Phosphate-containing surgical cements
Assignee: Ceramedical Inc
•
Filing: 1992-02-03
•
Granted: 1993-06-08
•
Expires: 2012-02-03
Abstract
Abstract New surgical cements for use in medical applications such as orthopedic and maxillofacial surgeries and dental applications are disclosed. These surgical cements comprise a hardened cement formed from a mixture comprising a cementing component selected from the group consisting of ceramics having the formula w(RO)--x(R.sub.2 O)--y(P.sub.2 O.sub.5)--z(X) wherein RO is selected from the group consisting of CaO and mixtures of CaO and MgO, R 2 O is selected from the group consisting of alkali metal oxides and mixtures thereof, X is selected from the group consisting of SO 4 and Cl, and w, x, y and z are the mole fractions of the respective constituents in the ceramic, when X is SO 4 , w is in the range of about 0.25 to about 0.5, x is in the range of about 0.05 to about 0.4, y is in the range of about 0.05 to about 0.25 and z is in the range of about 0.01 to about 0.25, and when X is Cl, w is in the range of about 0.25 to about 0.5, x is in the range of about 0.05 to about 0.5, y is in the range of about 0.1 to about 0.25 and z is in the range of about 0.01 to about 0.4 and mixtures thereof; a setting component selected from the group consisting of polyfunctional carboxylic acids containing 2 to about 10 carbon atoms, salts thereof, monobasic phosphate salts and mixtures thereof; and water in an amount effective to form a paste from the mixture which paste hardens into the hardened cement which is biocompatible.
Inventors
- 👤 Sung-Tsuen Liu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 07:40
CPC Classifications
A; A61; A61L; A61L24/00; A61L24/02; A61K; A61K6/00; A61K6/30; A61K6/50; A61K6/54; A61K6/60; A61K6/69; A61K6/70; A61K6/71; A61K6/74; A61K6/75; A61K6/80; A61K6/802; A61K6/807; A61K6/849; A61K6/858; A61K6/876; C; C04; C04B; C04B28/00; C04B28/34; C04B2111/00; C04B2111/00474; C04B2111/00836
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
258 words
A surgical cement for use in medical applications such as orthopedic and maxillofacial surgeries and dental applications comprising a hardened cement formed from a mixture comprising a cementing component selected from the group consisting of ceramics having the formula w(RO)--x(R.sub.2 O)--y(P.sub.2 O.sub.5)--z(X) wherein RO is selected from the group consisting of CaO and mixtures of CaO and MgO, R 2 O is selected from the group consisting of alkali metal oxides and mixtures thereof, X is selected from the group consisting of SO 4 and Cl, and w, x, y and z are the mole fractions of the respective constituents in said ceramic, when X is SO 4 , w is in the range of about 0.25 to about 0.5, x is in the range of about 0.05 to about 0.4, y is in the range of about 0.05 to about 0.25 and z is in the range of about 0.01 to about 0.25, and when X is Cl, w is in the range of about 0.25 to about 0.5, x is in the range of about 0.05 to about 0.5, y is in the range of about 0.1 to about 0.25 and z is in the range of about 0.01 to about 0.4, and mixtures thereof; a setting component selected from the group consisting of polyfunctional carboxylic acids containing 2 to about 10 carbon atoms, acidic salts thereof, monobasic phosphate salts and mixtures thereof; and water in an amount effective to form a paste from said mixture which paste hardens into said hardened cement which is biocompatible.
Claim 2
Dependent Claim
258 words
A surgical cement for use in medical applications such as orthopedic and maxillofacial surgeries and dental applications comprising a hardened cement formed from a mixture comprising a cementing component selected from the group consisting of ceramics having the formula w(RO)--x(R.sub.2 O)--y(P.sub.2 O.sub.5)--z(X) wherein RO is selected from the group consisting of CaO and mixtures of CaO and MgO, R 2 O is selected from the group consisting of alkali metal oxides and mixtures thereof, X is selected from the group consisting of SO 4 and Cl, and w, x, y and z are the mole fractions of the respective constituents in said ceramic, when X is SO 4 , w is in the range of about 0.25 to about 0.5, x is in the range of about 0.05 to about 0.4, y is in the range of about 0.05 to about 0.25 and z is in the range of about 0.01 to about 0.25, and when X is Cl, w is in the range of about 0.25 to about 0.5, x is in the range of about 0.05 to about 0.5, y is in the range of about 0.1 to about 0.25 and z is in the range of about 0.01 to about 0.4, and mixtures thereof; a setting component selected from the group consisting of polyfunctional carboxylic acids containing 2 to about 10 carbon atoms, acidic salts thereof, monobasic phosphate salts and mixtures thereof; and water in an amount effective to form a paste from said mixture which paste hardens into said hardened cement which is biocompatible.
Claim 3
Dependent Claim
48 words
The surgical cement of claim 1 wherein the weight ratio of said cementing component to said setting component in said mixture is in the range of about 5:1 to about 1.5 to 1, and said mixture hardens in about 30 minutes or less after said paste is formed.
Claim 4
Dependent Claim
26 words
The surgical cement of claim 1 wherein R 2 O is selected from the group consisting of Na 2 O, K 2 O and mixtures thereof.
Claim 5
Dependent Claim
35 words
The surgical cement of claim 1 wherein X is SO 4 , x is in the range of about 0.12 to about 0.38, and y is in the range of about 0.12 to about 0.25.
Claim 6
Dependent Claim
29 words
The surgical cement of claim 1 wherein said setting component is selected from the group consisting of citric acid, citrates, tartaric acid, tartrates monobasic phosphate salts and mixtures thereof.
Claim 7
Dependent Claim
29 words
The surgical cement of claim 1 wherein said setting component is selected from the group consisting of Ca(H 2 PO 4 ) 2 , hydrates thereof and mixtures thereof.
Claim 8
Dependent Claim
13 words
The surgical cement of claim 1 wherein said setting component is tartaric acid.
Claim 9
Dependent Claim
42 words
The surgical cement of claim 1 wherein said mixture further comprises a setting rate modifier component in an amount effective to modify the rate at which said mixture is hardened relative to a substantially identical mixture without said setting rate modifier component.
Claim 10
Dependent Claim
35 words
The surgical cement of claim 8 wherein said setting rate modifier component is other than said setting component and is selected from the group consisting of citric acid, malic acid, citrates, malates and mixtures thereof
Claim 11
Dependent Claim
40 words
The surgical cement of claim 1 wherein said mixture further comprises a biocompatible filler component wherein the amount of filler component is such that the weight ratio of said filler component to said cementing component is about 4:1 or less.
Claim 12
Dependent Claim
170 words
A surgical cement for use in medical applications such as orthopedic and maxillofacial surgeries and dental applications comprising a hardened cement formed from a mixture comprising a cementing component selected from the group consisting of ceramics having the formula w(RO)--x(R.sub.2 O)--y(P.sub.2 O.sub.5) wherein RO is selected from the group consisting of CaO and mixtures of CaO and MgO, R 2 O is selected from the group consisting of alkali metal oxides and mixtures thereof, and w, x, y and z are the mole fractions of the respective constituents in said ceramic wherein w is in the range of about 0.2 to about 0.85, x is in the range of about 0.05 to about 0.6, and y is in the range of about 0.05 to about 0.3, and mixtures thereof; a setting component selected from the group consisting of tartaric acid, tartrates, monobasic phosphate salts and mixtures thereof; and water in an amount effective to form a paste from said mixture which paste hardens into said hardened cement which is biocompatible.
Claim 13
Dependent Claim
170 words
A surgical cement for use in medical applications such as orthopedic and maxillofacial surgeries and dental applications comprising a hardened cement formed from a mixture comprising a cementing component selected from the group consisting of ceramics having the formula w(RO)--x(R.sub.2 O)--y(P.sub.2 O.sub.5) wherein RO is selected from the group consisting of CaO and mixtures of CaO and MgO, R 2 O is selected from the group consisting of alkali metal oxides and mixtures thereof, and w, x, y and z are the mole fractions of the respective constituents in said ceramic wherein w is in the range of about 0.2 to about 0.85, x is in the range of about 0.05 to about 0.6, and y is in the range of about 0.05 to about 0.3, and mixtures thereof; a setting component selected from the group consisting of tartaric acid, tartrates, monobasic phosphate salts and mixtures thereof; and water in an amount effective to form a paste from said mixture which paste hardens into said hardened cement which is biocompatible.
Claim 14
Dependent Claim
48 words
The surgical cement of claim 11 wherein the weight ratio of said cementing component to said setting component in said mixture is in the range of about 5:1 to about 1.5 to 1, and said mixture hardens in about 30 minutes or less after said paste is formed.
Claim 15
Dependent Claim
26 words
The surgical cement of claim 11 wherein R 2 O is selected from the group consisting of Na 2 O, K 2 O and mixtures thereof.
Claim 16
Dependent Claim
10 words
The surgical cement of claim 11 wherein RO is CaO.
Claim 17
Dependent Claim
31 words
The surgical cement of claim 1 wherein said setting component is selected from the group consisting of tartaric acid, Ca(H 2 PO 4 ) 2 , hydrates thereof and mixtures thereof.
Claim 18
Dependent Claim
42 words
The surgical cement of claim 11 wherein said mixture further comprises a setting rate modifier component in an amount effective to modify the rate at which said mixture is hardened relative to a substantially identical mixture without said setting rate modifier component.
Claim 19
Dependent Claim
28 words
The surgical cement of claim 16 wherein said setting rate modifier component is selected from the group consisting of citric acid, malic acid, citrates, malates and mixtures thereof.
Claim 20
Dependent Claim
40 words
The surgical cement of claim 11 wherein said mixture further comprises a biocompatible filler component wherein the amount of filler component is such that the weight ratio of said filler component to said cementing component is about 4:1 or less.
Claim 21
Dependent Claim
190 words
A composition for use in medical applications such as orthopedic and maxillofacial surgeries and dental applications comprising ceramic having the following formula w(RO)--x(R.sub.2 O)--y(P.sub.2 O.sub.5)--z(X) wherein RO is selected from the group consisting of CaO and mixtures of CaO and MgO, R 2 O is selected from the group consisting of alkali metal oxides and mixtures thereof, X is selected from the group consisting of SO 4 and Cl, and w, x, y and z are the mole fractions of the respective constituents in said ceramic, when X is SO 4 , w is in the range of about 0.25 to about 0.5, x is in the range of about 0.05 to about 0.4, y is in the range of about 0.05 to about 0.25 and z is in the range of about 0.01 to about 0.25; and when X is Cl, w is in the range of about 0.25 to about 0.5, x is in the range of about 0.05 to about 0.5, y is in the range of about 0.1 to about 0.25 and z is in the range of about 0.01 to about 0.4, and mixtures thereof.
Claim 22
Dependent Claim
190 words
A composition for use in medical applications such as orthopedic and maxillofacial surgeries and dental applications comprising ceramic having the following formula w(RO)--x(R.sub.2 O)--y(P.sub.2 O.sub.5)--z(X) wherein RO is selected from the group consisting of CaO and mixtures of CaO and MgO, R 2 O is selected from the group consisting of alkali metal oxides and mixtures thereof, X is selected from the group consisting of SO 4 and Cl, and w, x, y and z are the mole fractions of the respective constituents in said ceramic, when X is SO 4 , w is in the range of about 0.25 to about 0.5, x is in the range of about 0.05 to about 0.4, y is in the range of about 0.05 to about 0.25 and z is in the range of about 0.01 to about 0.25; and when X is Cl, w is in the range of about 0.25 to about 0.5, x is in the range of about 0.05 to about 0.5, y is in the range of about 0.1 to about 0.25 and z is in the range of about 0.01 to about 0.4, and mixtures thereof.
Claim 23
Dependent Claim
33 words
The composition of claim 19 wherein X is SO 4 , x in the range of about 0.12 to about 0.38, and y is in the range of about 0.12 to about 0.25.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-06-07 | 1996-12-07 | 1997-06-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-06-07 | 2000-12-07 | 2001-06-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-06-07 | 2004-12-07 | 2005-06-08 | $7700.00 | Window Closed / Lapsed |