Polyester fiber having excellent thermal dimensional _ stability, chemical stability and high _ tenacity and process for the production thereof
Assignee: Toyobo Petcord Co Ltd
•
Filing: 1985-04-22
•
Granted: 1989-05-09
•
Expires: 2005-04-22
Abstract
Abstract A polyester fiber having excellent thermal dimensional stability and chemical stability as well as high tenacity, which is a drawn yarn produced by melt-spinning a polyester comprising predominantly polyethylene terephthalate, solidification the spun yarn and then drawing the yarn under specified conditions and has specified properties such as intrinsic viscosity, diethylene glycol content, carboxyl group content, birefringence, yarn tenacity and difference of average birefringence between surface and center of monofilament, and further low dry heat shrink and work loss when heat-treated, said polyester fiber being useful as a reinforcement for rubber goods, specifically as a tire cord, and processes for the production of the polyester fiber.
Inventors
- 👤 Kazuyuki Yabuki
- 👤 Yohji Kohmura
- 👤 Mitsuo Iwasaki
- 👤 Hiroshi Yasuda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 00:39
CPC Classifications
D; D01; D01F; D01F6/00; D01F6/58; D01F6/62; D01D; D01D5/00; D01D5/08
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
190 words
A polyester fiber having excellent thermal dimensional stability and chemical stability as well as high tenacity, comprising a drawn yarn produced by melt-spinning a polyester comprising predominantly polyethylene terephthalate, solidifying the spun yarn with cooling and then drawing the yarn, and having the following properties: (i) intrinsic viscosity: 0.8 or more; (ii) content of diethylene glycol: approximately 2.5% of terephthalic acid residue; (iii) content of carboxyl groups: 30 equivalent/10 6 g or less; (vi) average birefringence: 0.190 or more; (v) yarn tenacity: 8.5 g/d or more; and (vi) value obtained by dividing the difference of birefringence between surface and center of monofilament by average birefringence: 0.555 or less, said polyester fiber further having the following properties when it is heat-treated at constant length at 240° C. for one minute: (a) dry heat shrink when freely heat-treated at 175° for 30 minutes: 3.0% or less, and (b) work loss when the hysteresis loop is measured at a stress between 0.6 g/d and 0.05 g/d under the following conditions length of test sample of 10 inch, strain rate of 0.5 inch/minute and a temperature of 150° C.: 2.0×10 -5 inch-pound/denier or less.
Claim 2
Dependent Claim
190 words
A polyester fiber having excellent thermal dimensional stability and chemical stability as well as high tenacity, comprising a drawn yarn produced by melt-spinning a polyester comprising predominantly polyethylene terephthalate, solidifying the spun yarn with cooling and then drawing the yarn, and having the following properties: (i) intrinsic viscosity: 0.8 or more; (ii) content of diethylene glycol: approximately 2.5% of terephthalic acid residue; (iii) content of carboxyl groups: 30 equivalent/10 6 g or less; (vi) average birefringence: 0.190 or more; (v) yarn tenacity: 8.5 g/d or more; and (vi) value obtained by dividing the difference of birefringence between surface and center of monofilament by average birefringence: 0.555 or less, said polyester fiber further having the following properties when it is heat-treated at constant length at 240° C. for one minute: (a) dry heat shrink when freely heat-treated at 175° for 30 minutes: 3.0% or less, and (b) work loss when the hysteresis loop is measured at a stress between 0.6 g/d and 0.05 g/d under the following conditions length of test sample of 10 inch, strain rate of 0.5 inch/minute and a temperature of 150° C.: 2.0×10 -5 inch-pound/denier or less.
Claim 3
Dependent Claim
20 words
A polyester fiber according to claim 1, wherein the content of carboxyl group is 12 equivalent/10 6 g or less.
Claim 4
Dependent Claim
31 words
A polyester fiber according to claim 1, which is subjected to surface treatment with a compound selected from an epoxy compound and an isocyanate compound in the spinning and drawing steps.
Claim 5
Dependent Claim
16 words
A rubber goods which is reinforced with the polyester fiber as set forth in claim 1.
Claim 6
Dependent Claim
24 words
A rubber goods according to claim 4, wherein the polyester fiber has a content of carboxyl group of 12 equivalent/10 6 g or less.
Claim 7
Dependent Claim
34 words
A rubber goods according to claim 4, wherein the polyester fiber is subjected to surface treatment with a compound selected from an epoxy compound and an isocyanate compound in the spinning and drawing steps.
Claim 8
Dependent Claim
10 words
A rubber goods according claim 4, which is a tire.
Claim 9
Dependent Claim
34 words
A rubber goods according to claim 5, wherein the polyester fiber is subjected to surface treatment with a compound selected from an epoxy compound and an isocyamate compound in the spinning and drawing steps.
Claim 10
Dependent Claim
11 words
A rubber goods according to claim 5, which is a tire.
Claim 11
Dependent Claim
11 words
A rubber goods according to claim 6, which is a tire.
References Cited (Backward Citations)
GB585994A
Cited
US3051212A
Cited
US3665994A
Cited
US3616832A
Cited
JPS5331852A
Cited
US4101525A
Cited
US4195052A
Cited
JPS5557070A
Cited
US4414169A
Cited
JPS55118855A
Cited
US4715418A
Cited
JPS61116816A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-05-08 | 1992-11-07 | 1993-05-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-05-08 | 1996-11-07 | 1997-05-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-05-08 | 2000-11-07 | 2001-05-09 | $7700.00 | Window Closed / Lapsed |