Polyethylene superthin film and a process for the production of the same
Assignee: Tonen General Sekiyu KK
•
Filing: 1985-04-29
•
Granted: 1986-07-15
•
Expires: 2005-04-29
Abstract
Abstract A polyethylene superthin film having a thickness of at most 3 mu m, a tensile modulus of at least 2000 kg/cm2, a breaking strength of at least 500 kg/cm2 and a haze of at most 10% is produced by heating and dissolving polyethylene having a weight average molecular weight of at least 5x105 in a solvent, forming a gel sheet from the resulting solution, subjecting the gel sheet to a solvent removal treatment to adjust the amount of the solvent in the gel sheet to 10 to 80% by weight, heating and stretching the sheet, removing the residual solvent therefrom and then subjecting the stretched product to a compressing treatment at a temperature of at most the melting point of the polyethylene.
Inventors
- 👤 Koichi Kono
- 👤 Shoichi Mori
- 👤 Kenji Miyasaka
- 👤 Jyoichi Tabuchi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 13:58
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/02; C08J3/09; C08J3/091; C08J3/092; B; B29; B29C; B29C55/00; B29C55/005; C08J5/00; C08J5/18; B29K; B29K2023/00; B29K2023/04; B29K2023/06; C08J2323/00; C08J2323/02; C08J2323/04; C08J2323/06; Y; Y10; Y10T; Y10T428/00; Y10T428/26; Y10T428/269; Y10T428/31504; Y10T428/31855; Y10T428/31938
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
54 words
A polyethylene superthin film consisting of polyethylene having a weight average molecular weight of at least 5×10 5 , and having a thickness of at most 3 μm, a tensile modulus of at least 2000 kg/cm 2 , a breaking strength of at least 500 kg/cm 2 and a haze of at most 10%.
Claim 2
Dependent Claim
54 words
A polyethylene superthin film consisting of polyethylene having a weight average molecular weight of at least 5×10 5 , and having a thickness of at most 3 μm, a tensile modulus of at least 2000 kg/cm 2 , a breaking strength of at least 500 kg/cm 2 and a haze of at most 10%.
Claim 3
Dependent Claim
41 words
The polyethylene superthin film of claim 1, wherein the thickness is 0.1 to 1 μm, the tensile modulus is at least 4000 kg/cm 2 , the breaking strength is at least 1000 kg/cm 2 and the haze is at most 5%.
Claim 4
Dependent Claim
20 words
The polyethylene superthin film of claim 1, wherein the weight average molecular weight is 1×10 6 to 10×10 6 .
Claim 5
Dependent Claim
212 words
A process for the production of a polyethylene superthin film having a thickness of at most 3 μm, a tensile modulus of at least 2000 kg/cm 2 , a breaking strength of at least 500 kg/cm 2 and a haze of at most 10%, which comprises heating and dissolving polyethylene having a weight average molecular weight of at least 5×10 5 in a solvent with sufficient agitation to ensure the complete dissolution of the polyethylene in the solvent, forming a gel sheet from the resulting solution by subjecting the polyethylene solution to extrusion through a die or to spreading over a support, and cooling and gelling at a temperature below the gelling temperature and at a cooling rate of at least 50° C./min., subjecting the gel sheet to a solvent removal treatment to adjust the amount of the solvent in the gel sheet to 10 to 80% by weight, heating and stretching the sheet biaxially simultaneously or in sequence at a temperature of from the α-dispersion point to the crystal melting point of the polyethylene with a surface magnification of at least 10 times, removing the residual solvent therefrom and then subjecting the stretched product to a compressing treatment at a temperature of 80° to 140° C. using a press or roll.
Claim 6
Dependent Claim
212 words
A process for the production of a polyethylene superthin film having a thickness of at most 3 μm, a tensile modulus of at least 2000 kg/cm 2 , a breaking strength of at least 500 kg/cm 2 and a haze of at most 10%, which comprises heating and dissolving polyethylene having a weight average molecular weight of at least 5×10 5 in a solvent with sufficient agitation to ensure the complete dissolution of the polyethylene in the solvent, forming a gel sheet from the resulting solution by subjecting the polyethylene solution to extrusion through a die or to spreading over a support, and cooling and gelling at a temperature below the gelling temperature and at a cooling rate of at least 50° C./min., subjecting the gel sheet to a solvent removal treatment to adjust the amount of the solvent in the gel sheet to 10 to 80% by weight, heating and stretching the sheet biaxially simultaneously or in sequence at a temperature of from the α-dispersion point to the crystal melting point of the polyethylene with a surface magnification of at least 10 times, removing the residual solvent therefrom and then subjecting the stretched product to a compressing treatment at a temperature of 80° to 140° C. using a press or roll.
Claim 7
Dependent Claim
18 words
The process of claim 4, wherein the weight average molecular weight is 1×10 6 to 10×10 6 .
Claim 8
Dependent Claim
43 words
The process of claim 4, wherein the solvent is at least one member selected from the group consisting of aliphatic hydrocarbons and cyclic hydrocarbons such as nonane, decane, undecane, dodecane, decalin and paraffin oils and mineral oil fractions having boiling points corresponding thereto.
Claim 9
Dependent Claim
17 words
The process of claim 6, wherein the solvent is a non-volatile solvent such as a paraffin oil.
Claim 10
Dependent Claim
21 words
The process of claim 4, wherein the heating and dissolving is carried cut at a temperature of 140° to 250° C.
Claim 11
Dependent Claim
18 words
The process of claim 4, wherein the solution has a polyethylene content of 1 to 10% by weight.
Claim 12
Dependent Claim
13 words
The process of claim 4, wherein the temperature is 15° to 25° C.
Claim 13
Dependent Claim
27 words
The process of claim 4, wherein the solvent removal treatment is carried out by immersing the gel sheet in a readily volatile solvent to extract the solvent.
Claim 14
Dependent Claim
56 words
The process of claim 12, wherein the readily volatile solvent is at least one member selected from the group consisting of hydrocarbons such as pentane, hexane and heptane, chlorinated hydrocarbons such as methylene chloride and carbon tetrachloride, fluorinated hydrocarbons such as trifluoroethane, ethers as diethyl ether and dioxane and alcohols such as methanol, ethanol and propanol.
Claim 15
Dependent Claim
43 words
The process of claim 4, wherein the solvent removal treatment is carried out in such a manner that the gel sheet shrinks with a shrinkage of at least 50% in the thickness direction and at most 20% in the longitudinal and lateral directions.
Claim 16
Dependent Claim
13 words
The process of claim 4, wherein the temperature is 90° to 140° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-07-14 | 1990-01-13 | 1990-07-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-07-14 | 1994-01-13 | 1994-07-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-07-14 | 1998-01-13 | 1998-07-15 | $7700.00 | Window Closed / Lapsed |