleus implant of initial water content within the range from about 75 to about 65 weight percent water.
Claim 15
Dependent Claim
24 words
A method according to claim 12, wherein said sample size initially (before dehydration) is within the range from about 6 to about 7 grams.
Claim 16
Dependent Claim
22 words
A method according to claim 13, wherein said original water content before dehydration of said sample is about 86 weight percent water.
Claim 17
Dependent Claim
34 words
A method according to claim 14, wherein said sample is subjected to dehydration by use of an organic solvent system for a time period within the range from about 2 to about 10 days.
Claim 18
Dependent Claim
24 words
A method according to claim 15, wherein said sample has a surface to volume ratio within the range from about 2.5 to about 5.
Claim 19
Dependent Claim
82 words
A method of subjecting a sample of polyvinyl alcohol (PVA) gel to sterilization by gamma ray irradiation without the sample incurring the side effects of discoloration and further reduction of its water content and increased crystallinity, said method comprising (1) subjecting said polyvinyl alcohol sample which has already been formed to the method of claim 1, so as to produce a dehydrated gel sample dehydrated by the solvent system method; and (2) then subjecting said dehydrated gel sample to gamma ray irradiation.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-01-05 | 2001-07-07 | 2002-01-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-01-05 | 2005-07-07 | 2006-01-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-01-05 | 2009-07-07 | 2010-01-06 | $7700.00 | Window Closed / Lapsed |