US4832790A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of making metal molds and dies
Assignee: Advanced Tool Technologies Inc
•
Filing: 1987-02-24
•
Granted: 1989-05-23
•
Expires: 2007-02-24
Abstract
Abstract A method of forming a metal mold or die from a model of the mold contours. A workpiece for the mold is coated with a material which is resistant to an acidic etchant, and is then immersed in the etchant and brought into contact with a template for the metal mold or dies. Those portions of the coating contacted by the template are displaced until the template contacts the surface of the workpiece. The template is then withdrawn to permit the echant to etch any portions of the workpiece exposed by displacement of the coating. The process is progressively repeated until the surface of the workpiece conforms to any contouring of the surface of the template.
Inventors
- 👤 James J. Rossetti
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 16:22
CPC Classifications
C; C23; C23F; C23F1/00; C23F1/02; C23F1/04
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
175 words
A method of forming a contoured surface in a workpiece in the form of a mold or die by selectively etching the surface thereof, comprising the steps of (a) providing a template having a contoured surface which is a negative pattern of the contoured surface to be formed in the workpiece, (b) applying a coating to the workpiece, the coating being resistant to an etchant and comprising a viscous material that may be physically displaced at ambient temperature, (c) immersing the coated workpiece in said etchant, (d) pressing the template against the coated workpiece and only displacing portions of the coating contacted by the template as the contoured surface moves into contact with the workpiece, and thereby exposing portions of the workpiece, (e) withdrawing the template from the coated workpiece without removing the displaced coating with the template to permit the etchant to etch portions of the workpiece exposed by displacement of the coating, and (f) repeating steps (d) through (e) until the surface of the workpiece conforms to the contoured surface of the template.
Claim 2
Independent Claim
175 words
A method of forming a contoured surface in a workpiece in the form of a mold or die by selectively etching the surface thereof, comprising the steps of (a) providing a template having a contoured surface which is a negative pattern of the contoured surface to be formed in the workpiece, (b) applying a coating to the workpiece, the coating being resistant to an etchant and comprising a viscous material that may be physically displaced at ambient temperature, (c) immersing the coated workpiece in said etchant, (d) pressing the template against the coated workpiece and only displacing portions of the coating contacted by the template as the contoured surface moves into contact with the workpiece, and thereby exposing portions of the workpiece, (e) withdrawing the template from the coated workpiece without removing the displaced coating with the template to permit the etchant to etch portions of the workpiece exposed by displacement of the coating, and (f) repeating steps (d) through (e) until the surface of the workpiece conforms to the contoured surface of the template.
Claim 3
Dependent Claim
16 words
The method according to claim 1 including the step of heating the workpiece before step (d).
Claim 4
Dependent Claim
17 words
The method according to claim 2 in which the workpiece is heated to at least 90° F.
Claim 5
Dependent Claim
32 words
The method according to claim 1 including the step of applying a detergent in an amount such that it acts as a wetting and release agent to the etchant before step (c).
Claim 6
Dependent Claim
24 words
The method according to claim 4 in which up to 6 drops of detergent are applied per 16 ounces by volume of the etchant.
Claim 7
Dependent Claim
24 words
The method according to claim 1 including the step of applying detergent in an amount to retard etching of the etchant before step (c).
Claim 8
Dependent Claim
24 words
The method according to claim 6 in which at least 20 drops of detergent are applied per 16 ounces by volume of the etchant.
Claim 9
Dependent Claim
31 words
The method according to claim 1 including the steps of periodically interrupting step (f), cleaning the workpiece, reapplying the coating, reimmersing the coated workpiece in the etchant, and resuming step (f).
Claim 10
Dependent Claim
17 words
The method according to claim 8 in which step (f) is interrupted at minimum ten minute intervals.
Claim 11
Dependent Claim
16 words
The method according to claim 1 in which the coating consists of a flowable petroleum-based material.
Claim 12
Dependent Claim
22 words
The method according to claim 10 in which the coating is selected from the group consisting of silicone grease and lithium grease.
Claim 13
Dependent Claim
23 words
The method according to claim 1 in which the coating consists of a petroleum-based asphaltum and beeswax, and is warmed before step (b).
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-05-22 | 1992-11-21 | 1993-05-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-05-22 | 1996-11-21 | 1997-05-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-05-22 | 2000-11-21 | 2001-05-23 | $7700.00 | Window Closed / Lapsed |