Method for forming hollow partially crystalline biaxially oriented heat set polyethylene terephthalate articles
Assignee: Graham Packaging Plastic Products Inc
•
Filing: 1988-05-18
•
Granted: 1989-10-03
•
Expires: 2008-05-18
Abstract
Abstract A method and apparatus of forming a hollow partially crystalline heat set biaxially oriented polyethylene terephthalate container having a hemispherical base comprising blowing a heated parison at orientation temperature outwardly against the confines of a mold which is at heat setting temperature wherein the side wall and the major portion of the base of the container are subjected to a heat setting temperature and the center of the base of the container is subjected to a temperature not greater than 150 DEG C. so that the central portion is crystallized a substantially lesser amount than the side wall and the major portion of the base. The container is then quenched. The resultant container can be formed at a rapid cycle and has good drop impact properties and obviates the problems of sticking to the hot mold or blow out when the hot mold is opened.
Inventors
- 👤 Prakash R. Ajmera
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 16:11
CPC Classifications
B; B29; B29C; B29C49/00; B29C49/42; B29C49/48; B29C49/4823; B29C49/64; B29C43/00; B29C43/32; B29C43/52; B29C2043/527; B29C2049/4838; B29C2049/4846; B29C2049/4874; B29C2049/4876; Y; Y10; Y10S; Y10S264/00; Y10S264/90; Y10S264/903
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
371 words
A method of forming a hollow biaxially oriented heat set partially crystalline polyethylene terephthalate container having side walls and a closed base opposite an open neck area, said closed base being of outwardly convex, hemispherical shape and comprising a major portion and a central portion surrounded by said major portion, the ratio of the diameter of said central portion of the base of the container to the diameter of the base of the container ranging from about 0.2 to 0.4, said method comprising the steps of: closing a mold around a biaxially oriented hollow polyethylene terephthalate container, said mold having side walls and a mold base portion comprising a major mold base portion corresponds to said major portion of the base of said container and a central mold base portion corresponding to the central portion of the base of said container, maintaining the side walls and major portion of the base of the mold at a temperature in the range of form 120° C. to 250° C., which corresponds to a temperature which effects heat setting of polyethylene terephthalate, while maintaining only said central portion of the base of the mold at a temperature substantially not greater than 150° C., said central portion of the base of the mold being maintained at a temperature substantially less than the temperature of the side walls of the mold, introducing fluid pressure internally of the hollow container to maintain contact between the container and internal mold surfaces for a time sufficient to heat set and partially crystallize the side walls of the container and the major portion of the base of the container while also crystallizing the central portion of the base of the container a substantially lesser amount than the sidewalls and major portion of the base of the container, and quenching the container to preclude shrinkage thereof, said heat setting of side walls of said container and of said central and major portions of the base of the container being sufficient to prevent the container from sticking to said internal mold surfaces and to eliminate deformation of or blow out of the central portion of the base of the container upon opening of said mold while maintaining internal pressure within said container.
Claim 2
Independent Claim
371 words
A method of forming a hollow biaxially oriented heat set partially crystalline polyethylene terephthalate container having side walls and a closed base opposite an open neck area, said closed base being of outwardly convex, hemispherical shape and comprising a major portion and a central portion surrounded by said major portion, the ratio of the diameter of said central portion of the base of the container to the diameter of the base of the container ranging from about 0.2 to 0.4, said method comprising the steps of: closing a mold around a biaxially oriented hollow polyethylene terephthalate container, said mold having side walls and a mold base portion comprising a major mold base portion corresponds to said major portion of the base of said container and a central mold base portion corresponding to the central portion of the base of said container, maintaining the side walls and major portion of the base of the mold at a temperature in the range of form 120° C. to 250° C., which corresponds to a temperature which effects heat setting of polyethylene terephthalate, while maintaining only said central portion of the base of the mold at a temperature substantially not greater than 150° C., said central portion of the base of the mold being maintained at a temperature substantially less than the temperature of the side walls of the mold, introducing fluid pressure internally of the hollow container to maintain contact between the container and internal mold surfaces for a time sufficient to heat set and partially crystallize the side walls of the container and the major portion of the base of the container while also crystallizing the central portion of the base of the container a substantially lesser amount than the sidewalls and major portion of the base of the container, and quenching the container to preclude shrinkage thereof, said heat setting of side walls of said container and of said central and major portions of the base of the container being sufficient to prevent the container from sticking to said internal mold surfaces and to eliminate deformation of or blow out of the central portion of the base of the container upon opening of said mold while maintaining internal pressure within said container.
Claim 3
Dependent Claim
66 words
The method set forth in claim 1 wherein the side walls and major portion of the base are maintained at a heated set temperature between about 120° C. and 250° C. and the central portion of the base of the mold is maintained at a temperature between about 1° C. and 150° C. and the quench temperature is maintained between about 1° C. and 100° C.
Claim 4
Dependent Claim
22 words
The method set forth in claim 2 wherein the heat set time comprises 1-10 seconds and the quenching time comprises 0.5-10 seconds.
Claim 5
Dependent Claim
44 words
The method set forth in claim 1 wherein the expanding and heat setting area performed in a hot mold and the quenching is provided in a cold mold and said container is transferred to said cold mold while maintaining internal pressure in said container.
Claim 6
Dependent Claim
19 words
The method set forth in claim 1 wherein the expanding and heat setting are performed in the same mold.
Claim 7
Dependent Claim
19 words
The method set forth in claim 5 wherein the quenching is performed by changing the temperature of the mold.
Claim 8
Dependent Claim
17 words
The method set forth in claim 5 wherein the quenching is performed by internally cooling the container.
Claim 9
Dependent Claim
27 words
The method set forth in claim 5 wherein the quenching is performed by removing the container from the mold and cooling the container externally under internal pressure.
Claim 10
Dependent Claim
39 words
The method set forth in claim 1 wherein said step of maintaining the central portion of the mold at a temperature not greater than 150° C. is achieved by insulating the central portion of the base of the mold.
Claim 11
Dependent Claim
45 words
The method set forth in claim 1 wherein said step of maintaining the central portion of the base of the mold at a temperature not greater than 150° C. is achieved by passing cooling fluid through the central portion of the base of the mold.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-10-02 | 1993-04-03 | 1993-10-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-10-02 | 1997-04-03 | 1997-10-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-10-02 | 2001-04-03 | 2001-10-03 | $7700.00 | Window Closed / Lapsed |