Colored hydrogel objects and their production-containing a water-insoluble opaquing agent
Assignee: Igel International Ltd
•
Filing: 1989-04-26
•
Granted: 1991-01-01
•
Expires: 2009-04-26
Abstract
Abstract Shaped organic polymer hydrogels, especially contact lenses, are provided with opaque or translucent coloring so as to be capable of masking effectively any underlying color, e.g. the natural color of the eye. The hydrogel may be rendered opaque by precipitation in situ of a white or yellow water-insoluble, inorganic or organic material e.g. barium sulphate or an optical brightener and then colored with a suitable dyestuff.
Inventors
- 👤 Nicholas M. Da Costa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 08:16
CPC Classifications
G; G02; G02B; G02B1/00; G02B1/04; G02B1/041; G02B1/043; B; B29; B29D; B29D11/00; B29D11/00009; B29D11/00038; B29D11/00865; B29D11/00894; B29D11/00913; C; C08; C08J; C08J3/00; C08J3/02; C08J3/03; C08J3/075; C08J7/00; C08J7/04; C08J7/0427; C08J7/06; C08J2339/00; C08J2339/04; C08J2339/06; C08J2427/00; C08J2427/02; C08J2427/04
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
75 words
A shaped organic polymer hydrogel containing within the gel an opaque or translucent, physiologically innocuous, water-insoluble precipitate selected from the group consisting of water-insoluble hydroxides, oxides, sulphates and sulphides of barium, aluminum and zinc in an amount sufficient to render said hydrogel opaque or translucent, and a dye for the hydrogel selected from the group consisting of reactive, solvent, disperse and vat dyes in at least part of those areas containing the said water-insoluble precipitate.
Claim 2
Dependent Claim
75 words
A shaped organic polymer hydrogel containing within the gel an opaque or translucent, physiologically innocuous, water-insoluble precipitate selected from the group consisting of water-insoluble hydroxides, oxides, sulphates and sulphides of barium, aluminum and zinc in an amount sufficient to render said hydrogel opaque or translucent, and a dye for the hydrogel selected from the group consisting of reactive, solvent, disperse and vat dyes in at least part of those areas containing the said water-insoluble precipitate.
Claim 3
Dependent Claim
39 words
A shaped hydrogel according to claim 1 in the form of a contact lens in which the part overlying the iris of the eye is coloured and opaque and the part overlaying the pupil of the eye is transparent.
Claim 4
Dependent Claim
39 words
A shaped hydrogel according to claim 2 in which, in the said part overlaying the iris of the eye, the water-insoluble precipitate is opaque, white or pale coloured, and patterned and the dye is uniform or in a pattern.
Claim 5
Dependent Claim
45 words
A shaped hydrogel according to claim 1 for cosmetic or prosthetic purposes in the form of a contact lens in which the part overlying the iris of the eye is coloured and opaque and the part overlying the pupil of the eye is dark coloured.
Claim 6
Dependent Claim
159 words
Method of making a shaped organic polymer hydrogel containing within the gel an opaque or translucent, physiologically innocuous, water-insoluble precipitate selected from the group consisting of water-insoluble hydroxides, oxides, sulphate and sulphides of barium, aluminum and zinc in an amount sufficient to render said hydrogel opaque or translucent, and a dye for the hydrogel selected from the group consisting of reactive, solvent, disperse and vat dyes in at least part of those areas containing the said water-insoluble precipitate which comprises applying to a shaped organic polymer hydrogel a solution of a precursor of the water-insoluble precipitate under conditions such that the said solution penetrates substantially into the hydrogel, and then an agent which interacts with said precursor to form said water-insoluble precipitate in situ in the hydrogel, and dyeing with a reactive, solvent, disperse or vat dye at least part of the area in which the precipitate is formed before, during or after the formation of the said precipitate.
Claim 7
Dependent Claim
159 words
Method of making a shaped organic polymer hydrogel containing within the gel an opaque or translucent, physiologically innocuous, water-insoluble precipitate selected from the group consisting of water-insoluble hydroxides, oxides, sulphate and sulphides of barium, aluminum and zinc in an amount sufficient to render said hydrogel opaque or translucent, and a dye for the hydrogel selected from the group consisting of reactive, solvent, disperse and vat dyes in at least part of those areas containing the said water-insoluble precipitate which comprises applying to a shaped organic polymer hydrogel a solution of a precursor of the water-insoluble precipitate under conditions such that the said solution penetrates substantially into the hydrogel, and then an agent which interacts with said precursor to form said water-insoluble precipitate in situ in the hydrogel, and dyeing with a reactive, solvent, disperse or vat dye at least part of the area in which the precipitate is formed before, during or after the formation of the said precipitate.
Claim 8
Dependent Claim
54 words
Method according to claim 5 in which a solution of a water-soluble salt of barium, aluminum or zinc is first applied to the hydrogel and a water-insoluble hydroxide, oxide, sulphate or sulphide is then precipitated in the hydrogel by applying thereto a reagent which reacts with the said salt to produce a water-insoluble precipitate.
Claim 9
Dependent Claim
36 words
Method according to claim 6, in which the said solution of a water-soluble salt of barium, aluminum or zinc includes as swelling agent for the said hydrogel, methanol, ethanol, acetone, ethylene glycol monomethyl ether, or dimethylformamide.
Claim 10
Dependent Claim
32 words
Method according to claim 5 in which the solution of the said precursor is applied uniformly or in a pattern to the hydrogel by screen printing, pad printing, or ink jet printing.
Claim 11
Dependent Claim
22 words
Method according to claim 6 in which the water-insoluble precipitate is barium sulphate, aluminum hydroxide, or zinc hydroxide or a mixture thereof.
Claim 12
Dependent Claim
25 words
Method according to claim 5 in which the dyestuff is applied uniformly or in a pattern by screen printing, pad printing or ink jet printing.
References Cited (Backward Citations)
GB1004424A
Cited
US3476499A
Cited
US3679504A
Cited
GB1583492A
Cited
US4559059A
Cited
US4494954A
Cited
JPS58136882A
Cited
US4559897A
Cited
EP0122771A1
Cited
US4518390A
Cited
US4582402A
Cited
US4702574A
Cited
US4634449A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-12-31 | 1994-07-02 | 1995-01-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-12-31 | 1998-07-02 | 1999-01-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-12-31 | 2002-07-02 | 2003-01-01 | $7700.00 | Window Closed / Lapsed |