Biocompatible microporous polymeric materials and methods of making same
Assignee: MATRIX MEMBRANES Inc
•
Filing: 1985-10-18
•
Granted: 1987-11-03
•
Expires: 2005-10-18
Abstract
Abstract A microporous biocompatible material is formed by preparing a segmented polyether urethane urea solution containing 25%±1.5% solids dissolved in a solvent. The solution has sufficient viscosity to be preshaped and formed into the desired thickness of the finished article, then immediately immersed into a precipitation bath in which the solvent in the solution is miscible for a time interval sufficient to cause the solution to set up into an opaque elastomeric article. The article is immediately removed from the bath, any excess solvent extracted and then dried at a temperature on the order of 35° C. to 70° C. followed by heat treating by annealing for approximately sixty minutes at a temperature at 100° C. to 130° C. The void volume of the membrane solution is controlled to within the 50% to 80% range and the pore size from ca <0.1 to several mms. as well as the shape of the pores and solid structures between them, thereby enabling close control over the characteristics and structure of the material as well as over variations in structural characteristics and porosity across the thickness of the material according to its intended application and use.
Inventors
- 👤 D. Keith Gilding
- 👤 Andrew M. Reed
- 👤 Ian N. Askill
- 👤 Stephen G. Briana
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 03:19
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/28; A; A61; A61F; A61F13/00; A61F13/00987; A61F13/00991; A61F13/00995; A61F13/02; A61F13/0276; A61F13/0289; A61F2/00; A61F2/02; A61F2/04; A61F2/06; A61F2/062; A61L; A61L15/00; A61L15/16; A61L15/22; A61L15/26; A61L15/42; A61L15/425; A61L27/00; A61L27/14; A61L27/18; B; B29; B29C; B29C48/00; B29C48/03; B29C48/07; B29C48/08; B29C48/25; B29C48/88; B29C48/919; A61F2013/00089; A61F2013/00093; A61F2013/00119; A61F2013/00217; A61F13/15; A61F2013/15008; A61F2013/15048; A61F13/53; A61F2013/530481; A61F2250/00; A61F2250/0014; A61F2250/0023; B29C48/09; C08J2201/00; C08J2201/04; C08J2201/054; C08J2201/0542; C08J2201/0544; Y; Y10; Y10T; Y10T428/00; Y10T428/249921; Y10T428/249953
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
126 words
The process for fabricating a biocompatible elastomeric article from a polymeric material containing a solvent, said process comprising the steps of: (1) forming said polymeric material in solution form into the shape of the desired finished article; (2) immersing said material in a precipitant bath which is miscible with said solvent contained in said polymeric material while causing precipitation of the remaining material into a microporous elastomeric article having a selective variation in pore size across its thickness, said material immersed in said precipitant bath for a time interval sufficient to produce an article having a greater porosity along one surface than the other; (3) removing the article from said precipitant bath and washing same to remove any solvent therefrom; and (4) heat treating the article.
Claim 2
Dependent Claim
126 words
The process for fabricating a biocompatible elastomeric article from a polymeric material containing a solvent, said process comprising the steps of: (1) forming said polymeric material in solution form into the shape of the desired finished article; (2) immersing said material in a precipitant bath which is miscible with said solvent contained in said polymeric material while causing precipitation of the remaining material into a microporous elastomeric article having a selective variation in pore size across its thickness, said material immersed in said precipitant bath for a time interval sufficient to produce an article having a greater porosity along one surface than the other; (3) removing the article from said precipitant bath and washing same to remove any solvent therefrom; and (4) heat treating the article.
Claim 3
Dependent Claim
17 words
The process according to claim 1, characterized by drying the article prior to the heat treating step.
Claim 4
Dependent Claim
15 words
The process according to claim 1, said polymeric material being a segmented polyurethane urea resin.
Claim 5
Dependent Claim
35 words
The process according to claim 3, said segmented polyether urea resin containing 25%±1.5% solids dissovled in a DMAC solvent, said material having a viscosity at 22° C. to 25° C. between 12,000 and 50,000 cps.
Claim 6
Dependent Claim
29 words
The process according to claim 1, characterized by drying said article for a period of four to seven hours at a temperature ranging from 35° C. to 75° C.
Claim 7
Dependent Claim
30 words
The process according to claim 5, further characterized by heat treating said article for one to one and one-half hours at a temperature ranging from 100° C. to 130° C.
Claim 8
Dependent Claim
43 words
The process according to claim 1, characterized by applying said solution to a flat substrate to form a layer having a thickness greater than that of the finished article as a preliminary to immersion of said substrate and layer into the precipitant bath.
Claim 9
Dependent Claim
216 words
The process for fabricating a microporous membrane from a polymeric material comprising the steps of: (a) preparing a segmented polyether urea resin in solution form containing 25%±1.5% solids dissolved in a DMAC solvent, said solution having a viscosity at 22° C.-25° C. between 12,000 cps and 50,000 cps; (b) applying said solution to a substrate to form a solution layer having a thickness greater than that of the finished article; (c) immersing said substrate and layer of solution into a bath which is miscible with said solvent while causing precipitation of the remaining solution layer into an opaque elastomeric article, said solution layer being immersed for a time interval sufficient to produce an article having a variation in pore size between the exposed surface of said solution layer and the surface in contact with said substrate, said porosity being in the range of 0.01 to 100 microns; (d) removing said article from the bath and extracting any remaining solvent therefrom; (e) placing said article on a drying frame and drying said article for a period of four to seven hours at a temperature on the order of 35° C. to 75° C.; and (f) heat-treating said article for one to one and one-half hours at a temperature on the order of 100° C. to 130° C.
Claim 10
Dependent Claim
216 words
The process for fabricating a microporous membrane from a polymeric material comprising the steps of: (a) preparing a segmented polyether urea resin in solution form containing 25%±1.5% solids dissolved in a DMAC solvent, said solution having a viscosity at 22° C.-25° C. between 12,000 cps and 50,000 cps; (b) applying said solution to a substrate to form a solution layer having a thickness greater than that of the finished article; (c) immersing said substrate and layer of solution into a bath which is miscible with said solvent while causing precipitation of the remaining solution layer into an opaque elastomeric article, said solution layer being immersed for a time interval sufficient to produce an article having a variation in pore size between the exposed surface of said solution layer and the surface in contact with said substrate, said porosity being in the range of 0.01 to 100 microns; (d) removing said article from the bath and extracting any remaining solvent therefrom; (e) placing said article on a drying frame and drying said article for a period of four to seven hours at a temperature on the order of 35° C. to 75° C.; and (f) heat-treating said article for one to one and one-half hours at a temperature on the order of 100° C. to 130° C.
Claim 11
Dependent Claim
28 words
The process according to claim 8, said substrate being in the form of a flat plate and said solution being applied to said substrate as a thin layer.
Claim 12
Dependent Claim
24 words
The process according to claim 8, the composition of said bath being selected from the group consisting water and of aqueous solutions of alcohols.
Claim 13
Dependent Claim
11 words
The process according to claim 8, the precipitant bath being water.
Claim 14
Dependent Claim
141 words
In a process for fabricating a biocompatible elastomeric membrane from a polyurethane material containing a solvent, the process being of the type including the steps of (1) forming said polyurethane material into the shape of the finished article; (2) immersing said material into a precipitant bath which is miscible with said solvent in said material while causing precipitation of the remaining material into an opaque elastomeric article; and (3) removing the article from said substrate and washing the article to remove any solvent therefrom; the improvement which comprises: (4) applying a modifying material to one surface of said polyurethane material and immersing said polyurethane material together with said modifying material in said precipitant bath for a time interval sufficient to produce an article having a selective variation in pore size across its thickness from less than 0.1 microns to 100 microns.
Claim 15
Dependent Claim
141 words
In a process for fabricating a biocompatible elastomeric membrane from a polyurethane material containing a solvent, the process being of the type including the steps of (1) forming said polyurethane material into the shape of the finished article; (2) immersing said material into a precipitant bath which is miscible with said solvent in said material while causing precipitation of the remaining material into an opaque elastomeric article; and (3) removing the article from said substrate and washing the article to remove any solvent therefrom; the improvement which comprises: (4) applying a modifying material to one surface of said polyurethane material and immersing said polyurethane material together with said modifying material in said precipitant bath for a time interval sufficient to produce an article having a selective variation in pore size across its thickness from less than 0.1 microns to 100 microns.
Claim 16
Dependent Claim
40 words
The process according to claim 12, said polymeric material being a segmented polyether urea resin containing 25%±1.5% solids dissolved in a DMAC solvent, said solution having a viscosity at 22° C. to 25° C. between 12,000 cps and 30,000 cps.
Claim 17
Dependent Claim
20 words
The process according to claim 13, the gradation in pore size ranging from less than 0.1 microns to 100 microns.
Claim 18
Dependent Claim
32 words
The process according to claim 14, said polyurethane material being formed into a tubular configuration and said modifying material being a precipitant solution applied to the internal surface of said polyurethane material.
Claim 19
Dependent Claim
26 words
The process according to claim 15, characterized by extruding said polyurethane material into a tubular member and pumping said modifying material internally through said tubular member.
Claim 20
Dependent Claim
33 words
The process according to claim 16, including the step of advancing said tubular member through an external modifying liquid preliminary to immersing said tubular member in said precipitant bath into an extraction tank.
Claim 21
Dependent Claim
13 words
The process according to claim 17, said external modifying liquid being dimethyl acetamide.
References Cited (Backward Citations)
US3301257A
Cited
US3645835A
Cited
US3665918A
Cited
US3949742A
Cited
US3978855A
Cited
US4173689A
Cited
US4203847A
Cited
US4460369A
Cited
US4341207A
Cited
US4452845A
Cited
EP0128501A2
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-11-02 | 1991-05-04 | 1991-11-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-11-02 | 1995-05-04 | 1995-11-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-11-02 | 1999-05-04 | 1999-11-03 | $7700.00 | Window Closed / Lapsed |