Method for producing liquid transfer articles
Assignee: Praxair ST Technology Inc
•
Filing: 1989-05-31
•
Granted: 1991-09-10
•
Expires: 2009-05-31
Abstract
Abstract The invention relates to a method for producing a liquid transfer article for use in transferring the liquid to another surface comprising the steps of: (a) coating an article with at least one layer of a coating material selected from the group consisting of ceramic and metallic carbides; (b) superimposing over the coated surface a removable mask material of discontinuous material opaque to a beam of radiation of a selected energy level; (c) directing a laser having a beam of radiation of said selected energy level onto the coated surface of the article so as to produce in the area of the coated surface not covered by the discontinuous material a pattern of wells adapted for receiving liquid and wherein said pattern of wells is defined by the area of the coated surface which is not covered by the discontinuous material; and (d) removing the mask material from the coated article.
Inventors
- 👤 Pierre Luthi
- 👤 Christian Hidber
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 06:58
CPC Classifications
B; B41; B41N; B41N1/00; B41N1/006; B41C; B41C1/00; B41C1/02; B41C1/04; B41C1/05; B41N7/00; B41N7/06; B41N2207/00; B41N2207/02; B41N2207/10
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
147 words
A method for producing a liquid transfer article for use in transferring a liquid to another surface comprising the steps of: (a) coating an article with at least one layer of a coating material selected from the group consisting of refractory oxides and metallic carbides; (b) patterning over the coated surface a removable mask material which is opaque to a laser beam comprising pulses of radiation of a selected energy level; (c) directing said laser beam of uniform pulses of radiation with each pulse of radiation being from 0.0001 to 0.4 joule for a duration of 10 to 300 microseconds, onto the surface of the article so that the plurality of pulses of radiation produce in the area of the coated surface not covered by the mask material a pattern of uniform wells adapted for receiving liquid; and (d) removing the mask material from the coated article.
Claim 2
Independent Claim
147 words
A method for producing a liquid transfer article for use in transferring a liquid to another surface comprising the steps of: (a) coating an article with at least one layer of a coating material selected from the group consisting of refractory oxides and metallic carbides; (b) patterning over the coated surface a removable mask material which is opaque to a laser beam comprising pulses of radiation of a selected energy level; (c) directing said laser beam of uniform pulses of radiation with each pulse of radiation being from 0.0001 to 0.4 joule for a duration of 10 to 300 microseconds, onto the surface of the article so that the plurality of pulses of radiation produce in the area of the coated surface not covered by the mask material a pattern of uniform wells adapted for receiving liquid; and (d) removing the mask material from the coated article.
Claim 3
Dependent Claim
31 words
The method of claim 1 wherein after step (a) the following step is added: (a') treating the coated surface to obtain a roughness of less than 20 micro-inches R a .
Claim 4
Dependent Claim
22 words
The method of claim 1 wherein after step (a) the following step is added: (a') sealing the coated surface with a sealant.
Claim 5
Dependent Claim
80 words
The method of claim 1 wherein said removable mask material in step (b) is composed of a two-layer film having a first layer substantially transparent to the beam of radiation of the selected energy level and disposed on said first layer a second layer of discontinuous material opaque to the beam of radiation of said selected energy level thereby producing a pattern in the first layer defined as the area of the first layer not covered by the second layer.
Claim 6
Dependent Claim
19 words
The method of claim 1 wherein said removable mask material is deposited onto the surface of the coated article.
Claim 7
Dependent Claim
31 words
The method of claim 3 wherein after step (a') the following step is added: (a") treating the coated surface to obtain a roughness of less than 20 micro-inches R a .
Claim 8
Dependent Claim
39 words
The method of claim 1, 2, 4, 5 or 6, wherein after step (d) the following step is added: (e) smoothing the surface of the laser treated article to a roughness of about 6 micro-inches R a or less.
Claim 9
Dependent Claim
38 words
The method of claim 4 wherein in step (b) the first layer is substantially transparent to the beam of radiation of at least 0.0001 to 0.4 joules and the second layer is opaque to said beam of radiation.
Claim 10
Dependent Claim
16 words
The method of claim 4 wherein in step (b) the first layer is a polyester film.
Claim 11
Dependent Claim
23 words
The method of claim 4 wherein in step (b) the second layer is selected from the group consisting of copper, nickel and gold.
Claim 12
Dependent Claim
22 words
The method of claim 4 wherein in step (b) the first layer is a polyester film and the second layer is copper.
Claim 13
Dependent Claim
24 words
The method of claim 5 wherein in step (b) the removable mask material is selected from the group consisting of copper, nickel and gold.
Claim 14
Dependent Claim
15 words
The method of claim 12 wherein in step (b) the removable mask material is copper.
Claim 15
Dependent Claim
19 words
The method of claim 1, 2, 4, 5 or 6 wherein the liquid transfer article is a gravure roll.
Claim 16
Dependent Claim
50 words
The method of claim 14 wherein the gravure roll comprises a substrate made of a material selected from the group consisting of aluminum and steel and wherein said gravure roll is coated with a material selected from the group consisting of chromium oxide, aluminum oxide, silicon oxide and mixtures thereof.
Claim 17
Dependent Claim
17 words
The method of claim 15 wherein the substrate is steel coated with a layer of chromium oxide.
Claim 18
Dependent Claim
34 words
The method of claim 1, 2 4, 5 or 6 wherein in step (c) the wells are from 10 microns to 300 microns in diameter and from 2 microns to 250 microns in depth.
References Cited (Backward Citations)
US3645744A
Cited
US3726685A
Cited
US4108659A
Cited
US4062686A
Cited
GB2049102A
Cited
US4566938A
Cited
US4379818A
Cited
US4504354A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-09-09 | 1995-03-11 | 1995-09-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-09-09 | 1999-03-11 | 1999-09-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-09-09 | 2003-03-11 | 2003-09-10 | $7700.00 | Window Closed / Lapsed |