Stress-softened elastomeric films, articles, and method and apparatus for making such films and articles
Assignee: Family Health International 360
•
Filing: 1991-10-11
•
Granted: 1994-08-09
•
Expires: 2011-10-11
Abstract
Abstract A stress-softened thermoplastic elastomeric (TPE) film which has been subjected to tensional deformation comprising at least uniaxial strain, and having improved textural and thermal transmissivity characteristics, as compared to a native, unstretched material. Such stress-softened thermoplastic elastomeric film may be employed in a wide variety of articles, including condoms, finger cots, tubular bandages, and the like. Condoms comprising such stress-softened TPE film are described, including condoms having a main sheath comprising stress-softened and non-stress-softened areas in a pattern or other predetermined arrangement. A variety of methods and apparatus for forming stress-softened tubular articles of thermoplastic elastomeric film is disclosed.
Inventors
- 👤 Robert G. Wheeler, deceased
- 👤 William D. Hawley
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 11:24
CPC Classifications
A; A61; A61L; A61L31/00; A61L31/14; A61F; A61F6/00; A61F6/02; A61F6/04; A61L31/04; A61L31/048; B; B29; B29C; B29C49/00; B29C49/42; B29C49/44; B29C53/00; B29C53/32; B29C55/00; B29C55/22; B29C55/26; B29C65/00; B29C65/02; B29C65/18; B29C65/22; B29C65/221; B29C65/222; B29C65/74; B29C65/743; B29C65/7441; B29C66/00; B29C66/70; B29C66/71; B29C66/80; B29C66/81; B29C66/818; B29C66/8182; B29C66/81821; B29C67/00; B29C67/0014; B29C67/0018; B29C43/00; B29C43/02; B29C43/10; B29C43/12; B29C66/73; B29C66/731; B29C66/7315; B29C66/73151; B29K; B29K2995/00; B29K2995/0037; B29K2995/007; B29L; B29L2031/00; B29L2031/48; B29L2031/4842; B29L2031/4864; B29L2031/753; B29L2031/7538; Y; Y10; Y10S; Y10S128/00; Y10S128/917; Y10S128/918
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
89 words
A stress-softened thermoplastic elastomeric film, having at least one of the following characteristics: (i) a shear stiffness value of less than 2.5 gf/cm degree; (ii) a tensile energy value of at least 1.0 gf/cm/cm 2 ; (iii) an extensibility at 50 gf/cm load of at least 4.0%; (iv) a dry heat loss value of at least 16.5 watts/m 2 /° C.; (v) a wet heat loss value of at least 22.0 watts/m 2 /° C.; and (vi) a Q max value of less than 12.25 watts/m 2 /° C.
Claim 2
Dependent Claim
89 words
A stress-softened thermoplastic elastomeric film, having at least one of the following characteristics: (i) a shear stiffness value of less than 2.5 gf/cm degree; (ii) a tensile energy value of at least 1.0 gf/cm/cm 2 ; (iii) an extensibility at 50 gf/cm load of at least 4.0%; (iv) a dry heat loss value of at least 16.5 watts/m 2 /° C.; (v) a wet heat loss value of at least 22.0 watts/m 2 /° C.; and (vi) a Q max value of less than 12.25 watts/m 2 /° C.
Claim 3
Dependent Claim
107 words
A stress-softened thermoplastic elastomeric film according to claim 1, characterized by at least one of the following characteristics: (i) a film thickness of less than 100 micrometers which has been reduced in thickness by at least 10% from its original film thickness by tensional stretching of the film; (ii) an elastic modulus at 20% elongation which is at least 15% lower than the elastic modulus at 20% elongation of a corresponding film of the aforementioned original film thickness, which has not been subjected to such tensional stretching, denoted hereinafter as "native film"; and (iii) a break ratio defined by ##EQU4## which is less than 0.9 in value.
Claim 4
Dependent Claim
33 words
A stress-softened thermoplastic elastomeric film according to claim 2, wherein the relatively harder segments of the polymer are selected from the group consisting of urethane linkages, (meth)acrylate ester moieties, and vinyl arylene groups.
Claim 5
Dependent Claim
37 words
A stress-softened thermoplastic elastomeric film according to claim 1, wherein the film is formed of a polymer comprising (i) hydrocarbonaceous chain moieties constituting relatively softer segments of the polymer, and (ii) relatively harder segments of the polymer.
Claim 6
Dependent Claim
31 words
A stress-softened thermoplastic elastomeric film according to claim 4, wherein the hydrocarbonaceous chain moieties are derived from polymerizable monomers or precursors, selected from the group consisting of monoolefins, dienes, and polyenes.
Claim 7
Dependent Claim
27 words
A stress-softened thermoplastic elastomeric film according to claim 5, wherein the hydrocarbonaceous chain moieties are selected from the group consisting of ethylene, propylene, butylene, butadiene, and isoprene.
Claim 8
Dependent Claim
31 words
A stress-softened thermoplastic elastomeric film according to claim 1, wherein the film is formed of a material selected from the group consisting of polyether-based polyurethanes, polyester-based polyurethanes, and multiblock rubber-based copolymers.
Claim 9
Dependent Claim
18 words
A stress-softened thermoplastic elastomeric film according to claim 1, wherein the film is formed of a polyether-based polyurethane.
Claim 10
Dependent Claim
18 words
A stress-softened thermoplastic elastomeric film according to claim 1, wherein the film is formed of a polyester-based polyurethane.
Claim 11
Dependent Claim
31 words
A stress-softened thermoplastic elastomeric film according to claim 1, wherein the film is formed of a multiblock rubber-based copolymer having an A-B-A structure comprising polystyrene end blocks and an elastomeric midblock.
Claim 12
Dependent Claim
47 words
A stress-softened thermoplastic elastomeric film according to claim 1, which is of tubular shape having a closed distal end and an open proximal end, and which has been stress-softened by biaxial stretching comprising longitudinal extension thereof under the application of tensional force, concurrently with radial expansion thereof.
Claim 13
Dependent Claim
13 words
A film article comprising a stress-softened thermoplastic elastomeric film according to claim 1.
Claim 14
Dependent Claim
128 words
A method of stress-softening a thermoplastic elastomeric film comprising tensionally stretching the film by applying thereto a strain which is at least uniaxial in orientation to reduce the thickness of the film by at least 10%, wherein the original thickness of the film is less than 100 micrometers, and such that the film subsequent to such tensional stretching is characterized by: (i) an elastic modulus at 20% elongation which is at least 15% lower than the elastic modulus at 20% elongation of a corresponding film of the same thickness which has not been subjected to the tensional stretching ("native film"); and (ii) at least one of the shear stiffness, tensile energy, extensibility, dry heat loss, wet heat loss, and Q max values, as numerically specified in claim 1.
Claim 15
Dependent Claim
88 words
A stress-softened thermoplastic elastomeric film, having at least one of the following characteristics: (i) a shear stiffness value of from 0.5 to 2.5 gf/cm degree; (ii) a tensile energy value of from 1 to 3 gf/cm/cm 2 ; (iii) an extensibility at 50 gf/cm load of 4-12%; (iv) a dry heat loss value of 16.5 to 20.0 watts/m 2 /° C.; (v) a wet heat loss value of 22 to 25 watts/m 2 /° C.; and (vi) a Q max value of from 12.25 watts/m 2 /° C.
Claim 16
Dependent Claim
88 words
A stress-softened thermoplastic elastomeric film, having at least one of the following characteristics: (i) a shear stiffness value of from 0.5 to 2.5 gf/cm degree; (ii) a tensile energy value of from 1 to 3 gf/cm/cm 2 ; (iii) an extensibility at 50 gf/cm load of 4-12%; (iv) a dry heat loss value of 16.5 to 20.0 watts/m 2 /° C.; (v) a wet heat loss value of 22 to 25 watts/m 2 /° C.; and (vi) a Q max value of from 12.25 watts/m 2 /° C.
References Cited (Backward Citations)
US1113561A
Cited
US2410460A
Cited
US2285981A
Cited
US2433538A
Cited
US2488938A
Cited
US2484356A
Cited
US2586674A
Cited
US2577345A
Cited
US3037508A
Cited
US3157724A
Cited
US3149017A
Cited
US3295145A
Cited
US3247857A
Cited
US3559651A
Cited
US3588997A
Cited
US3631857A
Cited
US3627579A
Cited
US4031214A
Cited
FR2085323A1
Cited
DE2020280A1
Cited
US3733383A
Cited
US3759254A
Cited
DE2349361A1
Cited
JPS577050B2
Cited
US4009717A
Cited
US4022213A
Cited
US3992766A
Cited
US4275812A
Cited
US4004591A
Cited
US4241828A
Cited
GB1595711A
Cited
US4576156A
Cited
USD253009S
Cited
US4232675A
Cited
US4446860A
Cited
US4354494A
Cited
US4626250A
Cited
US5096896A
Cited
US4475910A
Cited
US4795425A
Cited
US4484918A
Cited
US4432357A
Cited
USRE32983E
Cited
EP0147072A1
Cited
US4603174A
Cited
US4546029A
Cited
US4794929A
Cited
US4735621A
Cited
US4867937A
Cited
US4833172A
Cited
US4781709A
Cited
US4798600A
Cited
US4805604A
Cited
US4955392A
Cited
US4855169A
Cited
US4964416A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-08-08 | 1998-02-07 | 1998-08-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-08-08 | 2002-02-07 | 2002-08-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-08-08 | 2006-02-07 | 2006-08-09 | $7700.00 | Window Closed / Lapsed |