Optical disc base plate having a primer layer formed of an ultraviolet-cured resin composition
Assignee: Hitachi Ltd
•
Filing: 1985-11-08
•
Granted: 1988-03-08
•
Expires: 2005-11-08
Abstract
Abstract An optical disc obtained by placing in parallel two optical disc base plates comprising a transparent substrate, a primer layer formed thereon, and a recording film formed thereon, or the transparent substrate and the primer layer being integrated into one body, wherein the primer layer is made from a special resin composition, is excellent in properties, particularly in moisture resistance.
Inventors
- 👤 Tetsuo Tajima
- 👤 Hiroaki Miwa
- 👤 Ryoichi Sudo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 12:41
CPC Classifications
G; G11; G11B; G11B7/00; G11B7/24; G11B7/241; G11B7/252; G11B7/253; G11B7/2533; G11B7/2535; C; C08; C08F; C08F20/00; C08F20/02; C08F20/10; C08F20/26; C08F20/30; G11B7/2531; G11B7/256; G11B7/242; G11B7/243; G11B7/2433; G11B7/2534; Y; Y10; Y10S; Y10S430/00; Y10S430/146
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
105 words
An optical disc base plate comprising a transparent substrate, a primer layer formed on the substrate and having depressions and protuberances for carrying information signals, and a recording film formed on the primer layer, said primer layer being obtained by curing with ultraviolet light irradiation an ultraviolet-curable resin composition comprising at least one compound selected from the compounds of the formulae: ##STR8## wherein R 1 is hydrogen or a halogen; R 2 is an alkyl group having 1 to 12 carbon atoms; R 3 is hydrogen or a methyl group; m and n are independently an integer of 1 to 4, and a photopolymerization initiator.
Claim 2
Dependent Claim
105 words
An optical disc base plate comprising a transparent substrate, a primer layer formed on the substrate and having depressions and protuberances for carrying information signals, and a recording film formed on the primer layer, said primer layer being obtained by curing with ultraviolet light irradiation an ultraviolet-curable resin composition comprising at least one compound selected from the compounds of the formulae: ##STR8## wherein R 1 is hydrogen or a halogen; R 2 is an alkyl group having 1 to 12 carbon atoms; R 3 is hydrogen or a methyl group; m and n are independently an integer of 1 to 4, and a photopolymerization initiator.
Claim 3
Dependent Claim
40 words
An optical disc base plate according to claim 1, wherein the photopolymerization initiator is used in an amount of 0.01 to 5 parts by weight based on 100 parts by weight of the compounds of the formulae (1) to (4).
Claim 4
Dependent Claim
50 words
An optical disc base plate according to claim 1, wherein the compound of the formula (1) is ##STR9## the compound of the formula (2) is ##STR10## the compound of the formula (3) is ##STR11## or a mixture thereof, the compound of the formula (4) is ##STR12## or a mixture thereof.
Claim 5
Dependent Claim
98 words
An optical disc base plate comprising a transparent resin substrate having depressions and protuberances for carrying information signals, and a recording film formed on the resin substrate, said resin substrate being obtained by curing with ultraviolet light irradiation a ultraviolet-curable resin composition comprising at least one compound selected from the compounds of the formulae: ##STR13## wherein R 1 is hydrogen or a halogen; R 2 is an alkyl group having 1 to 12 carbon atoms; R 3 is hydrogen or a methyl group; m and n are independently an integer of 1 to 4, and a photopolymerization initiator.
Claim 6
Dependent Claim
98 words
An optical disc base plate comprising a transparent resin substrate having depressions and protuberances for carrying information signals, and a recording film formed on the resin substrate, said resin substrate being obtained by curing with ultraviolet light irradiation a ultraviolet-curable resin composition comprising at least one compound selected from the compounds of the formulae: ##STR13## wherein R 1 is hydrogen or a halogen; R 2 is an alkyl group having 1 to 12 carbon atoms; R 3 is hydrogen or a methyl group; m and n are independently an integer of 1 to 4, and a photopolymerization initiator.
Claim 7
Dependent Claim
40 words
An optical disc base plate according to claim 4, wherein the photopolymerization initiator is used in an amount of 0.01 to 5 parts by weight based on 100 parts by weight of the compounds of the formulae (1) to (4).
Claim 8
Dependent Claim
50 words
An optical disc base plate according to claim 4, wherein the compound of the formula (1) is. ##STR14## the compound of the formula (2) is ##STR15## the compound of the formula (3) is ##STR16## or a mixture thereof, the compound of the formula (4) is ##STR17## or a mixture thereof.
Claim 9
Dependent Claim
28 words
An optical disc base plate according to claim 1, wherein the ultraviolet-curable resin composition is cured by irradiation of ultraviolet light at 50 to 400 mW/cm 2 .
Claim 10
Dependent Claim
28 words
An optical disc base plate according to claim 4, wherein the ultraviolet-curable resin composition is cured by irradiation of ultraviolet light at 50 to 400 mW/cm 2 .
Claim 11
Dependent Claim
77 words
An optical disc base plate according to claim 1, wherein the ultraviolet-curable resin composition further comprises at least one monomer selected from the group consisting of lauryl acrylate, lauryl methacrylate, tridecyl methacrylate, isobornyl acrylate, isobornyl methacrylate, neopenthyl glycol diacrylate, neopentyl gylcol dimethacrylate, trimethylolethane triacrylate, trimethylolethane trimethacrylate, trimethylolpropane triacrylate, trimethylolpropane trimethacrylate, 1,6-hexanediol dimethacrylate, and 1,10-decanediol dimethacrylate, in an amount of 0 to 40 parts by weight based on 100 parts by weight of the at least one compound.
Claim 12
Dependent Claim
55 words
An optical disc base plate according to claim 9, wherein said ultraviolet-curable resin composition further comprises a silane coupling agent selected from the group consisting of γ-acryloxypropyltrimethoxysilane, γ-methacryloxypropyltrimethoxysilane, vinyltrimethoxysilane, vinyltriethoxysilane, and N-β-(N-vinylbenzylamino)ethyl-γ-aminopropyltrimethoxysilane monohydrogenchloride in an amount of 0 to 6.0 parts by weight based on 100 parts by weight of the at least one compound.
Claim 13
Dependent Claim
77 words
An optical disc base plate according to claim 4, wherein the ultraviolet-curable resin composition further comprises at least one monomer selected from the group consisting of lauryl acrylate, lauryl methacrylate, tridecyl methacrylate, isobornyl acrylate, isobornyl methacrylate, neopenthyl glycol diacrylate, neopentyl gylcol dimethacrylate, trimethylolethane triacrylate, trimethylolethane trimethacrylate, trimethylolpropane triacrylate, trimethylolpropane trimethacrylate, 1,6-hexanediol dimethacrylate, and 1,10-decanediol dimethacrylate, in an amount of 0 to 40 parts by weight based on 100 parts by weight of the at least one compound.
Claim 14
Dependent Claim
55 words
An optical disc base plate according to claim 11, wherein said ultraviolet-curable resin composition further comprises a silane coupling agent selected from the group consisting of γ-acryloxypropyltrimethoxysilane, γ-methacryloxypropyltrimethoxysilane, vinyltrimethoxysilane, vinyltriethoxysilane, and N-β-(N-vinylbenzylamino)ethyl-γ-aminopropyltrimethoxysilane monohydrogenchloride in an amount of 0 to 6.0 parts by weight based on 100 parts by weight of the at least one compound.
Claim 15
Dependent Claim
27 words
An optical disc base plate according to claim 3, wherein said primer layer is obtained by curing with ultraviolet light irradiation the compound of the formula (E).
Claim 16
Dependent Claim
27 words
An optical disc base plate according to claim 3, wherein said primer layer is obtained by curing with ultraviolet light irradiation the compound of the formula (F).
Claim 17
Dependent Claim
27 words
An optical disc base plate according to claim 6, wherein said primer layer is obtained by curing with ultraviolet light irradiation the compound of the formula (E).
Claim 18
Dependent Claim
27 words
An optical disc base plate according to claim 6, wherein said primer layer is obtained by curing with ultraviolet light irradiation the compound of the formula (F).
References Cited (Backward Citations)
US3520683A
Cited
US4199421A
Cited
JPS56148705A
Cited
US4434429A
Cited
JPS6045952A
Cited
JPS6127946A
Cited
DE3505355A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-03-08 | 1991-09-07 | 1992-03-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-03-08 | 1995-09-07 | 1996-03-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-03-08 | 1999-09-07 | 2000-03-08 | $7700.00 | Window Closed / Lapsed |