Process for the preparation of reflective pyrolytic graphite

Claim 2

A process for preparing reflective graphite having improved reflectance which comprises the steps of (a) preparing pyrolytic graphite by depositing carbon by the chemical vapor deposition technique on a suitable support from a short chain hydrocarbon at a temperature of about 1850° C. to 2250° C. and a pressure of about 1 to 3 torr until the film is at least 1 mm thick and cooling, to room temperature, (b) positioning said support and pyrolytic graphite in a furnace, evacuating said furnace and slowly increasing the temperature of about 700°-1000° C. while maintaining a pressure of about 1 torr, (c) increasing the pressure in the furnace to 5 to 10 torr while increasing the temperature to about 2600° C. to 3300° C., (d) maintaining said temperature and pressure for about 10 minutes to 2 hours, and (e) cooling and recovering the reflective graphite product.

Claim 3

The process according to claim 1, wherein the support is selected from the group consisting of graphite, tungsten metal and hafnium metal.

Claim 4

The process according to claim 1, wherein the hydrocarbon is selected from the group consisting of methane, ethane, propane and natural gas.

Claim 5

The process according to claim 1 wherein the pyrolytic graphite film is about 0.1 to 0.6 cm in thickness.

Claim 6

The process according to claim 1 wherein the temperature is increased to about 900° C. at the rate of about 300° C. per hour in step (a) and about 200° C. per hour in step (b).

Claim 7

The process according to claim 1 wherein the temperature is increased to 2150° to 2160° C. in step (a).

Claim 8

The process according to claim 1 wherein the temperature is increased to about 2900° C. to 2950° C. in step (c).

Claim 9

The process according to claim 1 wherein the methane is fed to the furnace at a rate of about 36 standard cubic feet per hour in step (a).

Claim 10

The process according to claim 1 wherein the furnace is cooled in a nitrogen atmosphere in step (e).

Claim 11

A process for preparing reflective graphite having improved reflectance on a graphite, tungsten or hafnium substrate which comprises the steps of (a) positioning the said substrate in a furnace chamber, (b) evacuating the furnace chamber to a pressure of about 1 mm, (c) heating the furnace to about 2150° C. at a rate of about 300° C. per hour, (d) passing methane into said furnace chamber at a rate of about 36 standard cubic feet per hour and adjusting the pressure in said furnace chamber to about 4.8 to 5.2 torr, (e) maintaining the temperature at about 2150° C. to 2160° C., the methane flow at about 36 standard cubic feet per hour and the pressure at about 4.8 to 5.2 torr until pyrolytic graphite is deposited to a thickness of 0.1 to 0.6 centimeters, (f) discontinuing the methane flow and heating and passing nitrogen through the furnace until the temperature in the furnace is at room temperture and the pressure is at atmospheric, and recovering the substrate with the pyrolytic graphite deposited thereon, and (g) annealing said pyrolytic graphite structure by (a) evacuating said furnace to a pressure of about 1 torr, (b) heating the furnace chamber to about 900° C. at a rate of about 200° C. per hour, (c) increasing the pressure in said furnace chamber by passing nitrogen into the furnace until the pressure reaches about 5 to 10 torr, (d) maintaining the pressure at 5 to 10 torr while increasing the temperature to about 2850° to 2950° C. and maintaining the temperature for about 1 hour, and (e) cooling said furnace to room temperature and recovering the reflective graphite structure.

Claim 12

A process for preparing reflective graphite having improved reflectance on a graphite, tungsten or hafnium substrate which comprises the steps of (a) positioning the said substrate in a furnace chamber, (b) evacuating the furnace chamber to a pressure of about 1 mm, (c) heating the furnace to about 2150° C. at a rate of about 300° C. per hour, (d) passing methane into said furnace chamber at a rate of about 36 standard cubic feet per hour and adjusting the pressure in said furnace chamber to about 4.8 to 5.2 torr, (e) maintaining the temperature at about 2150° C. to 2160° C., the methane flow at about 36 standard cubic feet per hour and the pressure at about 4.8 to 5.2 torr until pyrolytic graphite is deposited to a thickness of 0.1 to 0.6 centimeters, (f) discontinuing the methane flow and heating and passing nitrogen through the furnace until the temperature in the furnace is at room temperture and the pressure is at atmospheric, and recovering the substrate with the pyrolytic graphite deposited thereon, and (g) annealing said pyrolytic graphite structure by (a) evacuating said furnace to a pressure of about 1 torr, (b) heating the furnace chamber to about 900° C. at a rate of about 200° C. per hour, (c) increasing the pressure in said furnace chamber by passing nitrogen into the furnace until the pressure reaches about 5 to 10 torr, (d) maintaining the pressure at 5 to 10 torr while increasing the temperature to about 2850° to 2950° C. and maintaining the temperature for about 1 hour, and (e) cooling said furnace to room temperature and recovering the reflective graphite structure.

Claim 13

A process for impregnating rigidized fabric or felt with reflective graphite which comprises the steps of: (a) positioning said fabric or felt in a furnace chamber and evacuating said chamber to a pressure of about 1 torr, (b) evacuating the furnace chamber to about 900° C. at a rate of about 300° C. per hour, (c) passing hydrogen into said furnace chamber at a rate of about 15 standard cubic feet per hour while heating said furnace chamber, (d) when the temperature in said furnace reaches about 1100° C. passing methane into said furnace at a rate of about 30 standard cubic feet per minute, and adjusting the pressure to 2 torr, (e) maintaining the methane flow at about 30 standard cubic feet per hour, the hydrogen flow at about 5 standard cubic feet per minute, the pressure at about 2 torr and the temperature at about 1100° to 1110° C. for a period of 24 hours, (f) after 24 hours discontinuning methane flow while maintaining hydrogen flow and increasing the furnace temperature to about 2150° C. at a rate of about 200° C. per hour, (g) after the temperature reaches about 2150° C. discontinuing hydrogen flow and passing methane into said furnace at a rate of about 36 standard cubic feet per minute, (h) adjusting the pressure in said furnace to about 4.8 to 5.2 torr and maintaining the temperature at about 2140° to 2160° C., the methane flow at about 36 standard cubic feet per hour until 0.1 to 0.6 centimeters of graphite is impregnated into said cloth or felt, and (i) discontinuing methane flow and heating and allowing said furnace chamber to cool to room temperature and recovering the pyrolytic graphite impregnated fabric or felt product, annealing said pyrolytic graphite impregnated fabric or felt by (a) evacuating said furnace to a pressure of about 1 torr, (b) heating said furnace chamber to about 900° C. at a rate of about 200° C. per hour, (c) increasing the pressure in said furnace to about 5 to 10 torr while continuing to heat said furnace to about 2900° to 2950° C., (d) maintaining the furnace temperature at about 2900° to 2950° C. and furnace pressure at about 5 to 10 torr for about 1 hour; and (e) allowing the furnace to cool to room temperature and atmospheric pressure and recovering the reflective graphite impregnated fabric or felt product.

Claim 14

A process for impregnating rigidized fabric or felt with reflective graphite which comprises the steps of: (a) positioning said fabric or felt in a furnace chamber and evacuating said chamber to a pressure of about 1 torr, (b) evacuating the furnace chamber to about 900° C. at a rate of about 300° C. per hour, (c) passing hydrogen into said furnace chamber at a rate of about 15 standard cubic feet per hour while heating said furnace chamber, (d) when the temperature in said furnace reaches about 1100° C. passing methane into said furnace at a rate of about 30 standard cubic feet per minute, and adjusting the pressure to 2 torr, (e) maintaining the methane flow at about 30 standard cubic feet per hour, the hydrogen flow at about 5 standard cubic feet per minute, the pressure at about 2 torr and the temperature at about 1100° to 1110° C. for a period of 24 hours, (f) after 24 hours discontinuning methane flow while maintaining hydrogen flow and increasing the furnace temperature to about 2150° C. at a rate of about 200° C. per hour, (g) after the temperature reaches about 2150° C. discontinuing hydrogen flow and passing methane into said furnace at a rate of about 36 standard cubic feet per minute, (h) adjusting the pressure in said furnace to about 4.8 to 5.2 torr and maintaining the temperature at about 2140° to 2160° C., the methane flow at about 36 standard cubic feet per hour until 0.1 to 0.6 centimeters of graphite is impregnated into said cloth or felt, and (i) discontinuing methane flow and heating and allowing said furnace chamber to cool to room temperature and recovering the pyrolytic graphite impregnated fabric or felt product, annealing said pyrolytic graphite impregnated fabric or felt by (a) evacuating said furnace to a pressure of about 1 torr, (b) heating said furnace chamber to about 900° C. at a rate of about 200° C. per hour, (c) increasing the pressure in said furnace to about 5 to 10 torr while continuing to heat said furnace to about 2900° to 2950° C., (d) maintaining the furnace temperature at about 2900° to 2950° C. and furnace pressure at about 5 to 10 torr for about 1 hour; and (e) allowing the furnace to cool to room temperature and atmospheric pressure and recovering the reflective graphite impregnated fabric or felt product.