Biocompatible polyurethane
Assignee: Membrana GmbH
•
Filing: 1990-02-13
•
Granted: 1992-04-28
•
Expires: 2010-02-13
Abstract
Abstract A process is disclosed for the production of bio-compatible polyurethane, proceeding from cyclo aliphatic diisocyanate and macrodiol, which are reacted into a pre-adduct that is then chain lengthened with a mixture of the lower-molecular diol and a macrodiol. The so-obtained polyurethane displays high resistance in human and animal bodies and is suitable for the manufacture of catheters, blood pumps, heart valves, as well as bio-compatible lacquers and coatings.
Inventors
- 👤 Gerhard Wick
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 16:56
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/40; C08G18/42; C08G18/44; A; A61; A61L; A61L33/00; A61L33/06; A61L33/068; C08G18/08; C08G18/10; A61F; A61F2/00; A61F2/02; A61F2/24
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
83 words
Process for production of biocompatible polyurethane, comprising the steps of: a. reacting cycloaliphatic diisocyanate and an aliphatic or cycloaliphatic polycarbonate polymer, using molar excess of diisocyanate, to form a pre-adduct having NCO groups, said reacting being performed in the absence of solvent, and b. chain lengthening said pre-adduct with a chain lengthening mixture of low molecular aliphatic or cycloaliphatic diol having from 2 to 8 carbon atoms and another aliphatic or cycloaliphatic polycarbonate polymer to form said polyurethane, said mixture having OH groups.
Claim 2
Dependent Claim
83 words
Process for production of biocompatible polyurethane, comprising the steps of: a. reacting cycloaliphatic diisocyanate and an aliphatic or cycloaliphatic polycarbonate polymer, using molar excess of diisocyanate, to form a pre-adduct having NCO groups, said reacting being performed in the absence of solvent, and b. chain lengthening said pre-adduct with a chain lengthening mixture of low molecular aliphatic or cycloaliphatic diol having from 2 to 8 carbon atoms and another aliphatic or cycloaliphatic polycarbonate polymer to form said polyurethane, said mixture having OH groups.
Claim 3
Dependent Claim
25 words
The process according to claim 1, wherein said reacting to form said pre-adduct is performed with 3 to 22 Mol diisocyanate per Mol polycarbonate polymer.
Claim 4
Dependent Claim
28 words
The process according to claim 1, wherein the molar ratio of the NCO-groups of said pre-adduct to the OH-groups of said chain-lengthening mixture is from 1.15:1 to 1.01:1.
Claim 5
Dependent Claim
25 words
The process according to claim 1, wherein said reacting to form said pre-adduct is performed with 6.5 to 8 Mol diisocyanate per Mol polycarbonate polymer.
Claim 6
Dependent Claim
28 words
The process according to claim 1, wherein the molar ratio of the NCO-groups of said pre-adduct to the OH-groups of said chain-lengthening mixture is from 1.07:1 to 1.04:1.
Claim 7
Dependent Claim
34 words
The process according to claim 1, wherein said reacting to form said pre-adduct is effected with polyhexamethylenecarbonate as said polycarbonate polymer and said chain-lengthening is effected with butanediol-(1,4) as said low molecular aliphatic diol.
Claim 8
Dependent Claim
13 words
The process according to claim 1, wherein said cycloaliphatic diisocyanate is 4,4'-dicyclohexylmethane diisocyanate.
Claim 9
Dependent Claim
13 words
The process according to claim 1, wherein said cycloaliphatic diisocyanate is cyclohexane diisocyanate-(1,4).
Claim 10
Dependent Claim
19 words
The process according to claim 1, wherein said cycloaliphatic diisocyanate is a mixture of 4,4'-dicyclohexylmethane diisocyanate and cyclohexane diisocyanate.
Claim 11
Dependent Claim
24 words
The process according to claim 1, wherein said pre-adduct and said chain-lengthening mixture are provided in a weight ratio of from 30:70 to 70:30.
Claim 12
Dependent Claim
24 words
The process according to claim 1, wherein said pre-adduct and said chain-lengthening mixture are provided in a weight ratio of from 60:40 to 40:60.
Claim 13
Dependent Claim
32 words
The process according to claim 1, wherein said chain-lengthening is performed in solution and further comprising adjusting a viscosity of the polyurethane produced as final product to from 0.2 to 7.5 Pa's.
Claim 14
Dependent Claim
35 words
The process according to claim 1, wherein said chain-lengthening is performed in solution, employing an organic solvent selected from the group consisting of methylene chloride, acetone, chloroform, trichloroethylene, tetrahydrofuran, dioxan, n-propanol, cyclohexanol, dimethylformamide and dimethylacetamide.
Claim 15
Dependent Claim
28 words
The process according to claim 1, wherein said chain-lengthening is performed in solution; and further comprising allowing said polyurethane to separate out by means of precipitation in water.
Claim 16
Dependent Claim
34 words
The process according to claim 1, further comprising forming a solution of said pre-adduct and said chain lengthening mixture of a certain viscosity and adding additional solvent to said solution to change said viscosity.
Claim 17
Dependent Claim
31 words
The process according to claim 1, in which said polycarbonate polymer used to make said pre-adduct is the same as said other polycarbonate polymer used in said step of said chain-lengthening.
Claim 18
Dependent Claim
13 words
The process according to claim 16, in which said polycarbonate polymer comprises polyhexamethylenecarbonate.
Claim 19
Dependent Claim
92 words
Process for production of biocompatible polyurethane, comprising: a. reacting cycloaliphatic diisocyanate and an aliphatic or cycloaliphatic polycarbonate polymer, using excess of diisocyanate, to form a pre-adduct, said reacting being performed in the absence of solvent, and, b. chain-lengthening said pre-adduct with a mixture of low molecular weight aliphatic or cycloaliphatic diol having from 2 to 8 carbon atoms and another aliphatic or cycloaliphatic polycarbonate polymer, with molar excess of said diisocynate to said polycarbonate polymer, said pre-adduct employed in a molar ratio excess of NCO-groups to OH-groups of said chain lengthening mixture.
Claim 20
Dependent Claim
92 words
Process for production of biocompatible polyurethane, comprising: a. reacting cycloaliphatic diisocyanate and an aliphatic or cycloaliphatic polycarbonate polymer, using excess of diisocyanate, to form a pre-adduct, said reacting being performed in the absence of solvent, and, b. chain-lengthening said pre-adduct with a mixture of low molecular weight aliphatic or cycloaliphatic diol having from 2 to 8 carbon atoms and another aliphatic or cycloaliphatic polycarbonate polymer, with molar excess of said diisocynate to said polycarbonate polymer, said pre-adduct employed in a molar ratio excess of NCO-groups to OH-groups of said chain lengthening mixture.
References Cited (Backward Citations)
US3544524A
Cited
US3870683A
Cited
US3764457A
Cited
US4113705A
Cited
US4476293A
Cited
US4637909A
Cited
US4816529A
Cited
US4861909A
Cited
US5001208A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-04-28 | 1995-10-28 | 1996-04-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-04-28 | 1999-10-28 | 2000-04-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-04-28 | 2003-10-28 | 2004-04-28 | $7700.00 | Window Closed / Lapsed |