Chromium alloy electrodeposition and surface fixation of calcium phosphate ceramics
Assignee: Johns Hopkins University
•
Filing: 1993-06-17
•
Granted: 1994-08-16
•
Expires: 2013-06-17
Abstract
Abstract Process for simultaneous electrodeposition of at least a two component alloy system of cobalt and chromium on a substrate, by providing an aqueous solution of divalent cobalt and trivalent chromium ions and containing ethylenediaminetetraacetic acid, at a pH of about 3 to about 5, electrolyzing the solution in an electrolyte cell containing an anode and a cathode, and codepositing cobalt and chromium on the cathode, e.g. titanium, as substrate. According to a preferred embodiment molybdenum-containing ions are also added to the electrolyte, resulting in codeposition of an alloy of cobalt, chromium and molybdenum. In another embodiment, a calcium phosphate ceramic such as hydroxyapatite (HA)is added to the above electrolyte solution, resulting, e.g. , in a codeposit of the calcium phosphate material, e.g. HA, and an alloy of cobalt, chromium and molybdenum. In still another embodiment, a calcium phosphate material such as HA, which has been previously attached to a substrate by sintering, is fixated by simultaneous electrodeposition of cobalt-chromium-molybdenum alloy, such codeposits having utility for improvement of medical implants.
Inventors
- 👤 George W. Maybee
- 👤 Timothy E. Taylor
- 👤 Elmer L. Field
- 👤 Clyde Riley
- 👤 William R. Lacefield, Jr.
- 👤 Harold D. Coble
- 👤 Harini Dasarathy
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 14:55
CPC Classifications
A; A61; A61L; A61L27/00; A61L27/28; A61L27/30; A61L27/306; A61L27/32; C; C25; C25D; C25D15/00; C25D15/02; C25D3/00; C25D3/02; C25D3/56; C25D3/562; A61F; A61F2310/00; A61F2310/00389; A61F2310/00592; A61F2310/00796
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
68 words
A process for simultaneous electrodeposition of at least a two component alloy system of cobalt and chromium on a substrate which comprises electrolyzing an aqueous solution consisting essentially of divalent cobalt and trivalent chromium ions and ethylenediaminetetraacetic acid, at a pH of about 3 to about 5, in an electrolytic cell containing an anode and a cathode, and codepositing cobalt and chromium on said cathode as the substrate.
Claim 2
Dependent Claim
68 words
A process for simultaneous electrodeposition of at least a two component alloy system of cobalt and chromium on a substrate which comprises electrolyzing an aqueous solution consisting essentially of divalent cobalt and trivalent chromium ions and ethylenediaminetetraacetic acid, at a pH of about 3 to about 5, in an electrolytic cell containing an anode and a cathode, and codepositing cobalt and chromium on said cathode as the substrate.
Claim 3
Dependent Claim
89 words
A process for simultaneous electrodeposition of at least a two component alloy system of cobalt and chromium on a substrate which comprises electrolyzing an aqueous solution consisting essentially of divalent cobalt, trivalent chromium ions and ethylenediaminetetraacetic acid, at a pH of about 3 to about 5, using an anode selected from the group consisting of carbon, platinum and lead, and a cathode selected from the group consisting of titanium and alloys thereof, stainless steel, copper and cobalt-chromium-molybdenum alloy, and codepositing cobalt and chromium on said cathode as the substrate.
Claim 4
Dependent Claim
89 words
A process for simultaneous electrodeposition of at least a two component alloy system of cobalt and chromium on a substrate which comprises electrolyzing an aqueous solution consisting essentially of divalent cobalt, trivalent chromium ions and ethylenediaminetetraacetic acid, at a pH of about 3 to about 5, using an anode selected from the group consisting of carbon, platinum and lead, and a cathode selected from the group consisting of titanium and alloys thereof, stainless steel, copper and cobalt-chromium-molybdenum alloy, and codepositing cobalt and chromium on said cathode as the substrate.
Claim 5
Dependent Claim
31 words
The process of claim 1, including employing an amount of said ethylenediaminetetraacetic acid sufficient to provide said codeposited alloy of cobalt and chromium containing up to about 33% chromium by weight.
Claim 6
Dependent Claim
27 words
The process of claim 1, including adding molybdenum-containing ions to said solution, and said codepositing comprising codepositing cobalt, chromium and molybdenum on said cathode as the substrate.
Claim 7
Dependent Claim
33 words
The process of claim 4, including employing an amount of said ethylenediaminetetraacetic acid sufficient to provide a codeposited alloy of cobalt, chromium and molybdenum, containing about 12 to about 33% chromium by weight.
Claim 8
Dependent Claim
38 words
The process of claim 5, the amount of cobalt, chromium and molybdenum containing ions in said solution being sufficient to provide a codeposited alloy consisting of about 65% cobalt, about 30% chromium and about 5% molybdenum, by weight.
Claim 9
Dependent Claim
22 words
The process of claim 1, said electrolyzing taking place at a current density of about 25 to about 50 mA/cm 2 .
Claim 10
Dependent Claim
22 words
The process of claim 1, said cobalt and trivalent chromium ions being provided by soluble chromium (III) and soluble cobalt (II) salts.
Claim 11
Dependent Claim
25 words
The process of claim 4, said cobalt, trivalent chromium and molybdenum ions being provided by soluble chromium (III), soluble cobalt (II) and soluble molybdate salts.
Claim 12
Dependent Claim
15 words
The process of claim 9, said salts being chromium chloride, cobalt chloride and ammonium molybdate.
Claim 13
Dependent Claim
38 words
The process of claim 1, employing about 0.14 to about 1.4 grams cobalt (II) ions, about 11.0 to about 25.0 grams trivalent chromium ions, and about 0.35 to about 3.5 grams ethylenediaminetetraacetic acid, per liter of said solution.
Claim 14
Dependent Claim
46 words
The process of claim 4, employing about 0.14 to about 1.4 grams cobalt (II) ions, about 11.0 to about 25.0 grams trivalent chromium ions, about 0.13 to about 0.25 grams molybdenum-containing ions, and about 0.35 to about 3.5 grams ethylenediaminetetraacetic acid, per liter of said solution.
Claim 15
Dependent Claim
38 words
The process of claim 4, and including adding a calcium phosphate ceramic to said solution and said codepositing comprising codepositing said calcium phosphate and an alloy of said cobalt, chromium and molybdenum on said cathode as the substrate.
Claim 16
Dependent Claim
12 words
The process of claim 13, wherein said calcium phosphate ceramic is hydroxyapatite.
Claim 17
Dependent Claim
46 words
The process of claim 12, and including adding to said solution about 5 to about 60 grams of hydroxyapatite, per liter of said solution, and said codepositing comprising codepositing said hydroxylapatite and an alloy of said cobalt, chromium and molybdenum on said cathode as the substrate.
Claim 18
Dependent Claim
19 words
The process of claim 12, including initially fixing calcium phosphate ceramic to said cathode substrate by electrophoresis and sintering.
Claim 19
Dependent Claim
88 words
The process of claim 16, said electrophoresis including placing calcium phosphate ceramic particles in a nonconducting medium containing an inert anode and said substrate as cathode in an amount of about 25 gins to about 35 gms per liter, and applying about 100 volts for about 60 seconds to weakly attach said calcium phosphate ceramic to said substrate, said sintering comprising heat treating said substrate with weakly attached calcium phosphate ceramic at about 600° C. for about 4 hours to hold the calcium phosphate ceramic to the substrate.
Claim 20
Dependent Claim
11 words
The process of claim 16, said calcium phosphate ceramic being hydroxyapatite.
Claim 21
Dependent Claim
11 words
The process of claim 17, said calcium phosphate ceramic being hydroxyapatite.
Claim 22
Dependent Claim
56 words
An electrolyte solution for simultaneous electrodeposition of at least a two component alloy system of cobalt and chromium on a substrate consisting essentially of about 0.14 to about 1.4 grams cobalt (II) ions, about 11.0 to about 25.0 grams trivalent chromium ions, and about 0.35 to about 3.5 grams ethylenediaminetetraacetic acid, per liter of said solution.
Claim 23
Dependent Claim
56 words
An electrolyte solution for simultaneous electrodeposition of at least a two component alloy system of cobalt and chromium on a substrate consisting essentially of about 0.14 to about 1.4 grams cobalt (II) ions, about 11.0 to about 25.0 grams trivalent chromium ions, and about 0.35 to about 3.5 grams ethylenediaminetetraacetic acid, per liter of said solution.
Claim 24
Dependent Claim
47 words
The electrolyte solution of claim 20, said electrolyte solution also containing about 0.13 to about 0.25 grams molybdenum-containing ions per liter of said solution, capable of forming a codeposited alloy of cobalt, chromium and molybdenum, containing about 12 to about 33% chromium by weight on said substrate.
Claim 25
Dependent Claim
43 words
The electrolyte solution of claim 21, said electrolyte solution also containing about 5 to about 60 grams of hydroxyapatite per liter of said solution, capable of forming a codeposit of hydroxyapatite and an alloy of said cobalt, chromium and molybdenum on said substrate.
Claim 26
Dependent Claim
12 words
The process of claim 1, including adding formic acid to said solution.
Claim 27
Dependent Claim
25 words
The process of claim 12, including adding 60 ml of formic acid and 15 grams of potassium bromide per liter of solution, to said solution.
References Cited (Backward Citations)
US2377229A
Cited
US2516227A
Cited
US2927066A
Cited
US3966564A
Cited
US4196063A
Cited
US4422920A
Cited
US4610763A
Cited
US4673471A
Cited
US4990163A
Cited
US5205921A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-08-15 | 1998-02-14 | 1998-08-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-08-15 | 2002-02-14 | 2002-08-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-08-15 | 2006-02-14 | 2006-08-16 | $7700.00 | Window Closed / Lapsed |