Abstract
Abstract A method of forming a SOI integrated circuit includes defining thin silicon mesas by wet etching a device layer having the <100> orientation down to the underlying insulator so that the (111) crystal planes control the lateral etching, forming a nitride bottom polish stop in the bottom of the apertures by a low temperature CVD process, with nitride sidewalls on the (111) planes of the silicon mesas being susceptible to easy removal, so that no hard material is present during a chemical-mechanical polishing step to thin the device layer down to less than 1000 Å, and filling the apertures with a temporary layer of polysilicon to provide mechanical support to the edges of the device layer during the polishing operation.
Inventors
- 👤 Ahmet Bindal
- 👤 James E. Currie
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 13:14
CPC Classifications
H; H10; H10P; H10P52/00; H10P52/40; H10P52/403; H10P90/00; H10P90/19; H10P90/1904; H10P90/1906; H10P90/1914; H10W; H10W10/00; H10W10/01; H10W10/061; H10W10/10; H10W10/181; H10P90/1908; H10W10/011; H10W10/014; H10W10/17; Y; Y10; Y10S; Y10S148/00; Y10S148/168; Y10S438/00; Y10S438/977
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
273 words
A method of thinning a device layer of silicon oriented with a <100> crystal orientation, having an initial device layer thickness and disposed above a buried oxide layer on a bonded SOI wafer, to form a set of final silicon mesas, comprising the steps of: depositing a protective layer on the top surface of said device layer; forming a set of apertures in said protective layer having aperture dimensions dependent on a final polish stop size; wet etching a set of polish stop apertures in said device layer down to said buried oxide using an etchant that etches the <100> direction in preference to the <111> direction, whereby said (111) crystal planes serve as a lateral etch stop and said buried oxide serves as a vertical etch stop so that said polish stop apertures have slanting sidewalls on the (111) crystal planes of said device layer and a polish stop aperture bottom on said buried oxide; depositing a polish stop layer on said polish stop aperture sidewalls and bottom, said polish stop layer having a polish stop thickness on said aperture bottom; depositing and patterning a layer of photoresist above said polish stop layer to leave a protective photoresist plug on said aperture bottom; removing said polish stop layer outside said protective plug, thereby leaving a set of polish stops having a polish stop surface between a set of thick silicon mesas having said slanting sidewalls in said polish stop apertures; and polishing said set of silicon mesas to said polish stop surface to form a set of final silicon mesas, whereby said final set of silicon mesas have said polish stop thickness.
Claim 2
Independent Claim
273 words
A method of thinning a device layer of silicon oriented with a <100> crystal orientation, having an initial device layer thickness and disposed above a buried oxide layer on a bonded SOI wafer, to form a set of final silicon mesas, comprising the steps of: depositing a protective layer on the top surface of said device layer; forming a set of apertures in said protective layer having aperture dimensions dependent on a final polish stop size; wet etching a set of polish stop apertures in said device layer down to said buried oxide using an etchant that etches the <100> direction in preference to the <111> direction, whereby said (111) crystal planes serve as a lateral etch stop and said buried oxide serves as a vertical etch stop so that said polish stop apertures have slanting sidewalls on the (111) crystal planes of said device layer and a polish stop aperture bottom on said buried oxide; depositing a polish stop layer on said polish stop aperture sidewalls and bottom, said polish stop layer having a polish stop thickness on said aperture bottom; depositing and patterning a layer of photoresist above said polish stop layer to leave a protective photoresist plug on said aperture bottom; removing said polish stop layer outside said protective plug, thereby leaving a set of polish stops having a polish stop surface between a set of thick silicon mesas having said slanting sidewalls in said polish stop apertures; and polishing said set of silicon mesas to said polish stop surface to form a set of final silicon mesas, whereby said final set of silicon mesas have said polish stop thickness.
Claim 3
Dependent Claim
92 words
A method according to claim 1, in which said step of removing said polish stop layer leaves a set of gaps on said polish stop aperture bottom between said set of polish stops and said set of thick silicon mesas; and further including a step of forming an isolating oxide coating on said slanting sidewalls and a step of depositing a layer of polycrystalline silicon to fill in said gaps between said polish stops and said thick silicon mesas, whereby edge damage on said slanting sidewalls during said polishing step is reduced.
Claim 4
Dependent Claim
33 words
A method according to claim 1, in which said polish stop layer is formed from nitride and said step of removing said polish stop layers is effected by a reactive ion etching step.
Claim 5
Dependent Claim
49 words
A method according to claim 3, in which said slanting sidewalls of said thick silicon mesas extend above said final silicon mesas, whereby said device layer is removed in two steps comprising said step of forming said set of apertures and said step of polishing said thick silicon mesas.
Claim 6
Dependent Claim
49 words
A method according to claim 1, in which said slanting sidewalls of said thick silicon mesas extend above said final silicon mesas, whereby said device layer is removed in two steps comprising said step of forming said set of apertures and said step of polishing said thick silicon mesas.
Claim 7
Dependent Claim
44 words
A method according to claim 5, in which said set of apertures are positioned and have dimensions such that at least a predetermined minimum amount of said protective layer remains above said final silicon mesas during said step of forming said set of apertures.
Claim 8
Dependent Claim
33 words
A method according to claim 2, in which said polish stop layer is formed from nitride and said step of removing said polish stop layers is effected by a reactive ion etching step.
Claim 9
Dependent Claim
49 words
A method according to claim 7, in which said slanting sidewalls of said thick silicon mesas extend above said final silicon mesas, whereby said device layer is removed in two steps comprising said step of forming said set of apertures and said step of polishing said thick silicon mesas.
Claim 10
Dependent Claim
49 words
A method according to claim 2, in which said slanting sidewalls of said thick silicon mesas extend above said final silicon mesas, whereby said device layer is removed in two steps comprising said step of forming said set of apertures and said step of polishing said thick silicon mesas.
Claim 11
Dependent Claim
44 words
A method according to claim 9, in which said set of apertures are positioned and have dimensions such that at least a predetermined minimum amount of said protective layer remains above said final silicon mesas during said step of forming said set of apertures.
References Cited (Backward Citations)
US3911562A
Cited
US4408386A
Cited
US4824795A
Cited
JPS62247540A
Cited
US4971925A
Cited
US4735679A
Cited
JPS6449240A
Cited
US5124274A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-11-15 | 1997-05-17 | 1997-11-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-11-15 | 2001-05-17 | 2001-11-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-11-15 | 2005-05-17 | 2005-11-16 | $7700.00 | Window Closed / Lapsed |