Method for casting thin-walled work pieces of synthetic materials
Assignee: MAGNA INTERIOR SYSTEMS GmbH
•
Filing: 1984-06-18
•
Granted: 1986-08-19
•
Expires: 2004-06-18
Abstract
Abstract A thin-walled work piece of plastics material is cast in a mold by pouring or flowing the plastics material in the form of a plastisol or a flowable powder into a preheated casting mold which is locked to a casting container in a sealed manner to form a closed casting cavity. The mold and the container are then lifted or rotated through at least 180°. A reduced pressure is maintained in the cavity at least prior and during the tilting. After a predetermined time the reduced pressure is removed and the mold and container are tilted back into the starting position. The mold and container are then separated again and the mold is then heated for completion of the jelling or curing whereupon the mold is cooled for removing the work piece from the mold.
Inventors
- 👤 Erich M. Christoph
- 👤 Hermann A. Bartels
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 19:30
CPC Classifications
B; B29; B29C; B29C41/00; B29C41/02; B29C41/18; B29C33/00; B29C33/34; B29C33/36; Y; Y10; Y10S; Y10S425/00; Y10S425/06
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
338 words
A method for casting thin-walled work pieces of synthetic material, comprising the following steps: (a) preheating a casting mold (2), (b) maintaining a quantity of flowable powder of synthetic material in a casting container (3) substantially to a predetermined filling level, (c) closing the casting container (3) with the preheated casting mold (2) to form a liquid and pressure tight casting unit enclosing a casting cavity (13), (d) beginning to vibrate the casting unit and evacuating the casting cavity to a reduced pressure while the casting unit is vibrating, said reduced pressure being just sufficient to remove air from said casting cavity but also insufficient to suck said flowable powder out of said casting cavity, (e) rotating the casting unit in one direction through 180° from a mold-up starting position into a mold-down casting position, and providing a dwell time for permitting said flwoable powder of synthetic material to move into said preheated casting mold in the mold-down position, further rotating said casint unit in the same direction back to the starting mold-up position, providing a dwell time in said starting mold-up position, and then rotating the casting unit in the opposite direction again in two steps of 180° each with a dwell time at the casting position and at the starting position for uniformly covering the casting mold surfaces with a powder layer of substantially uniform thickness throughout, (f) said dwell times permitting the flowable powder of synthetic material to begin to form a jelled skin on the inner surface of said preheated casting mold, (g) permitting any excess flowable powder of synthetic material to move back into said casting container when said casting unit is in the last mentioned mold-up position, (h) removing the casting mold from the casting container and moving the casting mold into a heating station for curing the work piece which has formed as said jelled skin on the internal surfaces of the casting mold, and (i) after curing, cooling the casting mold and removing the work piece from the casting mold.
Claim 2
Independent Claim
338 words
A method for casting thin-walled work pieces of synthetic material, comprising the following steps: (a) preheating a casting mold (2), (b) maintaining a quantity of flowable powder of synthetic material in a casting container (3) substantially to a predetermined filling level, (c) closing the casting container (3) with the preheated casting mold (2) to form a liquid and pressure tight casting unit enclosing a casting cavity (13), (d) beginning to vibrate the casting unit and evacuating the casting cavity to a reduced pressure while the casting unit is vibrating, said reduced pressure being just sufficient to remove air from said casting cavity but also insufficient to suck said flowable powder out of said casting cavity, (e) rotating the casting unit in one direction through 180° from a mold-up starting position into a mold-down casting position, and providing a dwell time for permitting said flwoable powder of synthetic material to move into said preheated casting mold in the mold-down position, further rotating said casint unit in the same direction back to the starting mold-up position, providing a dwell time in said starting mold-up position, and then rotating the casting unit in the opposite direction again in two steps of 180° each with a dwell time at the casting position and at the starting position for uniformly covering the casting mold surfaces with a powder layer of substantially uniform thickness throughout, (f) said dwell times permitting the flowable powder of synthetic material to begin to form a jelled skin on the inner surface of said preheated casting mold, (g) permitting any excess flowable powder of synthetic material to move back into said casting container when said casting unit is in the last mentioned mold-up position, (h) removing the casting mold from the casting container and moving the casting mold into a heating station for curing the work piece which has formed as said jelled skin on the internal surfaces of the casting mold, and (i) after curing, cooling the casting mold and removing the work piece from the casting mold.
Claim 3
Dependent Claim
38 words
The method of claim 1, further comprising monitoring the filling level of flowable powder of synthetic material in said casting container, and keeping said filling level at the same level for casting work pieces of the same type.
Claim 4
Dependent Claim
30 words
The method of claim 1, further comprising maintaining the temperature of the flowable powder of synthetic material present in the casting container at a constant temperature level for each filling.
Claim 5
Dependent Claim
22 words
The method of claim 3, wherein said constant temperature level is a temperature within the range of 20° C. to 50° C.
Claim 6
Dependent Claim
27 words
The method of claim 1, further comprising moving the casting container and the casting mold through a plurality of work stations in which said steps are performed.
Claim 7
Dependent Claim
28 words
The method of claim 1, further comprising terminating said reduced pressure prior to said step of returning said casting container and the casting mold into the starting position.
Claim 8
Dependent Claim
17 words
The method of claim 1, wherein said closing and removing steps are performed in a timed sequence.
Claim 9
Dependent Claim
80 words
The method of claim 1, further comprising sequentially passing said casting mold through a first continuous heater means for heating said casting mold to a temperature sufficient for said flowable powder of synthetic material to begin to jell, and then passing said casting mold through a second continuous heater means for heating said casting mold to a temperature sufficient for completion of the jelling of said flowable powder of synthetic material or for curing said flowable powder of synthetic material.
Claim 10
Dependent Claim
34 words
The method of claim 1, further comprising deflecting said flowable powder of synthetic material in said casting cavity for guiding said flowable powder of synthetic material into any dead spaces inside said casting mold.
Claim 11
Dependent Claim
50 words
The method of claim 1, further comprising terminating said evacuating prior to stopping said vibrating of said casting cavity for moving said flowable powder of synthetic material into all recesses of said casting mold and to shake off excessive flowable powder material from the interior surface of the jelled skin.
Claim 12
Dependent Claim
17 words
The method of claim 1, further comprising loosening up said flowable synthetic material inside said casting cavity.
References Cited (Backward Citations)
US1506061A
Cited
DE1149882B
Cited
US2991506A
Cited
DE1186197B
Cited
US3337662A
Cited
US3506755A
Cited
DE1943151A1
Cited
DE1949125A1
Cited
US4063863A
Cited
US4167382A
Cited
US4473673A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-08-18 | 1990-02-17 | 1990-08-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-08-18 | 1994-02-17 | 1994-08-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-08-18 | 1998-02-17 | 1998-08-19 | $7700.00 | Window Closed / Lapsed |