Process for improving polymer fiber properties and fibers produced thereby
Assignee: Intera Technologies Inc
•
Filing: 1982-09-29
•
Granted: 1988-05-10
•
Expires: 2002-09-29
Abstract
Abstract A method is provided for treating polyester, and acrylic polymer fibers or fibrous structures made thereof to permanently improve the antistatic, hygroscopic, dye receptive, soil release, inter-fiber adhesion and bonding properties of the fibers and structures. The method involves contacting the fibers with an aqueous solution containing at least one unsaturated monomer and having an acid pH and a temperature between about 60 DEG C. and about 100 DEG C. After allowing the solution to uniformly disperse among the fibers, so that the monomer intimately contacts the fiber surfaces, polymerization of the monomer on the fiber surfaces is initiated by a polymerization initiator for the monomer, and the polymerization is continued for a sufficient time to allow substantial graft polymerization of the monomer on the fibers to modify the surface properties of the fibers. The fibers are preferably scoured prior to the treatment process, and after polymerization the fibers are rinsed to remove acid and excess homopolymer prior to dyeing and/or further processing of the fibers. The fibers may be in the form of knitted, woven or nonwoven fabrics, and may include mixtures of fibers such as acrylic yarns and nylon filaments or polyester and cotton staple fiber blends.
Inventors
- 👤 Michael E. Dyer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 15:10
CPC Classifications
D; D06; D06M; D06M14/00; D06M14/08; D06M14/12; D06M14/14; D06M14/10
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
129 words
A method of treating polymer fibers selected from the group consisting of polyester and arcylic polymers to improve the hygroscopic, dye receptive and other surface properties of the fibers, comprising the steps of: (a) contacting the fibers in the absence of a polymerization initiator with an aqueous solution heated to a temperature between about 60°-100° C., containing at least one unsaturated monomer under acidic conditions, and agitating said solution for about 10 minutes to allow uniform disposal and intimate contact of the monomer with the fiber surfaces; (b) thereafter initiating polymerization of the monomer on the fibers by means of a polymerization initiator for the monomer; and (c) continuing the polymerization of the monomer on the fiber until substantial polymerization has occurred to modify surface properties of the fibers.
Claim 2
Independent Claim
129 words
A method of treating polymer fibers selected from the group consisting of polyester and arcylic polymers to improve the hygroscopic, dye receptive and other surface properties of the fibers, comprising the steps of: (a) contacting the fibers in the absence of a polymerization initiator with an aqueous solution heated to a temperature between about 60°-100° C., containing at least one unsaturated monomer under acidic conditions, and agitating said solution for about 10 minutes to allow uniform disposal and intimate contact of the monomer with the fiber surfaces; (b) thereafter initiating polymerization of the monomer on the fibers by means of a polymerization initiator for the monomer; and (c) continuing the polymerization of the monomer on the fiber until substantial polymerization has occurred to modify surface properties of the fibers.
Claim 3
Dependent Claim
27 words
A method according to claim 1 wherein the pH of the aqueous solution is established and maintained below about 7 by addition of acid in step (a).
Claim 4
Dependent Claim
27 words
The method of claim 2 wherein said acid is selected from the group consisting of formic, hydrochloric, phosphoric, sulfuric, nitric, acetic, oxalic, tartaric, monochloroacetic, dichloroacetic and trichloroacetic.
Claim 5
Dependent Claim
25 words
A method according to claim 1 wherein the pH of the aqueous solution is established and maintained below about 7 by using an acidic monomer.
Claim 6
Dependent Claim
37 words
A method according to claim 1 wherein the pH of the solution is maintained below about 7 and the temperature of the solution is maintained between about 60° C. and 100° C. during steps (b) and (c).
Claim 7
Dependent Claim
19 words
A method according to claim 1 wherein the polymerization is continued for a period not exceeding about 30 minutes.
Claim 8
Dependent Claim
17 words
A method according to claim 1 wherein said fibers are scoured and rinsed prior to step (a).
Claim 9
Dependent Claim
16 words
A method according to claim 1 wherein said fibers are rinsed and dyed after step (c).
Claim 10
Dependent Claim
25 words
A method according to claim 1 wherein the solution is heated in step (a) to a temperature of about 70° C. to about 90° C.
Claim 11
Dependent Claim
27 words
A method according to claim 1 wherein step (c) is continued for about 10 minutes followed by draining the solution and rinsing the fibers with fresh water.
Claim 12
Dependent Claim
20 words
A method according to claim 1 wherein the fibers are in the form of a knitted, woven or non-woven fabric.
Claim 13
Dependent Claim
18 words
A method according to claim 11 wherein said fabric comprises a mixture of acrylic yarn and nylon filaments.
Claim 14
Dependent Claim
21 words
A method according to claim 11 wherein said fabric comprises yarns which are a blend of polyester and cotton staple fibers.
Claim 15
Dependent Claim
120 words
A method according to claim 1 wherein the fibers are treated as follows: (a) immersing said fibers in an aqueous solution at about 70° C. containing about 0.01 weight percent hydrochloric acid, about 0.03 weight percent formic acid and about 0.04 weight percent N, N'-methylene-bis-acrylamide, rapidly raising the temperature of the solution to about 85° C. and agitating the fibers in the solution for about 10 minutes; (b) thereafter adding about 0.02 weight percent potasium persulfate to the solution to initiate polymerization; and (c) continuing the polymerization for about 10 minutes, followed by draining the solution from the fibers and rinsing the fibers in water, all weight percents being on the basis of percentage by weight of the total solution.
Claim 16
Dependent Claim
28 words
The method of claim 1 which further comprises rinsing said fibers or fibrous structures after substantial polymerization has occurred to neutralize the pH and remove any excess homopolymers.
Claim 17
Dependent Claim
22 words
The method of claim 1 wherein said initiator is selected from the group consisting of peroxides, persulfates, acids and ceric salt compounds.
Claim 18
Dependent Claim
31 words
The method of claim 1 wherein said monomer is selected from the group consisting of N,N'-methylene-bisacrylamide; N,N'-(1,2 dihydroxyethylene)-bis-acrylamide; salts of N,N'-methylene-bis-acrylamide; salts of N,N'-(1,2 dihydroxyethylene)-bis-acrylamide; acrylic acid, 2-propyn-1-ol; crotonic acid and.
Claim 19
Dependent Claim
30 words
The method of claim 1 wherein the amount of said monomer is between about 0.01 weight percent and about 1.0 weight percent based on the total weight of said solution.
Claim 20
Dependent Claim
30 words
The method of claim 1 wherein the amount of said monomer is between about 0.02 weight percent and about 0.5 weight percent based on the total weight of said solution.
Claim 21
Dependent Claim
20 words
The method of claim 1 wherein said polymerization has a duration of between about 0.5 minutes and about 2.0 hours.
Claim 22
Dependent Claim
20 words
The method of claim 1 wherein said polymerization has a duration of between about 1.0 minute and about 30 minutes.
Claim 23
Dependent Claim
16 words
The method of claim 1 wherein said solution is agitated during steps (a), (b) and (c).
Claim 24
Dependent Claim
16 words
The improved polymer fiber product produced by the method of claims 11, 12, 13, 14, 15.
References Cited (Backward Citations)
US2732317A
Cited
CA628385A
Cited
US2764504A
Cited
GB770766A
Cited
US2784052A
Cited
US3005730A
Cited
US3115418A
Cited
US3252880A
Cited
GB805513A
Cited
US2956899A
Cited
GB845690A
Cited
GB901038A
Cited
US3092512A
Cited
US2959565A
Cited
US3083118A
Cited
US3313591A
Cited
US3099631A
Cited
US3046078A
Cited
US3097185A
Cited
GB872132A
Cited
US3236584A
Cited
US3202541A
Cited
US3218117A
Cited
GB1017861A
Cited
US3216781A
Cited
US3909195A
Cited
US3291560A
Cited
GB1067494A
Cited
US3278639A
Cited
US3297471A
Cited
US3687878A
Cited
GB1128696A
Cited
US3514385A
Cited
GB1189501A
Cited
GB1225275A
Cited
GB1279709A
Cited
US3598514A
Cited
GB1311542A
Cited
JPS4961500A
Cited
JPS4971299A
Cited
JPS5030197A
Cited
US4043753A
Cited
US3995998A
Cited
US4063887A
Cited
US4135877A
Cited
JPS5411395A
Cited
US4238193A
Cited
JPS54134112A
Cited
JPS5536334A
Cited
JPS5540815A
Cited
US4227882A
Cited
US4438151A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-05-10 | 1991-11-09 | 1992-05-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-05-10 | 1995-11-09 | 1996-05-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-05-10 | 1999-11-09 | 2000-05-10 | $7700.00 | Window Closed / Lapsed |