US5350484A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for the anisotropic etching of metal films in the fabrication of interconnects
Assignee: Micron Technology Inc
•
Filing: 1992-09-08
•
Granted: 1994-09-27
•
Expires: 2012-09-08
Abstract
Abstract The present invention discloses a method for anisotropically etching metal interconnects in the fabrication of semiconductor devices, especially ULSI interconnects having high aspect ratios. A metal film is first deposited on the appropriate layer of a semiconductor substrate by techniques well-known in the art. A mask layer is deposited over the metal film with openings defined in the mask layer for patterning of the metal film. Ions are then introduced into an exposed region of the metal film to anisotropically form a converted layer of the metal film comprising compounds of the metal. The introduction of the ions into the metal film can be performed by conventional methods, such as through the use of a reactive ion etch system or an ion implantation system, or by any other method which anisotropically forms the metal compounds. The mask layer is then removed by conventional means to leave behind the metal film having a converted layer of metal compounds. Finally, the metal compounds are selectively removed by a suitable removal means chosen for its properties in removing the metal compounds without causing significant etching or degradation of the metal film itself.
Inventors
- 👤 Donald S. Gardner
- 👤 Xiao-Chun Mu
- 👤 David B. Fraser
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 18:14
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/031; H10P; H10P50/00; H10P50/20; H10P50/26; H10P50/264; H10P50/266; H10P50/267
Claims Analysis
Total Claims: 55
Claim 1
Independent Claim
71 words
In the fabrication of a semiconductor device, a method is provided for etching a metal film formed over a semiconductor substrate comprising the steps of: implanting ions into a region of the metal film to form a converted layer of metal compounds in the region; and selectively removing the converted layer by etching the metal compounds at low temperatures with an etchant chosen to prevent substantial etching of the metal film.
Claim 2
Dependent Claim
71 words
In the fabrication of a semiconductor device, a method is provided for etching a metal film formed over a semiconductor substrate comprising the steps of: implanting ions into a region of the metal film to form a converted layer of metal compounds in the region; and selectively removing the converted layer by etching the metal compounds at low temperatures with an etchant chosen to prevent substantial etching of the metal film.
Claim 3
Dependent Claim
35 words
The method of claim 1, wherein the method further comprises the step of forming a mask on the metal film to define the preselected region of the metal film to be exposed to the ions.
Claim 4
Dependent Claim
28 words
The method of claim 2, wherein the mask comprises a hard mask selected from the group consisting of dielectric films, metal films and tightly bonded metal oxide films.
Claim 5
Dependent Claim
12 words
The method of claim 2, wherein the mask comprises a photoresist layer.
Claim 6
Dependent Claim
22 words
The method of claim 2, wherein the method further comprises the step of removing the mask after the converted layer is formed.
Claim 7
Dependent Claim
35 words
The method of claim 1, wherein the method further comprises the step of forming an implant barrier layer beneath the metal film to prevent the ions from penetrating into layers beneath the implant barrier layer.
Claim 8
Dependent Claim
24 words
The method of claim 6, wherein the implant barrier comprises a material that is electrically and chemically stable with respect to the ions implanted.
Claim 9
Dependent Claim
31 words
The method of claim 1, wherein the method further comprises the step of thermally treating the semiconductor substrate after the region is converted to assist in formation of the metal compounds.
Claim 10
Dependent Claim
36 words
The method of claim 1, wherein the metal film comprises copper, the ions comprise chlorine ions and the etchant is selected from the group consisting of HCl, NH 4 OH, MeOH, ether, alcohol, acetone and water.
Claim 11
Dependent Claim
39 words
The method of claim 1, wherein the metal film comprises copper, the ions comprise oxygen ions and the etchant is selected from the group consisting of HCl, NH 4 OH, NH 4 Cl, KCN, NH 4 F and acid.
Claim 12
Dependent Claim
34 words
The method of claim 1, wherein the metal film comprises copper, the ions comprise fluorine ions and the etchant is selected from the group consisting of HCl, HF, H 2 O and mineral acid.
Claim 13
Dependent Claim
41 words
The method of claim 1, wherein the metal film comprises copper, the ions comprise bromine ions and the etchant is selected from the group consisting of HCl, NH 4 OH, HBr, H 2 O, NH 3 , acetone, alcohol and pyridine.
Claim 14
Dependent Claim
33 words
The method of claim 1, wherein the metal film comprises copper, the ions comprise Iodine ions and the etchant is selected from the group consisting of HCl, KI, KCN and NH 3 .
Claim 15
Dependent Claim
39 words
The method of claim 1, wherein the metal film comprises molybdenum, the ions comprise oxygen ions and the etchant is selected from the group consisting of H 2 O, NH 4 OH, acid, and a solution comprising alkaline sulfur.
Claim 16
Dependent Claim
33 words
The method of claim 1, wherein the metal film comprises silver, the ions comprise fluorine ions and the etchant is selected from the group consisting of H 2 O and NH 4 OH.
Claim 17
Dependent Claim
32 words
The method of claim 1, wherein the metal film comprises silver, the ions comprise oxygen ions and the etchant is selected from the group consisting of NH 4 OH, acid and alcohol.
Claim 18
Dependent Claim
92 words
In the fabrication of a semiconductor device, a method is provided for etching a metal film formed over a semiconductor substrate comprising the steps of: forming an implant barrier layer on the semiconductor substrate; forming the metal film on the implant barrier layer; implanting ions into a region of the metal film to form a converted layer of metal compounds within the region, the implant barrier layer preventing the ions from penetrating into layers beneath the implant barrier layer; and selectively removing the converted layer without substantial etching of the metal film.
Claim 19
Dependent Claim
92 words
In the fabrication of a semiconductor device, a method is provided for etching a metal film formed over a semiconductor substrate comprising the steps of: forming an implant barrier layer on the semiconductor substrate; forming the metal film on the implant barrier layer; implanting ions into a region of the metal film to form a converted layer of metal compounds within the region, the implant barrier layer preventing the ions from penetrating into layers beneath the implant barrier layer; and selectively removing the converted layer without substantial etching of the metal film.
Claim 20
Dependent Claim
24 words
The method of claim 17, wherein the step of removing the converted layer is performed by applying an etchant to etch the metal compounds.
Claim 21
Dependent Claim
36 words
The method of claim 18, wherein the metal film comprises copper, the ions comprise chlorine ions and the etchant is selected from the group consisting of HCl, NH 4 OH, MeOH, ether, alcohol, acetone and water.
Claim 22
Dependent Claim
39 words
The method of claim 18, wherein the metal film comprises copper, the ions comprise oxygen ions and the etchant is selected from the group consisting of HCl, NH 4 OH, NH 4 Cl, KCN, NH 4 F and acid.
Claim 23
Dependent Claim
34 words
The method of claim 18, wherein the metal film comprises copper, the ions comprise fluorine ions and the etchant is selected from the group consisting of HCl, HF, H 2 O and mineral acid.
Claim 24
Dependent Claim
41 words
The method of claim 18, wherein the metal film comprises copper, the ions comprise bromine ions and the etchant is selected from the group consisting of HCl, NH 4 OH, HBr, H 2 O, NH 3 , acetone, alcohol and pyridine.
Claim 25
Dependent Claim
33 words
The method of claim 18, wherein the metal film comprises copper, the ions comprise iodine ions and the etchant is selected from the group consisting of HCl, KI, KCN and NH 3 .
Claim 26
Dependent Claim
39 words
The method of claim 18, wherein the metal film comprises molybdenum, the ions comprise oxygen ions and the etchant is selected from the group consisting of H 2 O, NH 4 OH, acid and a solution comprising alkaline sulfur.
Claim 27
Dependent Claim
33 words
The method of claim 18, wherein the metal film comprises silver, the ions comprise fluorine ions and the etchant is selected from the group consisting of H 2 O and NH 4 OH.
Claim 28
Dependent Claim
32 words
The method of claim 18, wherein the metal film comprises silver, the ions comprise oxygen ions and the etchant is selected from the group consisting of NH 4 OH, acid and alcohol.
Claim 29
Dependent Claim
24 words
The method of claim 17, wherein the implant barrier comprises a material that is electrically and chemically stable with respect to the ions implanted.
Claim 30
Dependent Claim
35 words
The method of claim 17, wherein the method further comprises the step of thermally treating the semiconductor substrate after the ions are implanted into the region to assist in the formation of the metal compounds.
Claim 31
Dependent Claim
35 words
The method of claim 17, wherein the metal film comprises copper, the ions comprise chlorine ions and the step of removing the metal compounds is performed by evaporating the metal compounds in a ligand ambient.
Claim 32
Dependent Claim
35 words
The method of claim 17, wherein the metal film comprises copper, the plasma comprises bromine ions and the step of removing the metal compounds is performed by evaporating the metal compounds in a ligand ambient.
Claim 33
Dependent Claim
35 words
The method of claim 17, wherein the method further comprises the step of forming a mask on the metal film to define the preselected region of the metal film to be exposed to the ions.
Claim 34
Dependent Claim
63 words
In the fabrication of a semiconductor device, a method is provided for etching a metal film formed on a semiconductor substrate comprising the steps of: exposing the semiconductor substrate to a plasma comprising ions under an electric potential to reactively form metal compounds within a region of the metal film; and selectively removing the converted layer without substantial etching of the metal film.
Claim 35
Dependent Claim
63 words
In the fabrication of a semiconductor device, a method is provided for etching a metal film formed on a semiconductor substrate comprising the steps of: exposing the semiconductor substrate to a plasma comprising ions under an electric potential to reactively form metal compounds within a region of the metal film; and selectively removing the converted layer without substantial etching of the metal film.
Claim 36
Dependent Claim
24 words
The method of claim 32, wherein the step of exposing the semiconductor substrate to a plasma is performed in a reactive ion etch system.
Claim 37
Dependent Claim
32 words
The method of claim 33, wherein the method further comprises the step of heating the semiconductor substrate to at least 200° Celsius during the exposure of the semiconductor substrate to the plasma.
Claim 38
Dependent Claim
35 words
The method of claim 33, wherein the metal film comprises copper, the plasma comprises chlorine ions and the step of removing the metal compounds is performed by evaporating the metal compounds in a ligand ambient.
Claim 39
Dependent Claim
34 words
The method of claim 33, wherein the metal comprises copper, the plasma comprises bromine ions and the step of removing the metal compounds is performed by evaporating the metal compounds in a ligand ambient.
Claim 40
Dependent Claim
24 words
The method of claim 33, wherein the step of removing the converted layer is performed by applying an etchant to etch the metal compounds.
Claim 41
Dependent Claim
36 words
The method of claim 33, wherein the metal film comprises copper, the ions comprise chlorine ions and the etchant is selected from the group consisting of HCl, NH 4 OH, MeOH, ether, alcohol, acetone and water.
Claim 42
Dependent Claim
39 words
The method of claim 33, wherein the metal film comprises copper, the ions comprise oxygen ions and the etchant is selected from the group consisting of HCl, NH 4 OH, NH 4 Cl, KCN, NH 4 F and acid.
Claim 43
Dependent Claim
34 words
The method of claim 33, wherein the metal film comprises copper, the ions comprise fluorine ions and the etchant is selected from the group consisting of HCl, HF, H 2 O and mineral acid.
Claim 44
Dependent Claim
41 words
The method of claim 33, wherein the metal film comprises copper, the ions comprise bromine ions and the etchant is selected from the group consisting of HCl, NH 4 OH, HBr, H 2 O, NH 3 , acetone, alcohol and pyridine.
Claim 45
Dependent Claim
33 words
The method of claim 33, wherein the metal film comprises copper, the ions comprise iodine ions and the etchant is selected from the group consisting of HCl, KI, KCN and NH 3 .
Claim 46
Dependent Claim
39 words
The method of claim 33, wherein the metal film comprises molybdenum, the ions comprise oxygen ions and the etchant is selected from the group consisting of H 2 O, NH 4 OH, acid, and a solution comprising alkaline sulfur.
Claim 47
Dependent Claim
33 words
The method of claim 33, wherein the metal film comprises silver, the ions comprise fluorine ions and the etchant is selected from the group consisting of H 2 O and NH 4 OH.
Claim 48
Dependent Claim
32 words
The method of claim 33, wherein the metal film comprises silver, the ions comprise oxygen ions and the etchant is selected from the group consisting of NH 4 OH, acid and alcohol.
Claim 49
Dependent Claim
35 words
The method of claim 32, wherein the method further comprises the step of forming a mask on the metal film to define the preselected region of the metal film to be exposed to the ions.
Claim 50
Dependent Claim
28 words
The method of claim 46, wherein the mask comprises a hard mask selected from the group consisting of dielectric films, metal films and tightly bonded metal oxide films.
Claim 51
Dependent Claim
12 words
The method of claim 46, wherein the mask comprises a photoresist layer.
Claim 52
Dependent Claim
22 words
The method of claim 46, wherein the method further comprises the step of removing the mask after the converted layer is formed.
Claim 53
Dependent Claim
28 words
The method of claim 46, wherein the mask comprises a hard mask selected from the group consisting of dielectric films, metal films and tightly bonded metal oxide films.
Claim 54
Dependent Claim
12 words
The method of claim 46, wherein the mask comprises a photoresist layer.
Claim 55
Dependent Claim
22 words
The method of claim 46, wherein the method further comprises the step of removing the mask after the converted layer is formed.
References Cited (Backward Citations)
US3637381A
Cited
JPS55157234A
Cited
JPS5662737A
Cited
US4333226A
Cited
US4352716A
Cited
US4451327A
Cited
US4468284A
Cited
GB2159327A
Cited
JPS6132428A
Cited
US4652334A
Cited
US5158629A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-09-26 | 1998-03-28 | 1998-09-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-09-26 | 2002-03-28 | 2002-09-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-09-26 | 2006-03-28 | 2006-09-27 | $7700.00 | Window Closed / Lapsed |