High resolution, multi-layer resist for microlithography and method therefor
Assignee: Arizona's Public Universities
•
Filing: 1992-06-08
•
Granted: 1994-05-24
•
Expires: 2012-06-08
Abstract
Abstract A high resolution, multi-layer resist for use in microlithography and a method is disclosed. The resist consists of a planarized layer deposited onto a substrate and an active layer, consisting of arsenic sulfide and silver is deposited onto the planarized layer. Irradiation with light, or other source of irradiation causes the silver to ionically diffuse into the arsenic sulfide, thereby creating a non-phase separate ternary chalcogenide glass. Removal of either the reacted or unreacted ternary compound will provide a positive or negative mask which may be used in subsequent processing or left as an intermetal dielectric as part of the underlying circuitry.
Inventors
- 👤 Michael N. Kozicki
- 👤 Shao-Wen Hsia
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 16:23
CPC Classifications
G; G03; G03F; G03F7/00; G03F7/004; G03F7/0042; G03F7/0044; G03F7/09; G03F7/094
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
159 words
A method for forming a multi-layer resist material for microlithography, comprising the steps of: depositing a planarized layer onto a substrate, depositing an active layer onto the surface of the planarized layer, said active layer comprising a layer of arsenic sulfide and a layer of silver metal, said layer of arsenic sulfide consisting essentially of about 28-37 at % As and about 63-72 at % S; exposing said active layer to radiation, thereby doping exposed portions of said silver layer into said arsenic sulfide layer and forming an silver-doped arsenic sulfide region, removing unexposed silver from said arsenic sulfide layer, etching one of said arsenic sulfide layer or said silver-doped arsenic sulfide region, etching said planarized layer underlying said etched arsenic sulfide or said silver-doped arsenic sulfide region, at least one of stripping said arsenic sulfide silver doped area or etching said silver-doped arsenic sulfide region, thereby forming a resist pattern capable of better than one-half micron resolution microlithography.
Claim 2
Independent Claim
159 words
A method for forming a multi-layer resist material for microlithography, comprising the steps of: depositing a planarized layer onto a substrate, depositing an active layer onto the surface of the planarized layer, said active layer comprising a layer of arsenic sulfide and a layer of silver metal, said layer of arsenic sulfide consisting essentially of about 28-37 at % As and about 63-72 at % S; exposing said active layer to radiation, thereby doping exposed portions of said silver layer into said arsenic sulfide layer and forming an silver-doped arsenic sulfide region, removing unexposed silver from said arsenic sulfide layer, etching one of said arsenic sulfide layer or said silver-doped arsenic sulfide region, etching said planarized layer underlying said etched arsenic sulfide or said silver-doped arsenic sulfide region, at least one of stripping said arsenic sulfide silver doped area or etching said silver-doped arsenic sulfide region, thereby forming a resist pattern capable of better than one-half micron resolution microlithography.
Claim 3
Dependent Claim
31 words
A method for forming a multi-layer resist material for microlithography according to claim 1, wherein said planarized layer is selected from the group consisting of novalac resin, polyimide, and polymethyl methacrylate.
Claim 4
Dependent Claim
22 words
A method for forming a multi-layer resist material for microlithography according to claim 1, wherein said planarized layer is self-levelling spin-on glass.
Claim 5
Dependent Claim
31 words
A method for forming a multi-layer resist material for microlithography according to claim 1, wherein said planarized layer is deposited by one of bias quartz deposition or resist etch back deposition.
Claim 6
Dependent Claim
29 words
A method for forming a multi-layer resist material for microlithography according to claim 1, wherein said arsenic sulfide layer forms a chalcogenide glass upon doping with the silver layer.
Claim 7
Dependent Claim
29 words
A method for forming a multi-layer resist material for microlithography according to claim 1, wherein said arsenic sulfide consists of 33 at % As and 67 at % S.
Claim 8
Dependent Claim
25 words
A method for forming a multi-layer resist material for microlithography according to claim 1, wherein said active layer is less than about 200 nm thick.
Claim 9
Dependent Claim
33 words
A method for forming a multi-layer resist material for microlithography according to claim 1, wherein a thickness ratio of arsenic sulfide to Ag is in the range of about 5:1 to about 3:1.
Claim 10
Dependent Claim
33 words
A method for forming a multi-layer resist material for microlithography according to claim 1, wherein said step of exposing said active layer further comprises optical, ion beam, electron beam, x-ray or laser irradiation.
Claim 11
Dependent Claim
74 words
A method for forming a multi-layer resist material for microlithography according to claim 1, further comprising the steps of exposing the active layer to irradiation, thereby forming a ternary compound of the arsenic sulfide and silver; and removing unreacted silver from the surface of the irradiated active layer, etching unreacted arsenic sulfide by reactive ion etching, and removing portions of the planarized layer by etching, to form a negative image of the exposed area.
Claim 12
Dependent Claim
31 words
A method for forming a multi-layer resist material for microlithography according to claim 10, in which said unreacted arsenic sulfide is etched by reactive ion etching in a CF 4 plasma.
Claim 13
Dependent Claim
59 words
A method for forming a multi-layer resist material for microlithography according to claim 1, further comprising the steps of exposing the active layer to irradiation thereby forming a ternary compound of the arsenic sulfide and silver; and etching said ternary compound and removing portions of the planarized layer by etching to form a positive image of the exposed area.
Claim 14
Dependent Claim
30 words
A method for forming a multi-layer resist material for microlithography according to claim 12 in which said ternary compound is etched by reactive ion etching in a sulfur gas plasma.
Claim 15
Dependent Claim
14 words
A multi-layer resist material for microlithography formed by the method according to claim 1.
Claim 16
Dependent Claim
14 words
A multi-layer resist material for microlithography formed by the method according to claim 2.
Claim 17
Dependent Claim
14 words
A multi-layer resist material for microlithography formed by the method according to claim 3.
Claim 18
Dependent Claim
14 words
A multi-layer resist material for microlithography formed by the method according to claim 4.
Claim 19
Dependent Claim
14 words
A multi-layer resist material for microlithography formed by the method according to claim 5.
Claim 20
Dependent Claim
14 words
A multi-layer resist material for microlithography formed by the method according to claim 6.
Claim 21
Dependent Claim
53 words
A multi-layer resist material for microlithography, comprising: a substrate; a planarized layer deposited onto said substrate; and an active layer deposited onto said planarized layer, said active layer comprising a layer of arsenic sulfide and a layer of silver, wherein said active layer forms a non-phase separated ternary compound upon exposure to irradiation.
Claim 22
Dependent Claim
53 words
A multi-layer resist material for microlithography, comprising: a substrate; a planarized layer deposited onto said substrate; and an active layer deposited onto said planarized layer, said active layer comprising a layer of arsenic sulfide and a layer of silver, wherein said active layer forms a non-phase separated ternary compound upon exposure to irradiation.
Claim 23
Dependent Claim
25 words
The multi-layer resist material according to claim 20, wherein said planarized layer is selected from the group consisting of novalac resin, polyimide, and polymethyl methacrylate.
Claim 24
Dependent Claim
17 words
The multi-layer resist material according to claim 20, wherein said planarized layer further comprises self-levelling spin-on glass.
Claim 25
Dependent Claim
15 words
The multi-layer resist according to claim 20, wherein said arsenic sulfide layer is chalcogenide glass.
Claim 26
Dependent Claim
22 words
The multi-layer resist according to claim 20, wherein said arsenic sulfide consists of 33 at % As and 67 at % S.
Claim 27
Dependent Claim
20 words
The multi-layer resist according to claim 20, wherein said active layer has a thickness of less than about 200 nm.
Claim 28
Dependent Claim
26 words
The multi-layer resist according to claim 20, wherein a thickness ratio of arsenic sulfide to silver is in the range of about 5:1 to about 3:1.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-05-23 | 1997-11-22 | 1998-05-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-05-23 | 2001-11-22 | 2002-05-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-05-23 | 2005-11-22 | 2006-05-24 | $7700.00 | Window Closed / Lapsed |