Zinc or cadmium coated, surface oxidized electrode wire for EDM cutting of a workpiece; and method for forming such a wire
Assignee: Agie Charmilles New Technologies SA
•
Filing: 1988-06-13
•
Granted: 1990-12-11
•
Expires: 2008-06-13
Abstract
Abstract A method for forming an EDM wire electrode includes coating a copper wire core with zinc, and then heating the coated wire in an oxidizing atmosphere to simultaneously provide a copper-zinc alloy layer over the copper core and a zinc oxide surface on the alloy layer. The oxide- and alloy-coated wire is then reduced in diameter to reduce the thickness of the alloy layer by about one-half of its initial thickness. The resulting electrodes wire permits a greater current density and a greater tractional force to be employed, yielding a significantly greater machining speed in the EDM process.
Inventors
- 👤 Jean Briffod
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 03:45
CPC Classifications
C; C23; C23C; C23C26/00; B; B23; B23H; B23H7/00; B23H7/02; B23H7/08; C23C8/00; C23C8/02
Claims Analysis
Total Claims: 41
Claim 1
Independent Claim
168 words
A method for forming a wire useful as an electrode tool in an EDM apparatus, comprising the steps of: depositing a coating containing a volatile metal selected from the group consisting of zinc, cadmium and alloys thereof on a wire core, said coating metal being capable of dissusing into a substance comprised in said core upon heating, so as to form an admixed layer on said core; heating the resulting coated wire in an oxidizing atmosphere at a temperature of at least 700° C. to diffuse at least one of said coating metal and said core substance into the other, and to create an admixed layer of said coating metal and said core substance, said admixed layer having a thickness of about three times that of said initial metal coating, while simultaneously oxidizing the outer surface of said coating metal; and reducing the diameter of the resulting wire sufficiently to reduce the thickness of said admixed layer by at least about 30 per cent of its initial thickness.
Claim 2
Independent Claim
168 words
A method for forming a wire useful as an electrode tool in an EDM apparatus, comprising the steps of: depositing a coating containing a volatile metal selected from the group consisting of zinc, cadmium and alloys thereof on a wire core, said coating metal being capable of dissusing into a substance comprised in said core upon heating, so as to form an admixed layer on said core; heating the resulting coated wire in an oxidizing atmosphere at a temperature of at least 700° C. to diffuse at least one of said coating metal and said core substance into the other, and to create an admixed layer of said coating metal and said core substance, said admixed layer having a thickness of about three times that of said initial metal coating, while simultaneously oxidizing the outer surface of said coating metal; and reducing the diameter of the resulting wire sufficiently to reduce the thickness of said admixed layer by at least about 30 per cent of its initial thickness.
Claim 3
Dependent Claim
12 words
The invention according to claim 1, wherein said core substance is copper.
Claim 4
Dependent Claim
25 words
The invention according to claim 1, comprising reducing the thickness of said admixed layer by at least about 35 per cent of its initial thickness.
Claim 5
Dependent Claim
21 words
The invention according to claim 1, comprising reducing the thickness of said admixed layer by about one-half of its initial thickness.
Claim 6
Dependent Claim
17 words
The invention according to claim 1, wherein said heating step is carried out at about 850° C.
Claim 7
Dependent Claim
17 words
The invention according to claim 1, wherein said heating step is carried out for about 8 seconds.
Claim 8
Dependent Claim
21 words
The invention according to claim 1, wherein said core substance is a metal, whereby said admixed layer is an alloy layer.
Claim 9
Dependent Claim
24 words
The invention according to claim 1, wherein said reducing step is carried out by drawing said coated wire through at least one drawing die.
Claim 10
Dependent Claim
21 words
The invention according to claim 1, wherein said reducing step is carried out by cold hammering said coated and covered wire.
Claim 11
Dependent Claim
15 words
The invention according to claim 1, wherein said core substance is steel, brass or carbon.
Claim 12
Dependent Claim
15 words
The invention according to claim 1, wherein said core substance has a high tensile strength.
Claim 13
Dependent Claim
20 words
The invention according to claim 1, wherein said coating metal has an initial thickness of about 5 to 20 micrometers.
Claim 14
Dependent Claim
19 words
The invention according to claim 1, wherein said coating metal has an initial thickness of 13 to 15 micrometers.
Claim 15
Dependent Claim
23 words
The invention according to claim 1, wherein the concentration of said core substance in said admixed layer decreases in a radially outward direction.
Claim 16
Dependent Claim
20 words
The invention according to claim 1, wherein said admixed layer has an initial thickness of about 20 to 70 micrometers.
Claim 17
Independent Claim
102 words
A method for forming a wire useful as an electrode tool in an EDM apparatus, comprising: depositing a zinc coating of about 15 micrometers thickness on a copper wire core; heating the resulting coated wire for about 8 seconds at about 850° C. in an oxidizing atmosphere so as to create a copper-zinc alloy layer of about 45 micrometers thickness on said core, covered by a metal oxide layer on the order of about 1 micrometer thickness; and reducing the diameter of the resulting alloy and oxide covered wire so as to reduce the thickness of said alloy layer by about one-half.
Claim 18
Independent Claim
102 words
A method for forming a wire useful as an electrode tool in an EDM apparatus, comprising: depositing a zinc coating of about 15 micrometers thickness on a copper wire core; heating the resulting coated wire for about 8 seconds at about 850° C. in an oxidizing atmosphere so as to create a copper-zinc alloy layer of about 45 micrometers thickness on said core, covered by a metal oxide layer on the order of about 1 micrometer thickness; and reducing the diameter of the resulting alloy and oxide covered wire so as to reduce the thickness of said alloy layer by about one-half.
Claim 19
Dependent Claim
105 words
An electrically conductive wire having a good tensile strength, comprising: a core containing a material having a high tensile strength; an intermediate admixed layer covering said core, made of a mixture of said core material and a metal selected from the group consisting of zinc and cadmium, the concentration of said metal in said admixed layer generally increasing in a radially outward direction; and a thin outer layer atop said admixed layer made of an oxide of said metal; the surface of said wire being hardened by a die-drawing step, conducted to reduce the thickness of said admixed layer by at least 30 per cent.
Claim 20
Dependent Claim
105 words
An electrically conductive wire having a good tensile strength, comprising: a core containing a material having a high tensile strength; an intermediate admixed layer covering said core, made of a mixture of said core material and a metal selected from the group consisting of zinc and cadmium, the concentration of said metal in said admixed layer generally increasing in a radially outward direction; and a thin outer layer atop said admixed layer made of an oxide of said metal; the surface of said wire being hardened by a die-drawing step, conducted to reduce the thickness of said admixed layer by at least 30 per cent.
Claim 21
Dependent Claim
25 words
A wire according to claim 17, wherein said core is made of a material selected from the group consisting of copper, brass, steel and carbon.
Claim 22
Dependent Claim
19 words
A wire according to claim 17, wherein said admixed layer is made of an alloy of copper and zinc.
Claim 23
Dependent Claim
22 words
A wire according to claim 17, wherein the thickness of said admixed layer is in the range between 10 to 35 micrometers.
Claim 24
Dependent Claim
19 words
A wire according to claim 17, wherein said metal has an initial thickness of about 5 to 20 micrometers.
Claim 25
Dependent Claim
18 words
A wire according to claim 17, wherein said metal has an initial thickness of 13 to 15 micrometers.
Claim 26
Dependent Claim
23 words
A wire according to claim 17, wherein the concentration of said core material in said admixed layer decreases in a radially outward direction.
Claim 27
Dependent Claim
20 words
A wire according to claim 17, wherein said admixed layer has an initial thickness of about 20 to 70 micrometers.
Claim 28
Dependent Claim
90 words
An electrically conductive wire comprising: a core comprised of a core material having a high tensile strength; an intermediate admixed layer covering said core, comprising a mixture of part of said core material and at least one volatile metal, at least one of said core material and said metal being diffused with the other; and a thin outer layer atop said admixed layer, comprising an oxide of said metal; said wire being surface hardened by a reduction of the thickness of said admixed layer by about at least 30 percent.
Claim 29
Dependent Claim
90 words
An electrically conductive wire comprising: a core comprised of a core material having a high tensile strength; an intermediate admixed layer covering said core, comprising a mixture of part of said core material and at least one volatile metal, at least one of said core material and said metal being diffused with the other; and a thin outer layer atop said admixed layer, comprising an oxide of said metal; said wire being surface hardened by a reduction of the thickness of said admixed layer by about at least 30 percent.
Claim 30
Dependent Claim
28 words
The invention according to claim 25, wherein the concentration of said metal in said intermediate admixed layer generally increases gradually in a direction radially outward from said core.
Claim 31
Dependent Claim
20 words
The invention according to claim 25, wherein said core material comprises at least one of copper, brass, steel and carbon.
Claim 32
Dependent Claim
19 words
The invention according to claim 25, wherein the thickness of said admixed layer is about 10 to 35 micrometers.
Claim 33
Dependent Claim
17 words
The invention according to claim 25, wherein said admixed layer comprises an alloy of copper and zinc.
Claim 34
Dependent Claim
12 words
The invention according to claim 25, wherein said wire is die-drawn hardened.
Claim 35
Dependent Claim
17 words
The invention according to claim 25, wherein said volatile metal is zinc, cadmium, or an alloy thereof.
Claim 36
Dependent Claim
94 words
An EDM apparatus incorporating an electrically conductive wire comprising: a core comprised of a core material having a high tensile strength; an intermediate admixed layer covering said core, comprising a mixture of part of said core material and at least one volatile metal, at least one of said core material and said metal being diffused with the other; and a thin outer layer atop said admixed layer, comprising an oxide of said metal; said wire being surface hardened by a reduction of the thickness of said admixed layer by about at least 30 percent.
Claim 37
Dependent Claim
94 words
An EDM apparatus incorporating an electrically conductive wire comprising: a core comprised of a core material having a high tensile strength; an intermediate admixed layer covering said core, comprising a mixture of part of said core material and at least one volatile metal, at least one of said core material and said metal being diffused with the other; and a thin outer layer atop said admixed layer, comprising an oxide of said metal; said wire being surface hardened by a reduction of the thickness of said admixed layer by about at least 30 percent.
Claim 38
Dependent Claim
115 words
An electrically conductive wire comprising: a core comprised of a core material having a high tensile strength; an intermediate admixed layer covering said core, comprising a mixture of part of said core material and at least one volatile metal, at least one of said core material and said metal being diffused with the other; and a thin outer layer atop said admixed layer, comprising an oxide of said metal; said wire being surface hardened by a reduction of the thickness of said admixed layer by about at least 30 percent, and said intermediate layer being formed from an initial coating of said volatile metal atop said core about one-third as thick as said intermediate layer.
Claim 39
Dependent Claim
115 words
An electrically conductive wire comprising: a core comprised of a core material having a high tensile strength; an intermediate admixed layer covering said core, comprising a mixture of part of said core material and at least one volatile metal, at least one of said core material and said metal being diffused with the other; and a thin outer layer atop said admixed layer, comprising an oxide of said metal; said wire being surface hardened by a reduction of the thickness of said admixed layer by about at least 30 percent, and said intermediate layer being formed from an initial coating of said volatile metal atop said core about one-third as thick as said intermediate layer.
Claim 40
Dependent Claim
112 words
An electrically conductive wire comprising: a copper wire core; a zinc oxide layer over said core, formed from an initial zinc coating about 15 micrometers thick which is heated for about 8 seconds at about 850° C. in an oxidizing atmosphere so as to yield a zinc oxide layer on the order of about one micrometer thick, and which is thereafter reduced in diameter by reducing said wire in diameter; and a copper-zinc alloy layer between said core and said zinc oxide layer, initially about 45 micrometers thick on said core and formed by said heating, which is reduced by about one-half in thickness upon said reduction in diameter of said wire.
Claim 41
Dependent Claim
112 words
An electrically conductive wire comprising: a copper wire core; a zinc oxide layer over said core, formed from an initial zinc coating about 15 micrometers thick which is heated for about 8 seconds at about 850° C. in an oxidizing atmosphere so as to yield a zinc oxide layer on the order of about one micrometer thick, and which is thereafter reduced in diameter by reducing said wire in diameter; and a copper-zinc alloy layer between said core and said zinc oxide layer, initially about 45 micrometers thick on said core and formed by said heating, which is reduced by about one-half in thickness upon said reduction in diameter of said wire.
References Cited (Backward Citations)
USRE21903E
Cited
US2383118A
Cited
US3478552A
Cited
US3664169A
Cited
US4287404B1
Cited
US4287404A
Cited
DE2922206A1
Cited
US4250371A
Cited
US4341939A
Cited
JPS5691308A
Cited
US4418263A
Cited
JPS5950143A
Cited
JPS59127921A
Cited
JPS59129629A
Cited
JPS59134623A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-12-10 | 1994-06-11 | 1994-12-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-12-10 | 1998-06-11 | 1998-12-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-12-10 | 2002-06-11 | 2002-12-11 | $7700.00 | Window Closed / Lapsed |