Porous metal coated implant and method for producing same
Assignee: Trigon Inc
•
Filing: 1988-09-14
•
Granted: 1989-08-08
•
Expires: 2008-09-14
Abstract
Abstract A porous metal coated implant is produced by diffusion bonding metal powder particles, preferably spherical or flattened spherical metal powder particles of commercially pure titanium grade, in the form of an insert or pad to a substrate, preferably commercially pure titanium or Ti 6Al-4V ELI, a prosthesis below the beta-transus of the substrate material, under pressure and temperature in a non-reactive atmosphere, such as vacuum. The use of pressure permits bonding temperatures to be reduced to approximately 50% of the melting point of the substrate material. A clamping mechanism for applying pressure to the components is also disclosed.
Inventors
- 👤 Clifford M. Bugle
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 16:04
CPC Classifications
A; A61; A61F; A61F2/00; A61F2/02; A61F2/30; A61F2/30767; A61L; A61L27/00; A61L27/28; A61L27/30; A61L27/306; B; B22; B22F; B22F7/00; B22F7/002; C; C23; C23C; C23C26/00; A61F2/3094; A61F2/32; A61F2/36; A61F2/3662; A61F2/367; A61F2002/30001; A61F2002/30316; A61F2002/30317; A61F2002/30322; A61F2002/30769; A61F2002/30929; A61F2/3609; A61F2002/3625; A61F2002/3631; A61F2250/00; A61F2250/0014; A61F2250/0026; A61F2310/00; A61F2310/00005; A61F2310/00011; A61F2310/00023; A61F2310/00389; A61F2310/00395; A61F2310/00407
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
200 words
A method of producing a porous metal coated substrate by diffusion bonding metal powder to a substrate comprising the steps of: (A) providing a substrate having a surface to which said powder is to be bonded; (B) providing a preformed porous metal powder coating shape having a bonding surface for contacting said substrate surface; wherein said preformed porous metal powder coating shape is produced by: (a) disposing metal powder particles in a mold having a cavity of the shape of the desired coating; (b) presintering said powder particles at a time and temperature to form said porous metal powder shape; (c) removing said metal powder shape from the mold; (d) sintering said metal powder shape at high temperature to achieve the required particle bond strength and porosity; and (e) flattening the particles on only one surface of the porous metal powder coating shape by removing a portion thereof to form the bonding surface of the porous metal powder shape; (C) contacting the bonding surface of the porous coating shape to the substrate surface; and (D) in a non-reactive atmosphere, applying heat and pressure to cause the contact surfaces to diffusion bond to one another below the beta-transus of the substrate.
Claim 2
Independent Claim
200 words
A method of producing a porous metal coated substrate by diffusion bonding metal powder to a substrate comprising the steps of: (A) providing a substrate having a surface to which said powder is to be bonded; (B) providing a preformed porous metal powder coating shape having a bonding surface for contacting said substrate surface; wherein said preformed porous metal powder coating shape is produced by: (a) disposing metal powder particles in a mold having a cavity of the shape of the desired coating; (b) presintering said powder particles at a time and temperature to form said porous metal powder shape; (c) removing said metal powder shape from the mold; (d) sintering said metal powder shape at high temperature to achieve the required particle bond strength and porosity; and (e) flattening the particles on only one surface of the porous metal powder coating shape by removing a portion thereof to form the bonding surface of the porous metal powder shape; (C) contacting the bonding surface of the porous coating shape to the substrate surface; and (D) in a non-reactive atmosphere, applying heat and pressure to cause the contact surfaces to diffusion bond to one another below the beta-transus of the substrate.
Claim 3
Dependent Claim
27 words
The method of producing a porous coated substrate as set forth in claim 1 wherein said portion is removed by one of mechanical, chemical and electrical means.
Claim 4
Dependent Claim
25 words
The method of producing a porous coated substrate as set forth in claim 1 wherein said mold is one of metal, ceramic and graphite material.
Claim 5
Dependent Claim
44 words
The method of producing a porous metal coated substrate as set forth in claim 1 or claim 2 wherein said powder particles are one of commercially pure titanium and titanium alloy and said substrate is one of commercially pure titanium and a titanium alloy.
Claim 6
Dependent Claim
31 words
The method of producing a porous metal coated substrate as set forth in claim 4 wherein said temperature is approximately 1700° F. and said time is approximately one and one-half hours.
Claim 7
Dependent Claim
21 words
The method of producing a porous metal coated substrate as set forth in claim 1 wherein said non-reactive atmosphere is vacuum.
Claim 8
Dependent Claim
54 words
The method of producing a porous metal coated substrate as set forth in claim 1 wherein said porous coated shape is in the form of an inset having a thickness between approximately 0.045 and 0.055 inches and said substrate includes a recess having a configuration of substantially the same shape for receiving said insert.
Claim 9
Independent Claim
111 words
A method of producing a porous metal coating shape for use as an insert in an implant comprising: (i) disposing spherical metal powder particles in a mold having a cavity of the shape of the desired coating; (ii) presintering said powder particles at time and temperature to form a porous metal powder shape; (iii) removing said metal powder shape from the mold; (iv) sintering said metal powder shape at high temperature to achieve the required particle bond strength and porosity; and (v) flattening the particles only on the surface of the porous metal coating shape by removing a portion thereof to provide a bonding surface on the porous metal powder shape.
Claim 10
Independent Claim
111 words
A method of producing a porous metal coating shape for use as an insert in an implant comprising: (i) disposing spherical metal powder particles in a mold having a cavity of the shape of the desired coating; (ii) presintering said powder particles at time and temperature to form a porous metal powder shape; (iii) removing said metal powder shape from the mold; (iv) sintering said metal powder shape at high temperature to achieve the required particle bond strength and porosity; and (v) flattening the particles only on the surface of the porous metal coating shape by removing a portion thereof to provide a bonding surface on the porous metal powder shape.
Claim 11
Dependent Claim
20 words
The method as set forth in claim 8 wherein said mold is one of a metal, ceramic and graphite material.
Claim 12
Dependent Claim
26 words
The method as set forth in claim 8 wherein said presintering is carried out at a temperature of approximately 1750° F. for one and one-half hours.
Claim 13
Dependent Claim
69 words
A porous metal coated substrate comprising a metal substrate having an outer surface and a porous powder metal coating shape consisting of a plurality of metal powder particles diffusion bonded thereto, said particles being spherical and the particles on a surface of the shape being flattened on one side by removal of portions thereof to form a bonding surface for contact to said outer surface of the metal substrate.
Claim 14
Dependent Claim
69 words
A porous metal coated substrate comprising a metal substrate having an outer surface and a porous powder metal coating shape consisting of a plurality of metal powder particles diffusion bonded thereto, said particles being spherical and the particles on a surface of the shape being flattened on one side by removal of portions thereof to form a bonding surface for contact to said outer surface of the metal substrate.
Claim 15
Dependent Claim
38 words
A porous metal coated substrate as set forth in claim 11 wherein said particles are one of a commercially pure titanium and titanium alloy material and said substrate is one of commercially pure titanium and titanium alloy material.
Claim 16
Dependent Claim
48 words
A porous metal coated substrate as set forth in claim 11 wherein said shape is in the form of an insert having a thickness between approximately 0.045 and 0.055 inches and said substrate includes a recess having a configuration of substantially the same shape for receiving said insert.
Claim 17
Dependent Claim
64 words
A porous metal coating shape for use as an insert in a medical implant comprising a plurality of presintered metal powder particles in the form of an insert and high temperature sintered for diffusion bonding to a metal substrate, said particles being spherical and the particles on a surface being flattened on one side by removal of portions thereof to form a bonding surface.
Claim 18
Dependent Claim
64 words
A porous metal coating shape for use as an insert in a medical implant comprising a plurality of presintered metal powder particles in the form of an insert and high temperature sintered for diffusion bonding to a metal substrate, said particles being spherical and the particles on a surface being flattened on one side by removal of portions thereof to form a bonding surface.
References Cited (Backward Citations)
US4570271A
Cited
US4644942A
Cited
US4534935A
Cited
US4589883A
Cited
US4612160A
Cited
US4743262A
Cited
US4743262B1
Cited
US4650109A
Cited
US4718912A
Cited
US4636219A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-08-07 | 1993-02-06 | 1993-08-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-08-07 | 1997-02-06 | 1997-08-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-08-07 | 2001-02-06 | 2001-08-08 | $7700.00 | Window Closed / Lapsed |