Process for the production of porous ceramics using decomposable polymeric microspheres and the resultant product
Assignee: WASHINGTON, University of
•
Filing: 1986-05-06
•
Granted: 1988-10-11
•
Expires: 2006-05-06
Abstract
Abstract A process for producing porous ceramics with controlled microstructure. Colloidal suspensions of polymeric microspheres of a selected size and shape, and aluminum oxide particles are consolidated to form a compact. The compact is heated to decompose the microspheres to leave pores, and to sinter the compact, to form a porous ceramic body with a plurality of pores preferably substantially the same size and shape, where the pores are substantially spherical and are evenly distributed and noncontiguous throughout the ceramic matrix and with strength comparable to its dense state.
Inventors
- 👤 Birol Sonuparlak
- 👤 Ilhan A. Aksay
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 18:29
CPC Classifications
C; C04; C04B; C04B38/00; C04B38/06; C04B38/063; C04B38/0635; C04B38/0645; C04B38/065; B; B32; B32B; B32B18/00; C04B35/00; C04B35/622; C04B35/64; C04B35/645; C04B38/067; C04B2237/00; C04B2237/30; C04B2237/32; C04B2237/34; C04B2237/343
Claims Analysis
Total Claims: 57
Claim 1
Independent Claim
115 words
A process for preparing a porous ceramic body with controlled microstructure consisting of pores of predetermined size, shape and spatial distribution, comprising the steps of: a. forming a colloidal suspension of polymeric microspheres of substantially the same size and substantially spherical in shape, and particles of a ceramic material in a liquid medium; b. stabilizing the particle-particle interactions between the microspheres and the particles of ceramic material in the colloidal suspension; c. consolidating said colloidal suspension to remove the liquid and to form a compact body; and d. heating said compact body to decompose said microspheres and to sinter said compact body into a porous ceramic body with a plurality of evenly distributed, noncontiguous pores.
Claim 2
Dependent Claim
115 words
A process for preparing a porous ceramic body with controlled microstructure consisting of pores of predetermined size, shape and spatial distribution, comprising the steps of: a. forming a colloidal suspension of polymeric microspheres of substantially the same size and substantially spherical in shape, and particles of a ceramic material in a liquid medium; b. stabilizing the particle-particle interactions between the microspheres and the particles of ceramic material in the colloidal suspension; c. consolidating said colloidal suspension to remove the liquid and to form a compact body; and d. heating said compact body to decompose said microspheres and to sinter said compact body into a porous ceramic body with a plurality of evenly distributed, noncontiguous pores.
Claim 3
Dependent Claim
33 words
The process according to claim 1 wherein said step of heating comprises: a. preheating said compact body to decompose said microspheres; and b. thereafter sintering said compact body into a porous ceramic body.
Claim 4
Dependent Claim
23 words
The process according to claim 1 or 2 wherein said microspheres are in the range of 2 μm to 6 μm in diameter.
Claim 5
Dependent Claim
33 words
The process according to claim 1, wherein said polymeric microspheres comprise a polymer selected from the group consisting of polystyrene, polyvinyldene chloride, polymethyl methacrylate, polystyrene divinylbenzene, polyvinyl toluene, styrene vinyltoluene, and styrene butadiene.
Claim 6
Dependent Claim
12 words
The process according to claim 4 wherein said microspheres comprise polyvinyldene chloride.
Claim 7
Dependent Claim
17 words
The process according to claim 5 wherein said polymeric microspheres are 30 to 60 μm in diameter.
Claim 8
Dependent Claim
12 words
The process according to claim 4 wherein said microspheres comprise polystyrene polymer.
Claim 9
Dependent Claim
17 words
The process according to claim 5 wherein said polystyrene microspheres are 3 to 6 μm in diameter.
Claim 10
Dependent Claim
36 words
The process according to claim 1 wherein said ceramic precursor material is selected from the group consisting of alumina, silicon carbide, boron carbide, silicon nitride, aluminum nitride, zirconium oxide, mullite, cordierite, and glass-ceramics, and combinations thereof.
Claim 11
Dependent Claim
13 words
The process according to claim 9 wherein said ceramic material is alpha alumina.
Claim 12
Dependent Claim
27 words
The process according to claim 10 wherein said alpha alumina is used in the form of a powder having particles with an average diameter of 0.75 μm.
Claim 13
Dependent Claim
21 words
The process according to claim 1 wherein the step of consolidating comprises slip casting said colloidal suspension using a filtering medium.
Claim 14
Dependent Claim
16 words
The process according to claim 12 wherein plaster of paris is used as the filtering medium.
Claim 15
Dependent Claim
25 words
The process according to claim 12 wherein said slip casting comprises casting the colloidal suspension so that said ceramic body comprises a single, porous layer.
Claim 16
Dependent Claim
14 words
A porous ceramic having controlled microstructure formed by the process according to claim 14.
Claim 17
Dependent Claim
12 words
The process according to claim 14 wherein said polymeric microspheres comprise polystyrene.
Claim 18
Dependent Claim
13 words
The process according to claim 14 wherein said ceramic material is alpha alumina.
Claim 19
Dependent Claim
65 words
The process according to claim 12 wherein said slip casting comprises the steps of: a. casting a first layer of pure ceramic material; b. casting a second layer of colloidal suspension containing particles of ceramic material and polymeric microspheres over said first pure ceramic material layer; and, c. applying a third pure ceramic material layer over said second layer to form a multi-layered ceramic body.
Claim 20
Dependent Claim
67 words
The process according to claim 18 wherein said step of casting a second layer of colloidal suspension over said first pure ceramic layer comprises adding said second layer prior to the completion of the drying of said first layer, and said step of applying a third pure ceramic material layer over said second layer comprises adding said third layer prior to the drying of said second layer.
Claim 21
Dependent Claim
15 words
A porous ceramic having a controlled microstructure formed by the process according to claim 18.
Claim 22
Dependent Claim
13 words
The process according to claim 18 wherein said ceramic material is alpha alumina.
Claim 23
Dependent Claim
12 words
The process according to claim 18 wherein said polymeric microspheres comprise polystyrene.
Claim 24
Dependent Claim
17 words
The process according to claim 1 wherein the step of consolidating comprises tape casting said colloidal suspension.
Claim 25
Dependent Claim
17 words
The process according to claim 23 wherein said colloidal suspension further comprises binders, defoamers and wetting agents.
Claim 26
Dependent Claim
75 words
The process according to claim 23 wherein said tape casting comprises the steps of: a. consolidating pure ceramic material into at least one pure ceramic tape; b. consolidating a colloidal suspension containing particles of a ceramic material and polymeric microspheres into at least one mixed ceramic tape; and wherein said process further comprises the steps of: c. stacking said pure ceramic material tapes and mixed tapes in alternating arrangement; and, d. fusing said tapes together.
Claim 27
Dependent Claim
13 words
The process according to claim 25 wherein said ceramic material comprises alpha alumina.
Claim 28
Dependent Claim
13 words
The process according to claim 25 wherein said polymeric microspheres comprise polystyrene polymer.
Claim 29
Dependent Claim
15 words
A porous ceramic having a controlled microstructure formed by the process according to claim 25.
Claim 30
Dependent Claim
20 words
The process according to claim 25 wherein said step of stacking comprises stacking a plurality of pure ceramic tapes together.
Claim 31
Dependent Claim
19 words
The process according to claim 25 wherein said step of stacking comprises stacking a plurality of mixed tapes together.
Claim 32
Dependent Claim
17 words
A porous ceramic having a controlled microstructure formed by the process according to claim 1 or 2.
Claim 33
Dependent Claim
40 words
The process according to claim 1 wherein the step of forming said colloidal suspension comprises stabilizing said microspheres and ceramic particles in the suspension so as to produce pores which are evenly distributed and noncontiguous throughout the ceramic body formed.
Claim 34
Dependent Claim
22 words
The process according to claim 32 wherein the pH of said colloidal suspension is maintained in the range of 2 to 11.
Claim 35
Dependent Claim
18 words
The process according to claim 33, wherein the pH of said colloidal suspension is maintained at approximately 9.5.
Claim 36
Dependent Claim
15 words
The process according to claim 32 wherein a surfactant is added to said colloidal suspension.
Claim 37
Dependent Claim
13 words
The process according to claim 35 wherein said surfactant is an anionic surfactant.
Claim 38
Dependent Claim
19 words
The process according to claim 36 wherein said surfactant is the ammonium salt of polyacrylic acid and citric acid.
Claim 39
Dependent Claim
21 words
The process according to claim 37 wherein the pH of said colloidal suspension is in the range of 7 to 9.
Claim 40
Dependent Claim
14 words
The process according to claim 1 wherein said colloidal suspension is a binary suspension.
Claim 41
Dependent Claim
43 words
The process according to claim 2 wherein said preheating step to decompose said microspheres is performed by heating said compact body in the range of 600° to 1000° C. at a heating rate in the range of 20° to 80° C. per hour.
Claim 42
Dependent Claim
27 words
The process according to claim 40 wherein said polymeric microspheres are decomposed by preheating to 1000° C. at a heating rate of approximately 22.5° C. per hour.
Claim 43
Dependent Claim
40 words
The process according to claim 2 wherein said sintering step comprises heating said compact body to a temperature in the range of 1300° to 1550° C., at a rate in the range of 250° to 750° C. for one hour.
Claim 44
Dependent Claim
25 words
The process according to claim 42 wherein said sintering comprises heating said compact body to 1550° C. at a rate of 254° C. per hour.
Claim 45
Dependent Claim
37 words
The porous ceramic according to claims 15, 20 or 28, wherein said microstructure consists of a plurality of substantially spherical pores of substantially the same size, said pores evenly distributed and noncontiguous throughout the porous ceramic matrix.
Claim 46
Dependent Claim
43 words
A porous ceramic according to claim 15 having a controlled microstructure consisting of a plurality of pores of substantially the same size and shape, said pores evenly distributed and noncontiguous throughout the porous ceramic matrix, and having strength comparable to its dense state.
Claim 47
Dependent Claim
16 words
The ceramic according to claim 45 wherein said pores are substantially the same size and shape.
Claim 48
Dependent Claim
12 words
The ceramic according to claim 45 wherein the pores are substantially spherical.
Claim 49
Dependent Claim
81 words
The porous ceramic according to claim 45 formed by a process comprising: a. forming a colloidal suspension of polymeric microspheres of a predetermined size and shape, and particles of a ceramic material in a liquid medium; b. consolidating said colloidal suspension to remove the liquid and to form a compact body; and c. heating said compact body to decompose said microspheres and to sinter said compact body into a porous ceramic body with a plurality of evenly distributed and noncontiguous pores.
Claim 50
Dependent Claim
22 words
The porous ceramic according to claim 48 wherein the step of consolidating comprises slip casting said colloidal suspension using a filtering medium.
Claim 51
Dependent Claim
27 words
The porous ceramic according to claim 49 wherein said slip casting comprises casting the colloidal suspension so that said compact body comprises a single, porous unit layer.
Claim 52
Dependent Claim
67 words
The porous ceramic according to claim 50 wherein said slip casting comprises the steps of: a. casting a first layer of pure ceramic material; b. casting a second layer of colloidal suspension containing particles of ceramic material and polymeric microspheres over said pure ceramic material first layer; and, c. applying a third pure ceramic material layer over said second porous layer to form a multi-layered ceramic body.
Claim 53
Dependent Claim
68 words
The porous ceramic acording to claim 50 wherein said step of casting a second layer of colloidal suspension over said first pure ceramic layer comprises adding said second layer prior to the completion of the drying of said first layer, and said step of applying a third pure ceramic material layer over said second layer comprises adding said third layer prior to the drying of said second layer.
Claim 54
Dependent Claim
18 words
The porous ceramic according to claim 51 wherein the step of consolidating comprises tape casting said colloidal suspension.
Claim 55
Dependent Claim
74 words
The porous ceramic according to claim 53 wherein said tape casting comprises the steps of: a. consolidating pure ceramic material into at least one pure ceramic tape; b. consolidating a colloidal suspension containng particles of a ceramic material and polymeric microspheres into at least one mixed tape; and wherein said process further comprises the steps of: c. stacking said pure ceramic tapes and mixed tapes in alternating arrangement; and, d. fusing said tapes together.
Claim 56
Dependent Claim
20 words
The porous ceramic according to claim 52 wherein said step of stacking comprises stacking a plurality of pure ceramic tapes.
Claim 57
Dependent Claim
20 words
The porous ceramic according to claim 52 wherein said step of stacking comprises stacking a plurality of mixed tapes together.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-10-11 | 1992-04-11 | 1992-10-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-10-11 | 1996-04-11 | 1996-10-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-10-11 | 2000-04-11 | 2000-10-11 | $7700.00 | Window Closed / Lapsed |