Abstract
Abstract A method of making a catalyst composition comprising an activated alumina coating stabilized against thermal degradation includes applying a coating of alumina having one or more platinum group metal catalytic components dispersed thereon onto a carrier substrate and calcining the coating. The calcined coating is then impregnated with a solution of a thermal stabilizer-precursor and calcined again to provide a thermal stabilizer in the alumina. Bulk ceria, optionally an aluminum-stabilized bulk ceria, may also be added to the composition, preferably at specified minimum levels, including a high purity bulk ceria on which one or more non-rhodium platinum group metal catalytic components, e.g., platinum, optionally, are dispersed. A separate aspect of the invention provides for a method of making a catalyst composition including dispersing one or more platinum group metal catalytic components on an activated alumina and calcining the combined alumina and platinum group metal catalytic components. The steps are carried out under limited acidification conditions whereby at least minimum dispersions of the platinum group metal catalytic components are attained. The invention also provides for catalyst compositions resulting from either or both the foregoing methods.
Inventors
- 👤 Chung-Zong Wan
- 👤 Joseph C. Dettling
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 18:03
CPC Classifications
B; B01; B01D; B01D53/00; B01D53/34; B01D53/92; B01D53/94; B01D53/9445; B01D53/945; B01J; B01J21/00; B01J21/02; B01J21/04; B01J23/00; B01J23/38; B01J23/40; B01J23/54; B01J23/56; B01J23/63; B01J37/00; B01J37/02; B01J37/024; B01J37/0242; F; F02; F02B; F02B1/00; F02B1/02; F02B1/04; Y; Y02; Y02T; Y02T10/00; Y02T10/10; Y02T10/12
Claims Analysis
Total Claims: 62
Claim 1
Independent Claim
88 words
A method of making a catalyst composition comprising a platinum group metal catalytic component and an activated alumina stabilized against thermal degradation, the method comprising: (a) applying a coating of activated alumina to a carrier substrate; (b) calcining the resultant alumina-coated substrate to provide a calcined coating of activated alumina thereon; (c) dispersing one or more platinum group metal components on the activated alumina; (d) after step (c), dispersing a stabilizer-precursor onto the calcining coating on the carrier; and (e) calcining the coating having the stabilizer-precursor dispersed thereon.
Claim 2
Independent Claim
88 words
A method of making a catalyst composition comprising a platinum group metal catalytic component and an activated alumina stabilized against thermal degradation, the method comprising: (a) applying a coating of activated alumina to a carrier substrate; (b) calcining the resultant alumina-coated substrate to provide a calcined coating of activated alumina thereon; (c) dispersing one or more platinum group metal components on the activated alumina; (d) after step (c), dispersing a stabilizer-precursor onto the calcining coating on the carrier; and (e) calcining the coating having the stabilizer-precursor dispersed thereon.
Claim 3
Dependent Claim
28 words
The method of claim 1 including dispersing the stabilizer-precursor onto the calcined coating in step (d) by impregnating the calcined coating with an aqueous solution of a stabilizer-precursor.
Claim 4
Independent Claim
135 words
A method of making a catalyst composition comprising a platinum group metal catalytic component and an activated alumina stabilized against thermal degradation, the method comprising: (a) dispersing one or more platinum group metal catalytic components on an activated alumina; (b) combining a solid, particulate ceria with the activated alumina to form an alumina-ceria mixture; (c) applying a coating of the alumina-ceria mixture to a carrier substrate; (d) calcining the substrate coated with the alumina-ceria mixture to provide thereon an activated alumina-containing calcined coating; (e) after step (d), impregnating the calcined coating on the carrier with a solution of a stabilizer-precursor which upon calcination yields a stabilizer chosen from the group consisting of rare earth metal oxides, alkaline earth metal oxides, titania, zirconia, hafnia, silicon dioxide and mixtures thereof; and (f) calcining the stabilizer-precursor impregnated coating.
Claim 5
Independent Claim
135 words
A method of making a catalyst composition comprising a platinum group metal catalytic component and an activated alumina stabilized against thermal degradation, the method comprising: (a) dispersing one or more platinum group metal catalytic components on an activated alumina; (b) combining a solid, particulate ceria with the activated alumina to form an alumina-ceria mixture; (c) applying a coating of the alumina-ceria mixture to a carrier substrate; (d) calcining the substrate coated with the alumina-ceria mixture to provide thereon an activated alumina-containing calcined coating; (e) after step (d), impregnating the calcined coating on the carrier with a solution of a stabilizer-precursor which upon calcination yields a stabilizer chosen from the group consisting of rare earth metal oxides, alkaline earth metal oxides, titania, zirconia, hafnia, silicon dioxide and mixtures thereof; and (f) calcining the stabilizer-precursor impregnated coating.
Claim 6
Dependent Claim
31 words
The method of claim 3 including combining said one or more platinum group metal components with the alumina prior to applying the alumina-ceria mixture to the carrier substrate in step (c).
Claim 7
Dependent Claim
63 words
The method of claim 4 wherein said one or more platinum group catalytic compounds comprise at least one rhodium compound and at least one compound of a platinum group metal other than rhodium and wherein said compound of a platinum group metal other than rhodium is combined with the ceria prior to applying the alumina-ceria mixture to the carrier substrate in step (c).
Claim 8
Independent Claim
30 words
The method of any one of claims 1, 2, 3, 4, and 5 wherein the calcining steps are carried out at a temperature of not more than about 600° C.
Claim 9
Dependent Claim
22 words
The method of claim 6 wherein the calcining steps are carried out at a temperature of not more than about 500° C.
Claim 10
Dependent Claim
22 words
The method of claim 6 wherein the calcining steps are carried out at a temperature of not more than about 350° C.
Claim 11
Dependent Claim
14 words
The method of claim 6 wherein the calcining steps are carried out in air.
Claim 12
Dependent Claim
14 words
The method of claim 8 wherein the calcining steps are carried out in air.
Claim 13
Independent Claim
28 words
The method of any one of claims 1, 2, 3, 4 and 5 wherein the activated alumina which is impregnated with the stabilizer-precursor is an unstabilized activated alumina.
Claim 14
Independent Claim
67 words
The method of any one of claims 1, 2, 3, 4 and 5 including the step of, subsequent to the first calcination but prior to the second, impregnating the calcined coating with an aqueous solution of a stabilizer-precursor selected from the group consisting of one or more of alkaline earth metal oxide precursors, silicon dioxide precursors, rare earth metal oxide precursors and Group IVB metal oxide precursors.
Claim 15
Dependent Claim
16 words
The method of claim 12 wherein the stabilizer-precursor comprises a barium compound and a lanthanum compound.
Claim 16
Independent Claim
27 words
The method of any one of claims 1, 2, 3, 4 or 5 wherein said one or more platinum group metal catalytic component comprises a platinum component.
Claim 17
Independent Claim
27 words
The method of any one of claims 1, 2, 3, 4 or 5 wherein said one or more platinum group metal catalytic components comprises a palladium component.
Claim 18
Independent Claim
31 words
The method of any one of claims 1, 2, 3, 4 or 5 wherein said one or more platinum group metal catalytic components comprise a platinum component and a palladium component.
Claim 19
Independent Claim
31 words
The method of any one of claims 1, 2, 3, 4 or 5 wherein said one or more platinum group metal catalytic components comprise a palladium component and a rhodium component.
Claim 20
Independent Claim
31 words
The method of any one of claims 1, 2, 3, 4 or 5 wherein said one or more platinum group metal catalytic components comprise a palladium component and a rhodium component.
Claim 21
Dependent Claim
36 words
The method of claim 1 or claim 2 including combining said one or more platinum group metal catalytic components with the activated alumina prior to applying catalytic metal components and activated alumina to the carrier substrate.
Claim 22
Dependent Claim
52 words
The method of claim 19 including combining the platinum group metal catalytic components with the activated alumina by contacting the activated alumina with one or more solutions comprising a liquid and one or more compounds of the metals of the platinum group metal catalytic components, said compounds being soluble in said liquid.
Claim 23
Dependent Claim
14 words
The method of claim 3 wherein the solid, particulate ceria comprises an aluminum-stabilized ceria.
Claim 24
Dependent Claim
36 words
The method of claim 21 wherein the aluminum-stabilized ceria contains from about 0.05 to about 10 weight percent of aluminum, measured as Al 2 O 3 , based on the total weight of the aluminum-stabilized ceria.
Claim 25
Dependent Claim
46 words
The method of claim 3 or claim 22 wherein rare earth metal oxide constituents other then CeO 2 are also applied to the substrate, the ceria comprising at least 90 weight percent, measured as CeO 2 , of the total rare earth metal oxide constituents applied.
Claim 26
Dependent Claim
45 words
The method of claim 3 or claim 22 wherein rare earth metal oxide constituents other than CeO 2 are also applied to the substrate, the ceria comprising at least 95 weight percent, measured as CeO 2 , of total rare earth metal oxide constituents applied.
Claim 27
Dependent Claim
46 words
The method of claim 3 or claim 22 wherein rare earth metal oxide constituents other that CeO 2 are also applied to the substrate, the ceria comprising at least 99 weight percent, measured as CeO 2 , or the total rare earth metal oxide constituents applied.
Claim 28
Independent Claim
68 words
The method of any one of claims 1, 2, 3, 4 and 5, including limiting the exposure of the alumina to acid so that platinum and rhodium catalytic components, when one or both are present, each has a dispersion of at least about 0.3 carbon monoxide molecules per atom of platinum group metal as measured by CO chemisorption after reduction in hydrogen at 750° C. for one hour.
Claim 29
Independent Claim
69 words
The method of any one of claims 1, 2, 3, 4 and 5, including limiting acidification conditions to which the alumina is exposed so that platinum and rhodium catalytic components, when one or both are present, each has a dispersion of at least about 0.4 carbon monoxide molecules per atom of platinum group metal as measured by CO chemisorption after reduction in hydrogen at 750° C. for one hour.
Claim 30
Independent Claim
171 words
A method of making a catalyst composition comprising an activated alumina having one or more platinum group metal catalytic components dispersed thereon, comprising: (a) dispersing one or more platinum group metal catalytic components on particles of an activated alumina; (b) applying to a carrier substrate the activated alumina having said one or more platinum group metal catalytic components thereon, and calcining the resultant coating on the carrier substrate; and (c) carrying out steps (a) and (b) while limiting the exposure of the activated alumina to acid so that platinum, rhodium and palladium catalytic components, when one or more are present, each has a dispersion of at least about 0.3 carbon monoxide molecules per atom of platinum group metal as measured by CO chemisorption (i) the disperson of platinum and rhodium being measured after reduction in hydrogen at 750° C. for one hour and (ii) the dispersion of palladium being measured after heating in air for one hour at 750° C. followed by reduction in hydrogen at 350° C. for one hour.
Claim 31
Independent Claim
171 words
A method of making a catalyst composition comprising an activated alumina having one or more platinum group metal catalytic components dispersed thereon, comprising: (a) dispersing one or more platinum group metal catalytic components on particles of an activated alumina; (b) applying to a carrier substrate the activated alumina having said one or more platinum group metal catalytic components thereon, and calcining the resultant coating on the carrier substrate; and (c) carrying out steps (a) and (b) while limiting the exposure of the activated alumina to acid so that platinum, rhodium and palladium catalytic components, when one or more are present, each has a dispersion of at least about 0.3 carbon monoxide molecules per atom of platinum group metal as measured by CO chemisorption (i) the disperson of platinum and rhodium being measured after reduction in hydrogen at 750° C. for one hour and (ii) the dispersion of palladium being measured after heating in air for one hour at 750° C. followed by reduction in hydrogen at 350° C. for one hour.
Claim 32
Dependent Claim
42 words
The method of claim 28 wherein the platinum, rhodium and palladium catalytic components, when one or more are present, each has a dispersion of at least about 0.4 carbon monoxide molecules per atom of platinum group metal as measured by CO chemisorption.
Claim 33
Dependent Claim
65 words
The method of claim 28 or claim 29 including dispersing said one or more platinum group metal catalytic components on the activated alumina by contacting the activated alumina with one or more liquids containing dispersions therein of compounds of the metals of said platinum group metal catalytic components said liquids being capable of being removed by volatilization or decomponsition upon application of heat and/or vacuum.
Claim 34
Dependent Claim
29 words
The method of claim 30 wherein the one or more liquids comprise one or more aqueous solutions of compounds of the metals of the platinum group metal catalytic components.
Claim 35
Independent Claim
55 words
The method of any one of claims 28, 29, 30 or 31 including modifying the activated alumina by incorporating therein a modifier selected from the group consisting of one or more of alkaline earth metal oxide, rare earth metal oxides, silicon dioxide, Group IVB metal oxides, chromium oxide, iron oxide, nickel oxide and precursors thereof.
Claim 36
Dependent Claim
24 words
The method of claim 28 or claim 29 wherein the calcining is carried out at a temperature not in excess of about 600° C.
Claim 37
Dependent Claim
24 words
The method of claim 28 or claim 29 wherein the calcining is carried out at a temperature not in excess of about 500° C.
Claim 38
Dependent Claim
24 words
The method of claim 28 or claim 29 wherein the calcining is carried out at a temperature not in excess of about 350° C.
Claim 39
Independent Claim
20 words
The method of any one of claims 33, 34 or 35 wherein th e calcining is carried out in air.
Claim 40
Dependent Claim
24 words
The method of claim 28 including applying to the carrier substrate particles of a solid, particulate ceria along with the particles of activated alumina.
Claim 41
Dependent Claim
13 words
The method of claim 37 wherein the solid, particulate ceria comprises aluminum-stabilized ceria.
Claim 42
Dependent Claim
30 words
The method of claim 37 or claim 38 wherein the ceria comprises at least 90 weight percent ceria, measured as CeO 2 , and exclusive of the aluminum stabilizer content.
Claim 43
Dependent Claim
30 words
The method of claim 37 or claim 38 wherein the ceria comprises at least 95 weight percent ceria, measured as CeO 2 , and exclusive of the aluminum stabilizer content.
Claim 44
Dependent Claim
30 words
The method of claim 37 or claim 38 wherein the ceria comprises at least 99 weight percent ceria, measured as CeO 2 , and exclusive of the aluminum stabilizer content.
Claim 45
Dependent Claim
41 words
The method of claim 28 or claim 29 including in a preliminary step, milling a slurry of particles of the activated alumina in a non-acidified milling liquid to reduce the size of the particles in a first stage size reduction step.
Claim 46
Dependent Claim
11 words
The method of claim 42 wherein the milling liquid comprises water.
Claim 47
Dependent Claim
31 words
The method of claim 42 including carrying out a second stage size reduction step comprising milling the particles of activated alumina obtained from the first step in an acidified milling liquid.
Claim 48
Dependent Claim
27 words
The method of claim 44 wherein the acidified milling liquid is an aqueous solution of a compound of a metal of said platinum group metal catalytic components.
Claim 49
Dependent Claim
86 words
A catalyst prepared by a process comprising the steps of: providing a carrier substrate; applying and dispersing upon said carrier substrate particles of an activated alumina having one or more platinum group metal catalytic components dispersed thereon, calcining said alumina and dispersed catalytic components subsequent to their application to said carrier substrate to provide a calcined coating on the carrier substrate, and subsequently stabilizing said calcined coating by (a) impregnating the calcined coating with a solution of a stabilizer-precursor, and (b) calcining the stabilizer-precursor impregnated coating.
Claim 50
Dependent Claim
86 words
A catalyst prepared by a process comprising the steps of: providing a carrier substrate; applying and dispersing upon said carrier substrate particles of an activated alumina having one or more platinum group metal catalytic components dispersed thereon, calcining said alumina and dispersed catalytic components subsequent to their application to said carrier substrate to provide a calcined coating on the carrier substrate, and subsequently stabilizing said calcined coating by (a) impregnating the calcined coating with a solution of a stabilizer-precursor, and (b) calcining the stabilizer-precursor impregnated coating.
Claim 51
Dependent Claim
44 words
The catalyst of claim 46 wherein the solution of a stabilizer-precursor is an aqueous solution containing a stabilizer-precursor selected from the group consisting of one or more of alkaline earth metal oxide precursors, rare earth metal oxide precursors, and Group IVB metal oxide precursors.
Claim 52
Dependent Claim
12 words
The catalyst of claim 47 wherein the Group IVB metal is zirconium.
Claim 53
Dependent Claim
19 words
The catalyst of claim 47 wherein the stabilizer-precursor comprises a mixture of a barium compound and a lanthanum compound.
Claim 54
Dependent Claim
26 words
The catalyst of any one of claims 46, 47, 48 or 49 wherein said one or more platinum group metal catalytic components comprises a platinum component.
Claim 55
Dependent Claim
26 words
The catalyst of any one of claims 46, 47, 48 or 49 wherein said one or more platinum group metal catalytic components comprises a palladium component.
Claim 56
Dependent Claim
30 words
The catalyst of any one of claims 46, 47, 48 or 49 wherein said one or more platinum group metal catalytic components comprise a platinum component and a palladium component.
Claim 57
Dependent Claim
30 words
The catalyst of any one of claims 46, 47, 48 or 49 wherein said one or more platinum group metal catalytic components comprise a palladium component and a rhodium component.
Claim 58
Dependent Claim
30 words
The catalyst of any one of claims 46, 47, 48 or 49 wherein said one or more platinum group metal catalytic components comprise a platinum component and a rhodium component.
Claim 59
Dependent Claim
33 words
The catalyst of claim 46 or claim 47 wherein the calcined coating is modified by being thermally stabilized and the solution of a modifier precursor is a solution of a thermal stabilizer precursor.
Claim 60
Dependent Claim
13 words
The catalyst of claim 46 or claim 47 including a solid, particulate ceria.
Claim 61
Dependent Claim
11 words
The catalyst of claim 56 including a solid, particulate aluminum-stabilized ceria.
Claim 62
Dependent Claim
36 words
The catalytic of claim 57 wherein the aluminum-stabilized ceria contains from about 0.05 to about 10 weight percent of aluminum, measured as Al 2 O 3 , based on the total weight of the aluminum-stabilized ceria.
References Cited (Backward Citations)
US3554929A
Cited
US3993572A
Cited
US4294726A
Cited
US4367162A
Cited
US4492770A
Cited
US4407735A
Cited
US4438219A
Cited
US4442024A
Cited
US4504598A
Cited
US4619909A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-02-22 | 1991-08-24 | 1992-02-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-02-22 | 1995-08-24 | 1996-02-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-02-22 | 1999-08-24 | 2000-02-23 | $7700.00 | Window Closed / Lapsed |